Pengaruh Kecepatan Putar Mata Pahat Dan Kecepatan Pengelasan Terhadap Konduktivitas Listrik Sambungan Aluminium Dan Tembaga Hasil Friction Stir Welding (FSW)

Kurniawan, Fauzan (2018) Pengaruh Kecepatan Putar Mata Pahat Dan Kecepatan Pengelasan Terhadap Konduktivitas Listrik Sambungan Aluminium Dan Tembaga Hasil Friction Stir Welding (FSW). Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 02511440000121_Undergraduate_Thesis.pdf]
Preview
Text
02511440000121_Undergraduate_Thesis.pdf - Accepted Version

Download (8MB) | Preview

Abstract

Pada penelitian ini didiskusikan pengaruh kecepatan
putar mata pahat dan kecepatan pengelasan pada nilai
konduktivitas listrik sambungan Al-Cu. Sambungan Al-Cu
diperoleh dari proses Friction Stir Welding (FSW) butt joint.
Bahan yang digunakan adalah Al 6061 dan tembaga murni.
Proses FSW menggunakan mata pahat dengan desain pin yang
menyatu dengan mata pahat dan sudut kemiringan tiga derajat.
Variabel yang digunakan pada penelitian ini adalah kecepatan
rotasi mata pahat 800, 1000 dan 1250 RPM serta kecepatan
pengelasan 10, 12,5 dan 16 mm/min. Pengujian yang dilakukan
pada penelitian ini adalah pengujian makro visual, pengukuran
nilai resistansi dan pengujian mikro hardness. Selain dilakukan
pengujian, dilakukan analisis mengenai heat input dan waktu
pengelasan yang dibutuhkan pada setiap variabel. Hasil pengujian
makro visual dan XRD didapati bahwa pada sambungan
aluminium dan tembaga terdapat senyawa intermetalik berupa
AlCu dan Al2Cu. Dari analisa yang dilakukan, didapatkan hasil
pengelasan dengan kecepatan pengelasan 12,5 mm/min
merupakan variabel teroptimum. Nilai konduktivitas yang didapat
dari proses pengelasan ini adalah berkisar antara 27,173 m Ω-1
mm-2 dan 28,09 m Ω-1 mm-2. Adanya senyawa intermetalik
mempengaruhi konduktivitas sambungan aluminium dan
tembaga. ============== Dissimilar friction stir welding between 6061 aluminum alloy and pure copper sheet with a thickness of 3 mm was
investigated. The variabels were three rotational tool speeds (800,
1000 and 1250 RPM) and three welding speeds (10, 12,5 and 16
mm/min). The influences of tool rotating speed and welding
speed on the electrical conductivity of the joints were
investigated. The examination that has been done were macro
visual examination, resistance measurement using micro
ohmmeter and micro hardness examination. Heat input and
welding time analysis was also done in this experiment. From
micro visual and XRD examination, AlCu and Al2Cu
intermetallic compound was found at the joint of aluminium and
copper. The optimum variabel was obtained a welding speed of
12,5 mm/min. The value of electrical conductivity was between
27,173 m Ω-1 mm-2 and 28,09 m Ω-1 mm-2. The presence of
intermetallic compound was affecting the electrical conductivity
of the joint.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 671.52 Kur p
Uncontrolled Keywords: Bimetal Al-Cu, Friction Stir Welding, Senyawa Intermetalik, Solid-state Welding, Bimetal Al-Cu, Friction Stir Welding, Intermetallic Compound, Solid-state Welding
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
T Technology > TN Mining engineering. Metallurgy
T Technology > TS Manufactures
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis