Analisa Pengaruh Fraksi Massa Terhadap Sifat Akustik Dan Kekuatan Lentur Pada Pembuatan Komposit Polyurethane/Serat Bambu Betung Dengan Metode Hand Lay-Up Untuk Aplikasi Door Panel Mobil

Ahaddin, Erdinanto Eko (2016) Analisa Pengaruh Fraksi Massa Terhadap Sifat Akustik Dan Kekuatan Lentur Pada Pembuatan Komposit Polyurethane/Serat Bambu Betung Dengan Metode Hand Lay-Up Untuk Aplikasi Door Panel Mobil. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img]
Preview
Text
2712100117-undergraduate-theses.pdf - Published Version

Download (2MB) | Preview

Abstract

Penelitian ini bertujuan untuk menganalisa material komposit polyurethane berpenguat serat bambu untuk penyerapan suara pada bagian door panel kendaraan. Permasalahan yang dikaji untuk mengetahui nilai koefisien absorpsi suara, kekuatan tarik serta kekuatan lentur dengan membandingkan variasi komposisi serat dengan matriksnya menggunakan metode hand lay up. Komposisi fraksi massa serat yang digunakan adalah 5%, 10%, 15%. Tujuannya untuk mendapatkan nilai koefisien absorpsi suara terbaik serta sifat mekanik yang baik. Metode yang digunakan berdasarkan standartd ASTM E 1050, ASTM D790, ASTM D3039. Dari hasil pengujian didapatkan nilai koefisien absorpsi suara, kekuatan lentur dan Tarik tertinggi secara berturut turut, 0.435 pada frekuensi 4000 Hz, 19.142 Mpa, 0.8 Mpa Nilai tertinggi ini didapatkan pada komposit dengan presentase 15%B-85%PU. =========================================================== Objective of this research was used to analyze bamboo fibre reinforced polyurethane composite for sound absorption used in the door panel part of the vehicle. The problem was examined to find out the value of sound absorption coefficient, tensile strength and flexural strength by comparing variation of composition reinforcement and matrix using hand lay up method. The composition of the mass fraction of the reinforcement used were 5%, 10%, 15%. The goal was to get the best sound absorption coefficient value and good mechanical properties. The methods used were based on ASTM E standartd 1050, ASTM D790, ASTM D3039. From the results was obtained by testing the sound absorption coefficient, Tensile strength and flexural strength in successive takes part, 0435 at 4000 Hz frequency, 19.142 MPa, 0.8 MPa. The highest value was obtained on composite with a percentage of 15% B-85% PU.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.112 44 Aha a-1
Uncontrolled Keywords: Sound Absorption Material, Interior, Serat Bambu, Polyurethane, Hand lay-up
Subjects: T Technology > TN Mining engineering. Metallurgy
T Technology > TN Mining engineering. Metallurgy > TN690 Metallography. Physical metallurgy
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 12 Nov 2019 08:25
Last Modified: 12 Nov 2019 08:25
URI: http://repository.its.ac.id/id/eprint/71720

Actions (login required)

View Item View Item