Dwijaya, Made Subekti (2016) Pengaruh Penambahan Asam Adipat Terhadap Kekuatan Tarik Dan Stabilitas Termal Poliuretan. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2709100008-Undergraduate-Theses.pdf Download (6MB) | Preview |
Abstract
Poliuretan adalah polimer dengan ciri khas adanya
gugus uretan dalam rantai utama. Asam adipat, sebagai polyester
poliol berfungsi untuk meningkatkan kekuatan tarik. Pada
penelitian ini dilakukan variasi penambahan asam adipat untuk
mengetahui pengaruhnya terhadap kekuatan tarik dan stabilitas
termal poliuretan. Penambahan asam adipat dilakukan dengan
komposisi 10, 20, 30, 40, 50, dan 60%wt. Resin epoksi dan
penguatnya ditambahkan pada proses pencampuran. Campuran
dituangkan kedalam cetakan spesimen uji tarik dan dilakukan
proses curing selama 72 jam. Pengujian yang dilakukan adalah
pengujian DSC/TGA, FTIR, pengujian kekerasan, dan pengujian
tarik. Hasil dari pengujian DSC/TGA menunjukkan stabilitas
termal tertinggi didapat pada spesimen 30% berat asam adipat
dengan temperatur degradasi 5% pada 203.167oC. Pengujian
FTIR memberikan hasil terdapatnya gugus pembentuk
poliuretan. Pengujian kekerasan menunjukkan kekerasan
tertinggi didapat dari spesimen 40% berat asam adipat dengan
nilai kekerasan 89 shore A. Hasil pengujian tarik memberikan
hasil nilai kekuatan tarik tertinggi didapat dari spesimen 40%
berat asam adipat sebesar 3.029554655 MPa.
==================================================================================
Polyurethane is polymer characterized by urethane
group on the main link. Adipic acid, as the polyester polyol, is
used to increase the tensile strength. In this research, adipic
acid was added with varying composition of 10, 20, 30, 40, 50,
and 60%wt. Epoxy resin & hardener were added when the
mixing process. The mixture poured into tensile test cast and
cured for 72 hour in room temperature. Characterized being
conducted in this research were DSC/TGA,FTIR, hardness test,
and tensile test. The result of DSC/TGA shows highest thermal
stability achieve with 30%wt adipic acid addition with 5%
thermal degradation on 203.167oC. FTIR test shows the forming
of Urethane group . Hardness test shows highest hardness
number 89 shore A when the speciment contain 40%wt adipic
acid . Tensile test shows highest tensile strength on 3.029554655
MPa when the speciment contain 40%wt adipic acid.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSMt 620.194 92 Dwi p |
| Uncontrolled Keywords: | Poliuretan, Asam Adipat, Epoxy Resin, Polyurethane, Adipic Acid |
| Subjects: | T Technology > T Technology (General) |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Anis Wulandari |
| Date Deposited: | 07 Jul 2017 05:39 |
| Last Modified: | 26 Dec 2018 07:20 |
| URI: | http://repository.its.ac.id/id/eprint/41908 |
Actions (login required)
 |
View Item |