Pemanfaatan pozzolan sebagai bahan dasar geopolimer

Triani, Desak Nyoman Deasi (2015) Pemanfaatan pozzolan sebagai bahan dasar geopolimer. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
3111100008-Paper.pdf - Published Version

Download (522kB) | Preview
[img]
Preview
Text
3111100008-Presentation.pdf - Presentation

Download (1MB) | Preview
[img]
Preview
Text
3111100008-Undergraduate_Theses.pdf - Published Version

Download (3MB) | Preview

Abstract

Pozzolan mengandung silika dan alumina yang dapat dipergunakan sebagai bahan dasar pada pasta geopolimer. Namun demikian, tidak semua pozzolan dapat digunakan sebagai bahan dasar geopolimer. Penelitian ini menggunakan metakaolin dan lempung yang memiliki kandungan silika dan alumina amorf setelah dikalsinasi pada suhu 7000C. Tingginya rasio Silika terhadap alumnina pada material tersebut mengasilkan pasta geopolimer yang memiliki sifat mekanik dan ketahanan terhadap bakar yang baik. Komposisi mix design penelitian ini, berdasarkan pada perbandingan Silika terhadap alumina di dalam campuran pasta. Pasta yang berbahan dasar metakaolin perbandingan silika terhadap alumina adalah sebesar 1.4 dan 1.8. Sedangkan untuk lempung, perbandingan yang digunakan adalah sebesar 2.8 dan 3.2. Larutan alkali aktivator menggunakan Na2SiO3 yang dicampur dengan larutan NaOH. Molaritas NaOH yang dipakai adalah 10 M dan 8 M. Hasil Pengujian menunjukan bahwa pada umur 28 hari, kuat tekan tertinggi pasta berbahan dasar clay Blitar adalah 69.75 mPa, dan metakaolin sebesar 75.37 mPa. Untuk pasta yang diuji bakar pada suhu 4000C selama 30 menit, seluruh benda uji mengalami penurunan kuat tekan. Persentase kuat tekan sisa tertinggi pada pasta metakaolin sebesar 42.89 % , dan pada pasta clay Blitar sebesar 73.06 %. vi Berdasarkan hasil analisa, diketahui bahwa semakin tinggi perbandingan Silika terhadap alumina pada campuran, ketahanan terhadap bakarnya lebih baik. Namun untuk kuat tekan awal ada faktor-faktor lain yang perlu dipertimbangkan yaitu perbandingan water/solid dan perbandingan SiO2/Na2O. Semakin tinggi water/solid didalam campuran, maka kuat tekan pasta cenderung semakin menurun terutama pada material lempung. Sedangkan untuk SiO2/Na2O, semakin tinggi rasionya maka kuat tekan pasta cenderung meningkat. ========== Pozzolan contains of silica and alumina which can be used as raw material for geopolymer paste. However not all pozzolan can be used for geopolymer material. Metakaolin and clay that contain with silica and alumina amorf after calcined at 7000C are used. Mechanical properties and fire resistance of geopolymer paste increase as the ratio of silica to alumina. Mix design composition on this research based on the ratio of silica to alumina. The ratio of silica to alumina for metakaolin paste are 1.4 and 1.8. While for clay paste the ratio that used are 2.8 and 3.2. Na2SiO3 and NaOH with 10 M and 8 M were used as alkali activator at this research. The result of this research showed that compressive strength at 28 days for clay and metakaolin were 69.75 mPa and 75.37 mPa respectively. For burning test, the paste were burned at 4000C for 30 minute. The compressive strength of geopolymer paste after burned are decerease. The highest residual strength for metakaolin paste is 42.98 % and 73.06% for clay paste. Based on analysis the effect of increasing the ratio of silica to alumina increase fire resistance ability for both metakaolin and clay. However initial compressive strength is effected not only by ratio of silica to alumina but also the ratio of water to solid and SiO2/Na2O. The compressive strength decerease as the ratio of viii water to solid increases. Meanwhile compressive strength increase as the ratio of SiO2/Na2O increase.

Item Type: Thesis (Undergraduate)
Additional Information: RSS 553.61 Tri p
Uncontrolled Keywords: kaolin, lempung, metakaolin, pozzolan, silica fume, kaolin, lempung, metakaolin, pozzolan, silica fume.
Subjects: T Technology > TN Mining engineering. Metallurgy > TN271.K2 Kaolin
T Technology > TP Chemical technology > TP1140 Polymers
Divisions: Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis
Depositing User: - Davi Wah
Date Deposited: 10 May 2019 03:41
Last Modified: 10 May 2019 03:41
URI: http://repository.its.ac.id/id/eprint/62991