Analisa Pengaruh Sudut Karbon Fiber Twill Dan Plain Dengan Core Polyurethane Rigid Foam Komposit Sandwich Yang Menggunakan Metode Vacuum Bagging Pada Pengujian Three Point Bending

Nugraha, Muhammad Adietya (2018) Analisa Pengaruh Sudut Karbon Fiber Twill Dan Plain Dengan Core Polyurethane Rigid Foam Komposit Sandwich Yang Menggunakan Metode Vacuum Bagging Pada Pengujian Three Point Bending. Diploma thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 10211500000077-Non_Degree.pdf]
Preview
Text
10211500000077-Non_Degree.pdf - Accepted Version

Download (6MB) | Preview

Abstract

Nogogeni adalah mobil yang dirancang untuk kendaraan hemat energi, ramah lingkungan, efisiensi tinggi. Untuk mencapai rancangan tersebut maka tim harus mereduksi berat pada kendaraan. Salah satu upaya untuk mereduksi berat mobil adalah dengan menggunakan bahan bodi mobil dengan yang lebih ringan, dengan menggunakan bodi yang ringan pada mobil, maka nilai efisiensi yang tinggi akan lebih mudah untuk didapatkan.
Penelitian diawali dengan proses komposit sandwich menggunakan proses hand lay up pada semua lapisan serat dan core. Setelah komposit sandwich tersusun, pasang imstalasi vacuum bagging pada lapisan komposit yang telah di hand lay up tadi, setelah itu hubungkan instalasi vacuum bagging tadi dengan pompa vacuum dan nyalakan pompa, tunggu hingga ± 6 jam. Kemudian hasil cetakan yang telah selesai divacuum tadi dipotong menggunakan gerinda tangan dengan variasi sudut 0°, 30°, 45° dan mengacu pada ukuran untuk spesimen bending ASTM C393. Setelah pemotongan selesai dilakukan pengujian bending dengan mengguakan metode three point bending. Foto makro pada setiap spesiemen yang telah diuji bending untuk mengetahui jenis kegagalan pada komposit.
Setelah dilakukan pengujian bending diketahui bahwa data pengujian menghasilkan kekuatan bending sebesar 4,709 MPa, momen bending 8446 Nmm, dan modulus elastisitas 4,5 MPa, facing bending stress 11,297 MPa, core shear ultimate stress 0,207 MPa komposit yang terbaik terdapat pada arah serat 450, model kegagalan komposit sandwich serat karbon fiber dengan core polyurethan akibat pengujian bending (three point bending) berupa micro Buckling dan kegagalan identation.
=========================================================Nogogeni is a car which is designed for energy efficient vehicles, environmentally friendly, high efficiency. To achieve this, the team must reduce the weight on the vehicle. One effort to reduce the weight of the car is to use a lighter material, using a lightweight body on the car, then the high efficiency will be easier to obtain.
The research begins with a sandwich composite process using hand lay up process on all layers of fiber and cores. After the composite sandwich is arranged, install the vacuum bagging installation on the composite layer that has been in the hand lay up, then connect the vacuum bagging installation with the vacuum pump and turn on the pump, wait up to ± 6 hours. Then the finished mold of the vacuum was cut using a hand grinder with angle variation of 0 °, 30 °, 45 ° and refers to the size for ASTM C393 bending specimen. After the cutting is done bending test by using the three point bending method. Photo macro on each specimen that has been tested bending to know the type of failure on the composite.
After do bending test data, the bending power is 4,709 MPa, bending moment is 8446 Nmm, and modulus elasticity is 4.5 MPa, facing bending stress is 11,297 MPa, shear stress core is 0.207 Mpa. The best composite variation direction of sandwich material is 45o, carbon fiber sandwich with polyurethan core due to bending test (three point bending) in the micro buckling failure and, identation failure.

Item Type: Thesis (Diploma)
Additional Information: RSMI 620.118 Nug a
Uncontrolled Keywords: Komposit, Karbon Fiber, Core Polyurethan Rigid Foam, Vacuum Bagging, Uji Bending
Subjects: T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
T Technology > TP Chemical technology > TP1140 Polymers
T Technology > TS Manufactures > TS170 New products. Product Development
Divisions: Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User: Muhammad Adietya Nugraha
Date Deposited: 26 Nov 2020 04:08
Last Modified: 26 Nov 2020 04:08
URI: http://repository.its.ac.id/id/eprint/59088

Actions (login required)

View Item View Item