Pengaruh Wt% Polikarbonat Dan Proses Pembuatan Terhadap Sifat Fisik Dan Mekanik Polypropylene/Polycarnonate Blend Sebagai Material Sabot

Hasanah, Nur (2016) Pengaruh Wt% Polikarbonat Dan Proses Pembuatan Terhadap Sifat Fisik Dan Mekanik Polypropylene/Polycarnonate Blend Sebagai Material Sabot. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
Binder1.pdf - Published Version

Download (3MB) | Preview

Abstract

Sabot merupakan penunjang proyektil yang mampu melindungi laras dari gesekan proyektil serta mampu meningkatkan performa proyektil setelah lepas dari laras. Polymer blend menjadi sebuah terobosan untuk mendapatkan polimer yang memiliki sifat khusus sebagai material sabot dengan produksi lebih mudah. Pada penelitian ini polypropylene/polycarbonate blend dibentuk dengan komposisi 10, 20 dan 30 wt% polikarbonat. Pelet polipropilen dan polikarbonat dihaluskan menjadi sebuk, kemudian dimixing sesuai komposisi pada 120 rpm selama 30 menit, dilanjutkan drying pada 120 oC selama 4 jam, dan dibentuk dengan handtruder serta compression molding sesuai parameter. Peningkatan wt% PC meningkatkan distribusi PC dalam PP, meningkatkan densitas dengan densitas tertinggi pada PP/PC30 sebesar 0,955 g/cm3, dan menurunkan penyusutan menjadi 0% pada PP/PC30. PP/PC10. Hasil compression molding memiliki kekuatan tekan dan modulus elastisitas tertinggi sebesar 50,056 MPa dan 0,58 GPa, sedangkan PP/PC10 hasil handtruder memiliki kekuatan tarik sebesar 23,76 MPa dan modulus elastisitas 0,87 GPa. Sementara proses pembentukan tidak memberikan pengaruh signifikan pada polymer blend yang dihasilkan. ========================================================== Sabots are used as supports for projectiles during gun tube travel and enhance projectile performa after exit from the gun. Polymer blend is a method to get polymer which has specific characristic of sabot material with more simple production and low costIn this research, polypropylene/polycarbonate blend has composition of 10, 20, and 30 wt% polycarbonate. Polypropylene and polycarbonate pellet was grinded into powder, then mixing for each composition at 120 rpm for 30 minutes, and drying at 120 oC for 4 hours. Polymer blend is manufactured by handtruder and compression molding with each process parameter. The increasing wt% polycarbonate affect the distribution and interaction of blend component, increase density with the highest is 0,955 g/cm3 at PP/PC30, and decrease shrinkage upto 0% at PP/PC30. PP/PC10 manufacrured by compression molding has highest compressive strength and modulus elasticity 50,056 MPa and 0,58 GPa. PP/PC10 manufactured by handtruder has tensile strength 23,76 MPa and modulus elasticity 0,87 GPa. Meanwhile, manufactured process doesn’t significantly affect the polymer blend.

Item Type: Thesis (Undergraduate)
Additional Information: RSMt 620.118 Has p-1
Uncontrolled Keywords: komposisi, polypropylene/polycarbonate blend, proses pembentukan, sifat fisik, sifat mekanik
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 06 Jan 2020 07:42
Last Modified: 06 Jan 2020 07:42
URI: http://repository.its.ac.id/id/eprint/72559

Actions (login required)

View Item View Item