Pengaruh Persentase Sio2 Terhadap Laju Korosi Komposit Pani/Sio2 Pada Larutan Korosif (Nacl)

Shoodiqin, Dian Mart (2014) Pengaruh Persentase Sio2 Terhadap Laju Korosi Komposit Pani/Sio2 Pada Larutan Korosif (Nacl). Masters thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 1112201016-Master_Theses.pdf]
Preview
Text
1112201016-Master_Theses.pdf - Published Version

Download (3MB) | Preview
[thumbnail of 1112201016-Presentation.pdf]
Preview
Text
1112201016-Presentation.pdf - Presentation

Download (5MB) | Preview

Abstract

Dalam penelitian ini dilakukan pelapisan baja tipe SS304 dengan
komposit PANi/SiO2 berbasis material alam sebagai pelapis anti korosi.
Penelitian meliputi ekstraksi pasir silika dari pasir alam Bancar untuk
mendapatkan SiO2 dengan kemurnian yang tinggi dan pembuatan komposit
PANi/SiO2. Sintesis komposit PANi/ SiO2 dilakukan dengan menggunakan metode
polimerisasi in situ. Komposit PANi/SiO2 dicampurkan ke dalam cat yang
selanjutnya dilapiskan pada baja tipe SS304 untuk dijadikan sebagai pelapis anti
korosi. Perbandingan konsentrasi komposit PANi:SiO2 yaitu 70:30, 80:20, dan
90:10. Baja tipe SS304 yang telah terlapisi diuji sifat korosi menggunakan metode
Polarisasi. Topografi dan morfologi permukaan setelah uji korosi diamati
menggunakan SEM dan EDX. Berdasarkan dari uji Polarisasi dan perhitungan
laju korosi menunjukkan komposit PANi/SiO2 dengan perbandingan 70:30
memiliki ketahanan korosi yang paling baik diantara komposit yang lain.
Pengamatan SEM menunjukkan jenis korosi yang terbentuk adalah korosi merata
(uniform corrosion). ========== In this research covers the extraction of silica sand from the sand Bancar
to obtain high purity with SiO2 and manufacture composite PANi/SiO2. Synthesis
of composite PANi/SiO2 is done by using the method of in situ polymerization.
Composite PANi/SiO2 mixed into paint then coated on steel SS304 type to serve as
anti-corrosion coatings. Comparison of the concentration of SiO2 : PANi
composite that is 70 : 30, 80 : 20, and 90 : 10. Steel SS304 type that has been
tested using the method of corrosion properties of polarization. The topography
and morphology of surface after corrosion test observed using SEM and EDX.
Based on a test of Polarization and the calculation of corrosion rate shows a
composite PANi/SiO2 with 70 : 30 ratio has the most excellent corrosion
resistance among other composite. SEM observations indicate the type of
corrosion is evenly formed (uniform corrosion).

Item Type: Thesis (Masters)
Additional Information: RTFi 620.112 23 Sho p
Uncontrolled Keywords: Polianilin (PANi), SiO2, Polimerisasi in situ, korosi, in situ polymerization, corrosion
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.75 Corrosion-resistant materials
Divisions: Faculty of Mathematics and Science > Physics > 45101-(S2) Master Thesis
Depositing User: - Davi Wah
Date Deposited: 04 Jul 2019 05:48
Last Modified: 04 Jul 2019 05:48
URI: http://repository.its.ac.id/id/eprint/63323

Actions (login required)

View Item View Item