Supriyanto, Widi (2016) Pengaruh post heat 700c dan 900c selama 5 jam pada sambungan las SMAW, Elektroda E7016, Material SA 36 terhadap kekuatan tarik, kekerasan dan metalografi. Diploma thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text
2113030012-non degree thesis.pdf Download (2MB) | Preview |
Preview |
Text
2113030012-presentationpdf.pdf Download (1MB) | Preview |
Abstract
Salah satu permasalahan dalam pengelasan suatu material logam itu ialah apabila sebuah konstruksi bangunan yang memiliki dasar berbahan logam hasil pengelasan SMAW terkena panas bertemperatur tinggi.
Pada penelitian ini akan menganalisa mengenai pengaruh panas temperatur 700˚C dan 900˚C selama 5 jam terhadap sifat mekanis dari material SA 36 dengan pengujian tarik yang bertujuan untuk mengetahui daerah patahan dan kekuatan tarik pada spesimen, kemudian hardness test bertujuan untuk mengetahui kepastian titik batas antara daerah Base Metal, HAZ, Weld Metal, juga untuk mengetahui nilai kekerasan daerah patahan pada pengujian tarik spesimen, dan uji metalografi yang bertujuan untuk mengetahui struktur mikro pada daerah batasan Base Metal, HAZ, Weld Metal.
Dari hasil pengujian tarik, didapatkan bahwa spesimen yang terpengaruh panas pada temperatur 700˚C memiliki nilai tegangan tarik lebih besar yaitu 505,18 Mpa daripada temperatur 900˚C yang sebesar 416,58 Mpa. Dilihat dari bentuk patahannya, dapat dikatakan bahwa material bersifat ductile atau ulet. Struktur mikro yang terbentuk adalah ferrite, pearlite dan austenite.
=============================================================================================================
One of the problems in welding a metal material that is when a building construction that has a base made of metal SMAW welding results exposed to high temperature heats.
This research will analyze the effects of heat temperature 700˚C and 900˚C for 5 hours to the mechanical properties of the material SA 36 with the tensile test that aims to identify the fault area and the tensile strength of the specimen, then hardness test aims to know the boundary points between regions Base Metal, HAZ, Weld Metal, also to determine the hardness value fault line in the tensile test specimens and metallographic test which aims to determine the microstructure in the area of limitation Base Metal, HAZ, Weld Metal.
From the tensile test results, it was found that the specimen effected of heat at a temperature of 700˚C has a tensile stress value of 505.18 Mpa is larger than the 900˚C temperature of 416.58 Mpa. Judging from the shape of the fracture, it can be said that the material is ductile or ductile. Microstructure formed is ferrite, pearlite and austenite
| Item Type: | Thesis (Diploma) |
|---|---|
| Additional Information: | RSM 671.52 Sup p |
| Uncontrolled Keywords: | Pengaruh Panas, Pengelasan SMAW, Hardness Test, Uji Tarik dan Metalography Test |
| Subjects: | T Technology > TS Manufactures > TS227 Welding. |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21401-(D3) Diploma 3 |
| Depositing User: | - Taufiq Rahmanu |
| Date Deposited: | 26 Nov 2019 02:56 |
| Last Modified: | 26 Nov 2019 02:56 |
| URI: | http://repository.its.ac.id/id/eprint/72029 |
Actions (login required)
 |
View Item |