Pengaruh Variasi Beda Potensial dan Waktu Oksidasi terhadap Struktur, Morfologi dan Ketahanan Oksidasi Temperatur Tinggi dari Paduan Ti-6Al-4V dengan Metode Plasma Electrolytic Oxidation untuk Aplikasi Fan Blade Mesin Pesawat

Sakti, Mahesa Anggara (2020) Pengaruh Variasi Beda Potensial dan Waktu Oksidasi terhadap Struktur, Morfologi dan Ketahanan Oksidasi Temperatur Tinggi dari Paduan Ti-6Al-4V dengan Metode Plasma Electrolytic Oxidation untuk Aplikasi Fan Blade Mesin Pesawat. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511640000143-Undergraduate_Thesis.pdf - Accepted Version Download (4MB)

Abstract

Ti-6Al-4V merupakan paduan titanium yang sangat penting bagi pesawat terutama pada bagian fan blade, namun karena keterbatasan dalam ketahanan oksidasi temperatur tinggi dari paduan ini membuat pemanfaatan dari paduan ini terbatas, sehingga perlu dilakukan rekayasa permukaan Plasma Electrolytic Oxidation (PEO). Tujuan dari penelitian ini adalah menganalisis pengaruh beda potensial dan waktu oksidasi terhadap struktur, morfologi dan ketahanan oksidasi temperatur tinggi paduan Ti-6Al-4V yang dioksidasi dengan PEO. Dalam penelitian ini variasi beda potensial yang diterapkan adalah 150V, 200V, dan 250V sedangkan untuk variasi waktu oksidasi yang digunakan adalah 4 menit, 8 menit, dan 12 menit. Fasa yang terbentuk berdasarkan hasil XRD adalah TiO2 (Rutile), TiO2 (Anatase) dan SiO2 amorphous dengan peningkatan fasa TiO2 (Rutile) seiring peningkatan beda potensial dan waktu oksidasi. Pengujian SEM/EDX menunjukkan lapisan oksida terdiri dari unsur Ti, Si, O, Al, dan Na, sedangkan untuk morfologi lapisan oksida mengalami peningkatan diameter pori, porositas, dan ketebalan lapisan oksida seiring dengan meningkatnya beda potensial dan waktu oksidasi. Pengujian oksidasi temperatur tinggi pada 700oC selama 5 jam menunjukkan bahwa sampel dengan variasi 150V-8 Menit memiliki ketahanan oksidasi temperatur tinggi terbaik yaitu 0,225 mg/cm2.
===============================================================================================================================
Ti-6Al-4V is a titanium alloy that is very important for fan blade in aircraft machine, but due to its limitations in high temperature oxidation makes the application of this alloy limited, so it is necessary to do the Plasma Electrolytic Oxidation (PEO). The purpose of this study was to analyze the voltage and oxidation time effect to structure, morphology and high temperature oxidation resistance of Ti-6Al-4V alloys that were oxidized with PEO. In this study the voltage variations used were 150V, 200V, and 250V while the oxidation time variations used were 4 minutes, 8 minutes and 12 minutes. Phases formed based on XRD results are TiO2 (Rutile), TiO2 (Anatase), and amorphous SiO2 with an increasing in TiO2 (Rutile) phase as voltage and oxidation time increase . SEM / EDX testing shows the oxide layer consists of Ti, Si, O, Al, and Na elements, while the morphology of the oxide layer like pores diameter, porosity, and thickness of the oxide layer increasing as voltage and oxidation time increase. Testing of high oxidation temperature at 700oC for 5 hours showed samples with variations of 150V-8 minutes had the best high temperature oxidation resistance of 0,225 mg /cm2.

Item Type:	Thesis (Other)
Additional Information:	RSMt 669.722 Sak p-1 2020
Uncontrolled Keywords:	Fan blade, Plasma Electrolytic Oxidation, Voltage, Ti-6Al-4V, Oxidation Time.
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ561 Surface T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL671.9 Airplanes--Maintenance and Repair T Technology > TS Manufactures > TS176 Manufacturing engineering. Process engineering (Including manufacturing planning, production planning) T Technology > TS Manufactures > TS699 Powder coating of metals
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mahesa Anggara Sakti
Date Deposited:	07 Mar 2023 03:22
Last Modified:	08 May 2023 02:56
URI:	http://repository.its.ac.id/id/eprint/73124

Actions (login required)

View Item