Pengaruh pH Air Hujan Dan Beban Terhadap Karakteristik Korosi Pada Baja Galvalum

Yanti, Anissa Febri Dwi (2016) Pengaruh pH Air Hujan Dan Beban Terhadap Karakteristik Korosi Pada Baja Galvalum. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2711100066-Undergraduate-Theses.pdf

Download (3MB) | Preview

Abstract

Baja galvalum memiliki sejarah sebagai rangka atap pada konstruksi bangunan yang efektif dan ekonomis. Baja galvalum terdiri dari lapisan tipis seng dan aluminium yang menyatu pada substrat baja. Kombinasi ini menjadikan material yang memiliki sifat mekanik bajadengan ketahanan korosi dari seng dan aluminium. Untuk komposisi Galvalum pada umumnya terdiri dari unsur coatingnya 55% Aluminium, 43.5% Seng dan 1.5% Silikon. Lapisan galvanis memiliki kinerja yang telah terbukti dalam berbagai kondisi lingkungan namun ketahanan korosi seng pelapis ditentukan oleh ketebalan lapisan yang bervariasi dengan kondisi lingkungan. Penelitian ini dilakukan untuk menganalisa karakteristik korosi pada baja galvalum dengan lingkungan air hujan dan pembebanan. Penelitian ini menggunakan metode weight loss air hujan dengan ph 5.6 dan 7.5 diberi variasi beban 5,10,15 % Beban Yield yang diperoleh dari hasil pengujian tarik dan direndam selama 10, 20, 30 hari dengan ph dijaga konstan. Hasil dari pengujian ini menunjukan bahwa baja galvalum dengan air hujan ph 5.6 dengan penambahan beban memberikan nilai laju korosi yang lebih rendah dibandingkan dengan menggunakan air hujan ph 7.5 dan pengaruh beban terhadap laju korosi berpengaruh, semakin besar beban yang diberikan maka semakin besar pula laju korosi yang dihasilkan hal ini dapat dibuktikan pada pengujian immerse dengan Air Hujan ph 5.6 pada 10 hari pertama dengan beban 5% menunjukan nilai laju korosi sebesar 10.514 Mpy, beban 10% sebesar 11.379 Mpy dan beban 15% sebesar 13.775 Mpy. Danpada 10hari pertama dan untuk pengujian immerse dengan Air Hujan ph 7.5 dan beban 5% sebesar13.376 Mpy, beban 10% sebesar 15.173 Mpy dan pada beban 15% sebesar 15.173 Mpy. Hasilpengujian SEM dan EDAX terlihat 2 area yang merupakan area terang indikasi unsur aluminium dan area gelap indikasi unsur seng. Selanjutnya dari pengujian XRD didapatkan senyawa produk korosi yang terbentuk yaitu Al2O4Zn, AlHO2, Al0.333Cl0.333H3.334O2.667Zn0.667 ===================================================================================== Galvalume steel has a history as roof truss construction of effective and economical buildings.Galvalume steel consists of thin layers of zinc and aluminium which layered on the steel substrate. This combination makes the material that has the mechanical properties of steel improved and also corrosion resistance from the zinc and aluminium. For galvalume material normally composed of coating unsure 55% aluminium, 43,5% zinc and 1,5% silicone. Galvanis coating is proven to has the good performance under various environmental conditions but corrosion resistance of the zinc layer depends on the thickness of the layer but varies with environmental conditions. This research was conducted to learn about the corrosion characteristic of galvalume steel due to the acidity of rainwater with the pH of 5.6 and 7.5 which was loaded with variety of load 5, 10, 15% from yield load that was obtained from the tensile test and soaked for 10, 20, 30 days with constant pH. The result of this test shows that galvalume steel with the pH 5.6 and the addition of load has the lower corrosion rate compare to the other material that use the rainwater with pH 7.5. Load will also affect the corrosion rate, the bigger load was given, the bigger corrosion rate is produced. It was proven in the first 10 days with a load of 5% shows thevalue ofthe corrosion rateof10.514Mpy, load of 10% is 11.379Mpy and load 15% of 13.775Mpy. Andin thefirst 10 days and for testing Immerse with rain waterpH 7.5 and 5% load of 13.376Mpy, load of10% is15 173Mpy and the load of15% amounting to15 173Mpy. The result of SEM and EDAX test show 2 areas, those are bright area indicated the aluminium unsure and dark area indicated the zinc unsure. Corrosion test shows that the compound obtained XRD testing produced from the corrosion process was Al2O4Zn, AlHO2, Al0.333Cl0.333H3.334O2.667Zn0.667.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 23 Yan p
Uncontrolled Keywords: Baja Galvalum, Zn55Al, Laju Korosi, Air Hujan ph 5.6 dan 7.5., Steel Galvalume, Corrosion rate, Rainwater pH 5.6 and 7.5
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Mrs Anis Wulandari
Date Deposited: 12 Jul 2017 06:59
Last Modified: 28 Dec 2018 02:22
URI: http://repository.its.ac.id/id/eprint/42077

Actions (login required)

View Item View Item