Mauretha, Nella (2019) Pengaruh Voltase dan Lapisan Dasar Tembaga Nikel terhadap Ketebalan, Kelekatan, dan Kekilapan Permukaan Produk Elektroplating Kuningan. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000020-Undergraduates_Theses.pdf Download (5MB) | Preview |
Abstract
Elektroplating memiliki tujuan untuk meningkatkan sifat-sifat tertentu dan untuk memperbaiki tampak rupa (dekoratif). Elektroplating kuningan merupakan salah satu contoh yang digunakan dalam fungsi dekoratif. Penelitian tugas akhir ini menggunakan kuningan sebagai logam pelapis dan baja karbon rendah AISI 1020 sebagai substratnya. Proses pengerjaan dilakukan di salah satu home industry yang beroperasi di Semarang. Pelaksanaan pelapisan ini menggunakan variabel voltase (3, 5, dan 7 volt) dan adanya lapisan dasar tembaga nikel. Untuk mengukur ketebalan lapisan yang terbentuk digunakan dengan coating thickness Elcometer dan untuk mengukur daya lekat lapisan digunakan uji Pull Off, Bending Test, dan Rockwell C Indentasi. Sedangkan untuk mengukur kekilapan digunakan alat glossmeter. Selain itu dilakukan juga uji SEM/EDX untuk mengamati ketebalan lapisan yang terbentuk dan mapping unsur yang terkandung dalam lapisan. Hasil yang diperoleh dalam percobaan adalah bahwa ketebalan paling tinggi dihasilkan oleh spesimen dengan voltase 7 volt dengan lapisan dasar tembaga nikel. Untuk nilai kilap paling tinggi juga dihasilkan oleh spesimen voltase 7 volt dengan lapisan dasar tembaga nikel. Sedangkan untuk adhesinya, secara kualitatif didapatkan bahwa seluruh spesimen memiliki adhesi yang baik. Untuk mengetahui spesimen mana yang memiliki kombinasi sifat-sifat paling baik, dilakukan skoring dengan berdasar pada produk pembanding. Didapatkan hasil bahwa spesimen dengan variasi tegangan 3 volt dengan lapisan dasar tembaga nikel adalah yang paling baik diantara lapisan yang lainnya. Dimana ketebalannya tidak berbeda jauh dengan produk pembanding, namun kekilapan yang dihasilkan (411.33 GU) lebih tinggi dari kekilapan produk pembanding (398 GU). Sehingga dapat disimpulkan bahwa dengan waktu elektroplating yang sama dan voltase yang lebih rendah menghasilkan kekilapan yang lebih tinggi. ==================================================================================================================================
The purposes of electroplating is to improve spesific properties and its appearance (decorative). Brass electroplating is one example used in decorative functions. This final project has done with brass as a coating metal and low carbon steel AISI 1020 as its substrate. The work process was carried out in one of the home industry operating in Semarang. The variables of research are the voltage ( 3, 5, and 7 volts) and the presence of copper nickel base coat. The Elcometer coating thickness was used to measure the thickness of the formed layer and Pull Off, Bending Test, and Rockwell C Indentation tests were used to measure the adhesion strength. To measure the gloss, a glossmeter was used. In addition, SEM / EDX tests were also conducted to observe the thickness of the layers formed and the mapping of elements contained in the layers. The results obtained in the experiment were that the highest thickness was produced at 7 volt with a copper nickel base coat. Also,the highest gloss value at 7 volt with copper nickel base coat. However for the adhesion, it was qualitatively found that all specimens had good adhesion. To find out which specimens have the best combination of properties, scoring is carried out based on the existing commercial product. The results showed that the specimens with voltage at 3 volts with copper nickel base coat is the best among the other specimens. The thickness at 3 volts with copper nickel base coat is no significant differences from the thickness of existing commercial products, and its glossines (411.33 GU) was higher from the glossiness of existing commercial products (398 GU). We can concluded that at the same electroplating time with lower voltage increase the surface glossiness.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 671.732 Mau p-1 2019 |
| Uncontrolled Keywords: | Elektroplating Kuningan, Ketebalan, Kelekatan, Kekilapan, Lapisan Dasar, Voltase |
| Subjects: | Q Science > Q Science (General) T Technology > TA Engineering (General). Civil engineering (General) T Technology > TA Engineering (General). Civil engineering (General) > TA491 Metal coating. T Technology > TS Manufactures > TS173 Reliability of industrial products |
| Divisions: | Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Nella Mauretha |
| Date Deposited: | 03 Dec 2024 03:36 |
| Last Modified: | 03 Dec 2024 03:36 |
| URI: | http://repository.its.ac.id/id/eprint/65427 |
Actions (login required)
 |
View Item |