Aisyah, Astrid Delia (2015) Rekayasa Material Penyerap Gelombang Radar Berbahan Dasar Batuan Besi Laterit Dan Karbon Aktif Kulit Singkong Pada Rentang Frekuensi X Band. Undergraduate thesis, Institut Technology Sepuluh Nopember.
Preview |
Text
1111100064-Undergraduate Thesis.pdf - Published Version Download (755kB) | Preview |
Abstract
Stealth technology (teknologi siluman) merupakan suatu
teknologi yang memungkinkan kapal tidak akan terdeteksi oleh
radar (Radio Detection and Ranging) dan dapat diterapkan
dengan melapisi kapal menggunakan Radar Absorbing Material
(RAM). RAM merupakan suatu material yang mampu menyerap
gelombang elektromagnetik melalui mekanisme polarisasi
kemagnetan dan sifat induksi kelistrikan. Penelitian ini bertujan
untuk mensintesis RAM dengan menggunakan bahan baku alam
berupa batuan besi laterit hasil tambang dari Kab. Tanah Laut
Provinsi Kalimantan Selatan yang direduksi menjadi pasir besi
laterit sebagai material magnetik yang dikombinasikan dengan
material dielektrik berupa karbon aktif berbahan baku kulit
singkong. RAM pada penelitian ini merupakan campuran pasir
besi laterit-karbon aktif kulit singkong dengan variasi massa 1:1,
1:2, 2:1, 2:3 dan cat sebagai bahan perekatnya. RAM tersebut
akan dilapiskan pada plat baja grade A tipe AH36 dengan metode
pelapisan Dallenbach single layer. Penyerapan gelombang mikro
diidentifikasi dengan pengujian VNA dan didapatkan bahwa nilai
rugi refleksi maksimum terdapat pada komposisi 1:1 dengan nilai
rugi refleksi -24.2 dB pada frekuensi 12.06 GHz. Nilai rugi
refleksi variasi komposisi 1:2, 2:1 dan 2:3 masing-masing adalah
-18.01 dB, -9.51 dB dan -10.1 dB pada rentang frekuensi x band.
=========================================================================================================
Stealth technology is a technology that enables the ship
to be undetected by radar (Radio Detection and Ranging) and
can be applied by coating the ship using radar absorbing
material (RAM). RAM is a material that can absorb
electromagnetic waves through the mechanism of magnetism
polarization and the nature of electricity induction. This research
aims to synthesize RAM using natural raw material such as
laterite iron rocks from Tanah Laut district of South Kalimantan
which is reduced to laterite iron sand as magnetic material
combined with a dielectric material such as active carbon made
from cassava peel. RAM in this research is a mixture of laterite
iron sand-cassava peel’s active carbon with mass variation of 1:
1, 1: 2, 2: 1, 2: 3 and paint as an adhesive. RAM will be
superimposed on the grade A type AH36 steel plate with
Dallenbach single layer coating method. The absorption of
microwave identified by VNA testing and found that the maximum
reflection loss (RL) value contained in the composition of 1: 1
with RL value of -24.2 dB at 12:06 GHz frequency. RL value of
another variations 1: 2, 2: 1 and 2: 3 are respectively at -18.01
dB, -9.51 dB and -10.1 dB in the x band frequency range.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSFi 669.141 Ais r |
| Uncontrolled Keywords: | frekuensi x band, Radar Absorbing Material (RAM), rugi refleksi, teknologi siluman |
| Subjects: | Q Science > QC Physics > QC162 Adsorption and absorption |
| Divisions: | Faculty of Mathematics and Science > Physics > 45201-(S1) Undergraduate Thesis |
| Depositing User: | Mr. Tondo Indra Nyata |
| Date Deposited: | 12 Dec 2019 06:14 |
| Last Modified: | 12 Dec 2019 06:14 |
| URI: | http://repository.its.ac.id/id/eprint/72343 |
Actions (login required)
 |
View Item |