Putri, Chandra Victoria Amanda and Novianty, Kantanegara Agquiline (2015) Sintesis partikel magnetite dengan metode elektrokimia dengan bantuan chelating agent. Diploma thesis, Institut Teknology Sepuluh Nopember.
Preview |
Text
2311100008-2311100184-Undergraduate_Thesis.pdf Download (2MB) | Preview |
Abstract
Penelitian ini bertujuan untuk mensintesis partikel
magnetite dengan metode elektrokimia pada variabel beda
potensial, pH larutan, rasio dan sumber ion Fe larutan prekursor.
Proses sintesis partikel magnetite (Fe3O4) ini diawali dengan
penambahan EDTA sebagai chelating agent untuk membentuk ion
kompleks dalam larutan elektrolit FeSO4 dan Fe2(SO4)3 dengan
konsentrasi mulai 0.25 M. Kemudian larutan dielektrolisis dengan
beda potensialmulai dari 5 V. Sintesis partikel magnetite dilakukan
selama 8 jam dan menggunakan elektroda karbon yang dipasang
secara paralel dengan jarak di antara keduanya yaitu 2 cm. Sintesis
Fe3O4 dilakukan pada beda potensial dan rasio larutan elektrolit
yang bervariasi. Variabel yang digunakan antara lain beda
potensial yang digunakan yaitu 2 hingga 10 volt; pH sekitar 3-8;
konsentrasi larutan 0,25 M; dan rasio larutan sebesar 1:1 dan 2:1.
Presipitat yang dihasilkan dipisahkan, dicuci dan dikeringkan
untuk mendapatkan partikel Fe3O4. Partikel yang telah dikeringkan
selanjutnya dikarakterisasi. Karakteristik besi oksida yang diamati
antara lain : struktur kristal dan komposisi penyusun sampel
dengan uji XRD, diameter partikel yang diukur secara tidak
langsung dengan mengukur luas permukaan spesifiknya dengan uji
BET, ikatan kimia dengan metode uji FTIR. Metode elektrokimia mampu menghasilkan partikel Fe3O4
meskipun masih terbentuk senyawa lain seperti Fe2O3, Fe(OH)3
dan FeOOH. Dari hasil XRD, BET dan FTIR pada variabel yang
telah ditentukan, didapatkan hasil terbaik partikel Fe3O4 pada
kondisi konsentrasi 0.25 M pada campuran FeSO4 dan Fe2(SO4)3
dengan rasio 1:1, pH 3 dan beda potensial 5 V. Sehingga dapat
disimpulkan bahwa karakteristik partikel Fe3O4 dipengaruhi oleh
kondisi pH, beda potensial dan komposisi larutan prekursor.
======================================================================================================
The main objectives of this research are to synthesize
magnetite particles using electrochemical method with chelating
agent by varying voltage, pH of solution, precursor solution ratio,
and Fe ion source for precursor solution. Magnetite (Fe3O4)
synthesize was started with EDTA as chelating agent addition into
FeSO4 and Fe2(SO4)3 electrolyte solution which concentration is
0.25 M to form complex ion. The solution was electrolyze with
voltage starting from 5 volt. The electrolysis was conducted for 8
hours and using carbon as electrodes. The electrodes were set
parallel with interelectrode spacing of 2 cm. The process was done
at varying voltage (2-10 volt); electrolyte ratio (1:1 and 2:1); and
with or without EDTA. The resulting precipitate was separated,
washed and dried to obtain Fe3O4 particles. Magnetite precipitate
were characterized by XRD to analyze crystalline structure and
sample composition, BET to analyze surface area and FTIR to
analyze chemical bonds.
The electrochemical method has successfully produce
Fe3O4 particles although there are still many polluter as Fe2O3 and
FeOOH. From the XRD, BET and FTIR results, the best condition
for produce Fe3O4 is with mixture of Fe2SO4 and FeSO4 (1:1); the
solution concentration is 0.25 M; pH 3 and 5 volt. It could be concluded that the Fe3O4 particles characteristics are be affected
by pH, voltage and the composition of precursor solution.
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSK 660.297 Cha s |
| Uncontrolled Keywords: | elektrokimia; partikel magnetite; chelating agent |
| Subjects: | T Technology > TD Environmental technology. Sanitary engineering > TD455 Chemical precipitation. Coagulation. Flocculation. Water--Purification--Flocculation. |
| Divisions: | Faculty of Industrial Technology > Chemical Engineering > 24201-(S1) Undergraduate Thesis |
| Depositing User: | - Taufiq Rahmanu |
| Date Deposited: | 02 Oct 2019 02:53 |
| Last Modified: | 02 Oct 2019 02:53 |
| URI: | http://repository.its.ac.id/id/eprint/70942 |
Actions (login required)
 |
View Item |