Putra, Audio Duana (2018) Pengaruh Variasi Jumlah Layer Pada Sambungan Las SMAW Dengan Elektroda E7016, Material SA 36 Terhadap Kekuatan Tarik, Kekerasan Dan Makro Etsa. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
10211500000003-AudioDuanaPutra.pdf - Accepted Version Download (5MB) | Preview |
Abstract
Pada era zaman sekarang penggunaan baja pada bidang konstruksi mulai dilirik karena relative ringan dan memiliki kekuatan serta ketahanan yang tinggi. Pada penyambungan baja tentu diperlukan suatu proses dan salah satunya pengelasan. Pengelasan sendiri merupakan salah satu proses yang cukup berperan dalam industri manufaktur dengan tujuan untuk proses maintenance maupun proses produksi.
Dalam tugas akhir ini pengelasan yang digunakan las SMAW. Salah satu jenis sambungan las yang perlu dikaji lebih lanjut adalah sambungan las multi layer dengan perbedaan jumlah layer yaitu 3 layer dan 2 layer. Karena pada pengelasan multi layer,layer kedua memberikan efek postheat pada layer sebelumnya dan preheat bagi layer sesudahnya. Selanjutnya untuk mengetahui perbedaan sifat mekanik berupa kekerasan dan keuletan pada material, sehingga dapat mengetahui nilai uji tarik, uji kekerasan dan makro etsa.
Dari hasil pengujian yang telah dilakukan pengelasan SMAW pada baja SA 36 dengan variasi jumlah layer dapat disimpulkan untuk hasil pengujian tarik, letak patahan berada pada HAZ. Untuk spesimen 3 layer memiliki nilai tegangan tarik lebih besar yaitu 47.2 kgf/mm2 daripada spesimen 2 layer yang sebesar 41.548 kgf/mm2. Untuk hasil pengujian kekerasan, spesimen 3 layer memiliki nilai kekerasan lebih rendah dari spesimen 2 layer yaitu sebesar 84.96 HRB dengan 85.11 HRB. Untuk hasil makro etsa HAZ specimen 3 layer lebih besar dibandingkan 2 layer.==================================================================================================================In this era use of steel in construction began a revival due to the relative lightness and strength as well as endurance. On the joining of steel certainly needed a process and one welding. Own welding process is one which is quite influential in the manufacturing industry with the purpose of maintenance process as well as the production process.
In this final task of welding used welding SMAW. One of the connection types need welding examined further is a multi layer with welding connection the difference number of layer 3 and 2 layer. Because welding multi layer second layer, the effect on the layer before and postheat preheat for the layer afterwards. Next to knowing the difference in the form of mechanical properties hardness and tenacity on the material, so it can know the value of testing tensile test, hardness, and macro etching.
From the results of testing that has been done welding SMAW at baja SA 36 with the variation of the total number of layers can be inferred for the tensile test results, the position of the Ridge are on HAZ. For layer 3 specimens have greater pull voltage values is 47.2 kgf/mm2 than layer 2 specimens of 41.548 kgf/mm2. For test results of violence, specimen 3 layer hardness value is lower than the specimen 2 layer is 84.96 HRB with 85.11 HRB. For the results of macro etching, HAZ specimens 3 layer larger than specimens 2 layer.
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSMI 671.52 Put p |
| Uncontrolled Keywords: | Pengelasan, SMAW, Multi Layer, 3 Layer, 2 Layer, Uji Tarik, Uji Kekerasan, Makro Etsa. |
| Subjects: | T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Vocational > Mechanical Industrial Engineering (D4) |
| Depositing User: | Audio Duana Putra |
| Date Deposited: | 08 Dec 2020 03:21 |
| Last Modified: | 08 Dec 2020 03:21 |
| URI: | http://repository.its.ac.id/id/eprint/58954 |
Actions (login required)
 |
View Item |