Analisa Brittle Crack Initiation Pada Baja Kekuatan Tinggi Akibat Pengaruh Temperatur

Bawafi, Mohan (2001) Analisa Brittle Crack Initiation Pada Baja Kekuatan Tinggi Akibat Pengaruh Temperatur. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 4195100033-Undergraduate-Thesis.pdf]
Preview
Text
4195100033-Undergraduate-Thesis.pdf - Published Version

Download (23MB) | Preview

Abstract

Brittle fracture adalah kepecahan yang terjadi secara tiba-tiba dengan sedikit atau tanpa deformasi. Seringkali harga dari tegangan nominal yang bekerja pada material pada saat brittle fracture terjadi dibawah yield point atau yield strength dari material tersebut. Proses timbulnya brittle fracture dapat dibagi menjadi dua yaitu crack initation dan crack propagation. Kepekaan terhadap brittle fracture adalah masalah besar pada baja. Penjalaran retak brittle fracture mempunyai kecepatan yang tinggi bahkan pada bangunan baja diperkirakan mepunyai kecepatan beberapa ribu kali perdetik. Brittle fracture kemungkinan terjadi pada temperatur rendah, keadaan ini bukan karena bertambahnya beban akibat penurunan temperatur tetapi karena berubahnya sifat material pada temperature rendah
Dalam tugas akhir ini untuk mengetahui proses terjadinya brittle crack diselidiki dengan memperhatikan perambatan pada brittle crack dengan metode crack tip opening displacement (CTOD) pada suhu ruangan dan suhu -ScfC dengan menggunakan material high tensile (A 516 grade 70) dan mild steel (SS 41 grade A). sehingga nantinya akan didapatkan fracture toughness (K1c), bukaan ujung retak (CTOD/b), energi minimum perunit perpanpanjangan retak ( J1c) dari material tersebut yang nantinya dapat digunakan sebagai acuan dalam mendesain sebuah konstruksi.
============================================================
Brittle fracture is a fracture that happens suddenly with little or without deformation. Frequently the value of the nominal strain working on a material at brittle fracture is under the yield point or yield strength of the respective material. The process of brittle fracture is divided into two
circumstances: crack initiation and crack propagation. The sensitivity to brittle fracture is a big problem for steel. The crack propagation of brittle fracture has a high speed; even at a steel construction it is assumed to have a speed of thousands times per second. Brittle fracture may occur at a low temperature. This is not because of the increase of the load due to the decrease in the temperature, but it is because the characteristic of material changes in low temperature.
In this final project, to study the process of brittle crack is obseNed by examining the spread on the brittle crack using crack tip opening displacement method (CTOD) at room temperature and -50° C applied to high tensile material (A 516 grade 70) and mild steel (SS 41 grade A). From this it can be yielded the values of fracture toughness (Kic), crack tip opening (CTOD/5), and the minimum energy per unit crack extension (Jic) of the respective material which later can used as a reference in designing a construction.

Item Type: Thesis (Undergraduate)
Additional Information: RSPe 623.843 Baw a
Subjects: Q Science > QC Physics > QC271 Temperature measurements
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Marine Technology (MARTECH) > Naval Architecture and Shipbuilding Engineering > 36201-(S1) Undergraduate Thesis
Depositing User: ansi aflacha
Date Deposited: 02 Apr 2018 07:55
Last Modified: 02 Apr 2018 07:55
URI: http://repository.its.ac.id/id/eprint/51666