Pengaruh Persentase Sio2 Terhadap Laju Korosi Komposit Pani/Sio2 Pada Larutan Korosif (Nacl)

Shoodiqin, Dian Mart (2014) Pengaruh Persentase Sio2 Terhadap Laju Korosi Komposit Pani/Sio2 Pada Larutan Korosif (Nacl). Masters thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
1112201016-Master_Theses.pdf - Published Version

Download (3MB) | Preview
[img]
Preview
Text
1112201016-Presentation.pdf - Presentation

Download (5MB) | Preview

Abstract

Dalam penelitian ini dilakukan pelapisan baja tipe SS304 dengan komposit PANi/SiO2 berbasis material alam sebagai pelapis anti korosi. Penelitian meliputi ekstraksi pasir silika dari pasir alam Bancar untuk mendapatkan SiO2 dengan kemurnian yang tinggi dan pembuatan komposit PANi/SiO2. Sintesis komposit PANi/ SiO2 dilakukan dengan menggunakan metode polimerisasi in situ. Komposit PANi/SiO2 dicampurkan ke dalam cat yang selanjutnya dilapiskan pada baja tipe SS304 untuk dijadikan sebagai pelapis anti korosi. Perbandingan konsentrasi komposit PANi:SiO2 yaitu 70:30, 80:20, dan 90:10. Baja tipe SS304 yang telah terlapisi diuji sifat korosi menggunakan metode Polarisasi. Topografi dan morfologi permukaan setelah uji korosi diamati menggunakan SEM dan EDX. Berdasarkan dari uji Polarisasi dan perhitungan laju korosi menunjukkan komposit PANi/SiO2 dengan perbandingan 70:30 memiliki ketahanan korosi yang paling baik diantara komposit yang lain. Pengamatan SEM menunjukkan jenis korosi yang terbentuk adalah korosi merata (uniform corrosion). ========== In this research covers the extraction of silica sand from the sand Bancar to obtain high purity with SiO2 and manufacture composite PANi/SiO2. Synthesis of composite PANi/SiO2 is done by using the method of in situ polymerization. Composite PANi/SiO2 mixed into paint then coated on steel SS304 type to serve as anti-corrosion coatings. Comparison of the concentration of SiO2 : PANi composite that is 70 : 30, 80 : 20, and 90 : 10. Steel SS304 type that has been tested using the method of corrosion properties of polarization. The topography and morphology of surface after corrosion test observed using SEM and EDX. Based on a test of Polarization and the calculation of corrosion rate shows a composite PANi/SiO2 with 70 : 30 ratio has the most excellent corrosion resistance among other composite. SEM observations indicate the type of corrosion is evenly formed (uniform corrosion).

Item Type: Thesis (Masters)
Additional Information: RTFi 620.112 23 Sho p
Uncontrolled Keywords: Polianilin (PANi), SiO2, Polimerisasi in situ, korosi, in situ polymerization, corrosion
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials
Divisions: Faculty of Mathematics and Science > Physics > (S2) Master Theses
Depositing User: - Davi Wah
Date Deposited: 04 Jul 2019 05:48
Last Modified: 04 Jul 2019 05:48