Sintesis Bahan Keramik Mg0, Zb02 TiO3 Sebagai Bahan Dielektrik Dengan Metode Pencampuran Attritor

Rani, Sefrilita Risqi Adikaning (2016) Sintesis Bahan Keramik Mg0, Zb02 TiO3 Sebagai Bahan Dielektrik Dengan Metode Pencampuran Attritor. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
1112100001-undergraduate theses.pdf - Accepted Version

Download (1MB)
[img] Text
1112100001-paperpdf.pdf - Accepted Version

Download (184kB)
[img] Text
1112100001-presentationpdf.pdf - Presentation

Download (2MB)

Abstract

Sintesis material Mg0,8Zn0,2TiO3 (MZT) dengan menggunakan metode pencampuran attritor telah berhasil dilakukan dengan variasi waktu milling 2 jam, 4 jam dan 6 jam. Pencampuran dengan attritor mill dapat menghasilkan serbuk dengan keseragaman tinggi membentuk ukuran serbuk submikronik. Keseragaman distribusi ukuran serbuk rata-rata sebesar 351,6 nm dengan lama waktu milling 6 jam. Keseragaman distribusi serbuk kalsinasi Mg0,8Zn0,2TiO3 (MZT) dengan penambahan Bi2O3 melalui proses milling 2 jam yaitu sebesar 482,8 nm. Fasa tunggal (Mg/Zn)TiO3 diperoleh melalui proses milling selama 6 jam dengan kecepatan 600 rpm dan kalsinasi pada temperatur 950oC selama 4 jam. Sintering MZT dengan penambahan 4mol% Bi2O3 pada temperatur 1100oC selama 4 jam dan 6 jam terbentuk fasa kristalin (Mg/Zn)TiO3 dan Bi4Ti3O12 (XRD) dan fasa non kristalin (SEM). Sifat dielektrik dari sampel (MZTA) dengan sintering 4 jam memiliki sifat dielektrik yang lebih baik ditandai dengan transisi polarisasi space charge ke polarisasi dipol pada frekuensi 10Hz dibandingkan dengan sampel (MZTB) dengan sintering selama 6 jam yang transisinya pada 1 KHz. Material MZT telah memenuhi spesifikasi sebagai bahan dielektrik yang dapat diaplikasikan. =========== Mg0,8Zn0,2TiO3 (MZT) material synthesis by using Attritor mill mixing method has been successfully performed by varying the milling time of 2 hours, 4 hours and 6 hours. Attritor mill mixing can gives the resulting high uniformity submicron sized powder. Distribution uniformity of the powder size by an average is of 351.6 nm with milling time up to 6 hours. Calcination powder distribution uniformity Mg0,8Zn0,2TiO3 with the addition of Bi2O3 through the milling process of 2 hours is equal to 482.8 nm. Single phase (Mg/Zn)TiO3 is obtained by milling time of 6 hours at a speed of 600 rpm and calcination at a temperature of 950oC for 4 hours. MZT sintering with the addition of 4mol% Bi2O3 at the temperature of 1100oC for 4 hours and 6 hours forming crystalline phases of (Mg/Zn)TiO3 and Bi4Ti3O12 (XRD) and non-crystalline phase (SEM). Samples MZTA with sintering time of 4 hours giving a better dielectric properties given by transition space charge polarization to the polarization dipole at a frequency of 10Hz when compared with samples (MZTB) with sintering time of 6 hours transition at 1 KHz. MZT material has met the specifications as a dielectric material eligible for applications.

Item Type: Thesis (Undergraduate)
Additional Information: RSFi 620.195 Ran s 3100016066593
Uncontrolled Keywords: Attritor milling, waktu milling, kalsinasi, sintering, milling time, calcination.
Subjects: Q Science > QC Physics > QC585 Dielectrics
Divisions: Faculty of Mathematics and Science > Physics > (S1) Undergraduate Theses