Silaen, Yohannes Marudut Tua (2019) Sintesis Dan Karakterisasi Injectable Hydrogel Biokomposit Alginat/PVA/rGO Untuk Aplikasi Rekayasa Jaringan. Other thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
02511540000102_Undergraduate_Theses.pdf Download (1MB) | Preview |
Abstract
Perkembangan dunia medis, organ yang hilang atau rusak dapat diganti organ lain yang dikenal transplantasi organ. Namun terdapat kekurangan dalam metode ini yaitu permintaan organ untuk transplantasi selalu lebih tinggi dibandingkan organ yang tersedia serta dapat terjadinya penolakan oleh sistem kekebalan tubuh. Terdapat metode lain yaitu rekayasa jaringan (tissue engineering) yang merupakan penumbuhan jaringan secara in vitro. Pembuatan rekayasa jaringan membutuhkan material yang bersifat biokompatibilitas salah satunya yaitu Alginat dan Poly(vinyl alcohol) (PVA). Alginat merupakan polisakarida alami yang banyak digunakan sebagai biomaterial seperti pengantar obat (drug delivery) maupun pembawa sel. PVA merupakan polimer sintetik yang banyak digunakan sebagai polimer termoplastik ramah terhadap jaringan, tidak berbahaya dan tidak beracun. Dikarenakan keterbatasan sifat fisik dan mekanik, maka ditambahkan material lain sebagai filler pada biokomposit Alginat dan PVA. Oleh karena itu pada penelitian ini dianalisa pengaruh penambahan reduced graphene oxide (rGO) hasil sintesis modifikasi metode Hummer sebagai filler biokomposit Alginat/PVA terhadap sifat fisik, mekanik dan thermal untuk rekayasa jaringan. Komposisi rGO yang digunakan sebesar 0, 0.4, 0.8, 1.2 dan 1.6 berat dari total biokomposit Alginat dan PVA tanpa aquades. Kemudian dilakukan karakterisasi fisik, mekanik dan thermal pada sampel. Dari pengujian didapatkan penambahan rGO mempercepat curing time, menurunkan water content dan swelling ratio, meningkatkan kekuatan tekan serta meningkatkan temperatur dekomposisi. Komposisi optimum untuk biokomposit diperoleh Alginat/PVA/0,8% rGO. Komposisi tersebut menghasilkan kekuatan tekan tertinggi sebesar 0,0571 MPa, sifat fisik diatas rerata komposisi lain berupa waktu curing selama 35,5 menit, water content sebesar 93,03% dan swelling ratio sebesar 82,31% serta kemampuan degradasi thermal diatas rerata dengan temperatur mulai dekomposisi 56,28oC.
=========================================================
Nowadays, lost or damaged organs can be replaced by other organs known as organ transplants. But there are deficiencies in this method, namely the demand for organs for transplantation is always higher than the available organs, furthermore it can be rejected by the immune system. Tissue engineering requires biocompatible material, such as Alginate and Poly (vinyl alcohol) (PVA). Alginate is a natural polysaccharide, widely used as a biomaterial such as a drug delivery and cell carriers. PVA is thermoplastic polymer biocompatible to the tissues, harmless and non-toxic. Due to the limitations of physical and mechanical properties, other materials were added as fillers in Alginate and PVA biocomposites. Therefore, this study analyzed the effect of the reduced graphene oxide (rGO) (synthesizer using a modified Hummer method) as an Alginate/PVA biocomposite filler on physical, mechanical and thermal properties for tissue engineering application. The composition of rGO used was 0, 0.4, 0.8, 1.2 and 1.6 by weight percent without distilled water. Physical, mechanical and thermal characterization were performed on the sample. The addition of rGO accelerate curing time, decrease water content and swelling ratio, increase compressive strength and decomposition temperature. The optimum composition for biocomposite is obtained by Alginate/PVA/0.8% rGO. This hydrogel composite has the highest compressive strength of 0.0571 MPa, the physical properties above the other compositions in the form of curing time for 35.5 minutes, the water content of 93.03% and swelling ratio of 82.31% and the ability of thermal degradation above average with temperature start decomposition 56,28oC.
| Item Type: | Thesis (Other) |
|---|---|
| Uncontrolled Keywords: | Alginat, Biokomposit, PVA, Rekayasa Jaringan, rGO |
| Subjects: | Q Science Q Science > Q Science (General) T Technology > TA Engineering (General). Civil engineering (General) > TA455.G65 Graphene |
| Divisions: | Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis |
| Depositing User: | Yohannes Marudut Tua Silaen |
| Date Deposited: | 21 Mar 2023 08:25 |
| Last Modified: | 21 Mar 2023 08:25 |
| URI: | http://repository.its.ac.id/id/eprint/66279 |