Pengaruh Kecepatan Putar Mata Pahat Dan Kecepatan Pengelasan Terhadap Konduktivitas Listrik Sambungan Aluminium Dan Tembaga Hasil Friction Stir Welding (FSW)

Kurniawan, Fauzan (2018) Pengaruh Kecepatan Putar Mata Pahat Dan Kecepatan Pengelasan Terhadap Konduktivitas Listrik Sambungan Aluminium Dan Tembaga Hasil Friction Stir Welding (FSW). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511440000121_Undergraduate_Thesis.pdf - Published Version
Restricted to Repository staff only

Download (8MB)

Abstract

Pada penelitian ini didiskusikan pengaruh kecepatan putar mata pahat dan kecepatan pengelasan pada nilai konduktivitas listrik sambungan Al-Cu. Sambungan Al-Cu diperoleh dari proses Friction Stir Welding (FSW) butt joint. Bahan yang digunakan adalah Al 6061 dan tembaga murni. Proses FSW menggunakan mata pahat dengan desain pin yang menyatu dengan mata pahat dan sudut kemiringan tiga derajat. Variabel yang digunakan pada penelitian ini adalah kecepatan rotasi mata pahat 800, 1000 dan 1250 RPM serta kecepatan pengelasan 10, 12,5 dan 16 mm/min. Pengujian yang dilakukan pada penelitian ini adalah pengujian makro visual, pengukuran nilai resistansi dan pengujian mikro hardness. Selain dilakukan pengujian, dilakukan analisis mengenai heat input dan waktu pengelasan yang dibutuhkan pada setiap variabel. Hasil pengujian makro visual dan XRD didapati bahwa pada sambungan aluminium dan tembaga terdapat senyawa intermetalik berupa AlCu dan Al2Cu. Dari analisa yang dilakukan, didapatkan hasil pengelasan dengan kecepatan pengelasan 12,5 mm/min merupakan variabel teroptimum. Nilai konduktivitas yang didapat dari proses pengelasan ini adalah berkisar antara 27,173 m Ω-1 mm-2 dan 28,09 m Ω-1 mm-2. Adanya senyawa intermetalik mempengaruhi konduktivitas sambungan aluminium dan tembaga. ============== Dissimilar friction stir welding between 6061 aluminum alloy and pure copper sheet with a thickness of 3 mm was investigated. The variabels were three rotational tool speeds (800, 1000 and 1250 RPM) and three welding speeds (10, 12,5 and 16 mm/min). The influences of tool rotating speed and welding speed on the electrical conductivity of the joints were investigated. The examination that has been done were macro visual examination, resistance measurement using micro ohmmeter and micro hardness examination. Heat input and welding time analysis was also done in this experiment. From micro visual and XRD examination, AlCu and Al2Cu intermetallic compound was found at the joint of aluminium and copper. The optimum variabel was obtained a welding speed of 12,5 mm/min. The value of electrical conductivity was between 27,173 m Ω-1 mm-2 and 28,09 m Ω-1 mm-2. The presence of intermetallic compound was affecting the electrical conductivity of the joint.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.52 Kur p
Uncontrolled Keywords: Bimetal Al-Cu, Friction Stir Welding, Senyawa Intermetalik, Solid-state Welding, Bimetal Al-Cu, Friction Stir Welding, Intermetallic Compound, Solid-state Welding
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TN Mining engineering. Metallurgy
T Technology > TS Manufactures
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > (S1) Undergraduate Theses
Depositing User: Fauzan Kurniawan
Date Deposited: 27 Nov 2018 07:38
Last Modified: 27 Nov 2018 07:38
URI: http://repository.its.ac.id/id/eprint/52879