Prameswati, Ajeng (2019) Pengaruh Heat Input dan Variasi Komposisi Shielding Gas terhadap Struktur Mikro dan Sifat Mekanik Sambungan Baja Karbon Rendah JIS G3101 Hasil Gas Metal Arc Welding (GMAW) Sebagai Aplikasi Arm Excavator di PT. X. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000021-Undergraduate_Theses.pdf Download (5MB) | Preview |
Abstract
JIS G3101 SS400 merupakan salah satu jenis baja struktural yang paling banyak digunakan dalam konstruksi. Pada proses pengelasan baja, Gas Metal Arc Welding (GMAW) merupakan teknik pengelasan paling banyak digunakan yang menggunakan CO2 dan Argon sebagai gas sebagai pelindung dari oksidasi. Variasi nilai heat input pengelasan juga mempengaruhi hasil las. Material carbon steel mengalami perubahan struktur dan butir serta sifat mekanik karena efek dari pemanasan dan pendinginan akibat pengelasan. Mengacu pada uraian diatas, penulis mengkaji bagaimana pengaruh heat input dan komposisi shielding gas terhadap struktur mikro dan sifat mekanik sambungan las JIS G3101 SS400. heat input yang diteliti adalah 620, 720 dan 740 J/mm. Sementara untuk komposisi shielding gas yang digunakan adalah 100% CO2, 80% CO2 + 20% Ar. Dari hasil pengujian didapatkan bahwa untuk kekerasan dan kekuatan impact variasi shielding gas 80% CO2 + 20% Ar memiliki hasil yang lebih bagus sedangkan untuk uji tarik hasil yang lebih baik didapatkan pada shielding gas 100% CO2.
=================================================================================================================================
JIS G3101 SS400 is one of the most widely used structural steel in construction. In the process of steel welding, Gas Metal Arc Welding (GMAW) is the most widely used welding technique that uses CO2 and Argon as a gas as a protector from oxidation. Variation in the value of welding heat input also affect the weld results. Carbon steel material will experience structural and grain changes and mechanical properties due to the effects of heating and cooling to welding. Referring to the description above, the author examines the influence of heat input and composition of shielding gas on the microstructure and mechanical properties of JIS G3101 SS400 welded joints. The heat inputs to be studied are 620, 720 and 740 J / mm. While the composition of shielding gas used is 100% CO2, 80% CO2 + 20% Ar. From the test results, it was found that for the hardness and impact strength of shielding gas 80% CO2 + 20% Ar had better results for the tensile than on shielding gas 100% CO2.
| Item Type: | Thesis (Other) |
|---|---|
| Additional Information: | RSMt 620.112 6 Pra p-1 2019 |
| Uncontrolled Keywords: | Gas Metal Arc Welding, JIS G30101 SS400, heat input, shielding gas. |
| Subjects: | T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy T Technology > TS Manufactures T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Prameswati Ajeng |
| Date Deposited: | 25 Jan 2024 02:40 |
| Last Modified: | 25 Jan 2024 02:40 |
| URI: | http://repository.its.ac.id/id/eprint/65821 |
Actions (login required)
 |
View Item |