Ardiansyah, Mutafawwiqin Rizqoni (2016) Studi Eksperimental Variasi Komposisi Pelet Biokomposit ( Polypropylene, Sekam Padi Dan Maleic Anhydride Pp ) Terhadap Sifat Thermal & Struktur Permukaan Sebagai Material Alternatif Produk Plastik Mutafawwiqin Rizqoni Ardiansyah Nrp 2112 100 058 Dosen Pembimbing Prof.Dr.Ing Ir I Made Londen Batan M.Eng. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.
Preview |
Text
2112100058-Undergraduate_Thesis.pdf - Published Version Download (2MB) | Preview |
Abstract
Plastik adalah salah satu bahan baku yang diperoleh melalui proses sintesi dari berbagi bahan mentah, yaitu minyak bumi, gas bumi dan bahan batu bara. Pada saat itu kebutuhan plastik dunia mencapai sembilan juta ton per tahun, pada tahun 2000 kebutuhan dunia akan plastik mencapai 170 juta ton dan volume produksi polyethylene (biji plastik) per tahun mencapai 320.000 ton, atau 40% (terbesar di Indonesia) dari produksi biji besi nasional pada tahun 2014 (www.pikiran-rakyat.com). Dari studi banding yang dilakukan khusunya pada industri / Usaha Kecil dan Menengah ( UKM ) pembuatan helm di Mojokerto pada bulan maret 2016 diketahui bahwa harga dari material plastic / resin sangat tinggi ( mahal ). Disamping itu akibat limbah resin ( material pembuat produk plastic) mencemari lingkungan. Akibatnya banyak industri tersebut yang gulung tikar dan beberapa beralih menjadi pengrajin helm, yaitu batok / sungkup helm dibeli dari pabrik, kemudian dilengkapi dengan aksessories menjadi helm kendaraan bermotor.Sehingga mereka tidak lagi membuat helm karena biaya material yang mahal.
v
Oleh karena itu tugas akhir ini berusaha menjawab permasalah tersebut dengan tujuan mengetahui sifat termal dari masing – masing variasi komposisi material biokomposi dan mengetahui struktur permukaan pada pemotongan melintang masing – masin variasi material biokomposit Metode yang digunakan pada penelitian tugas akhir ini adalah membuat campuran PP, MAPP dan sekam padi dengan komposisi PP sebagai berikut : RH berturut – turut 90 % PP 5% RH dan 5% MAPP, 85%PP 10% RH dan 5% MAPP, 80% PP 15% RH dan 5 % MAPP, 75 % PP 20% RH dan 5%MAPP, yang akan dicetak menjadi pellet menggunakan Mesin Screw extruder merk Labo Plastomill 4C150 di laboratorium Teknik Material dan Metalurgi ITS. Selanjutnya setelah menjadi pellet akan diuji menggunakan Mesin Mettler Toledo untuk menganalisa sifat termalnya dan dengan Mikroskop diuji untuk mendapat informasi voids pada permukaan pellet. Hasil dari studi eksperimental ini adalah didapatkan temperatur leleh variasi komposisi biokomposit berturut – turut yaitu 163,6 oC 164,2 oC, 163,3 oC, dan 163,1 oC. Sedangkan pada struktur permukaan didapat jumlah voids antara lain : 7,215 %, 14,279 %, 18,205 %, dan 26,569 %. Dari hasil diatas dapat diketahui bahwa kualitas pellet baik apabila ditinjau dari jumlah void paling sedikit maka terdapat pada pelet biokomposit A
=============================================================================================
Plastic is one of the raw materials that acquired through the process of synthesis raw materials( oil, gas and coal ). At that time the world's plastic needs reach nine million tones per year, in 2000 the world needs 170 million tons of plastic and volume production of polyethylene (plastic seed) per year reached 320,000 tons, or 40% (the largest in Indonesia) from iron seed production nationwide by 2014 (www.pikiran-rakyat.com). From the comparative study on the small home industry helmets on Mojokerto in March 2016. Note that the price of the material plastic/resin is very high (expensive). Beside that, due to the resin wastes (material plastic products maker) pollute the environment. As a result many industrial closed and some switched into the helmet shell that purchased from company. Then they were completing with accessories into the helmet . So, they no make the Plastic helmet because of the cost was very expensive. Therefore this final project tries to answer the problem with the purpose of knowing the thermal properties of each material composition variation of bio-composite and knowing the structure of the surface with
vii
transverse cuts at each variations of the material – biocomposite. The methods that used in the research is to create a mix of PP, MAPP and rice husk. Composition as follows: 90% PP 5% RH and 5% MAPP, 85% PP 10% RH and 5% MAPP, 80% PP 15% RH and 5% MAPP, 75% PP 20% RH and 5% MAPP, which will be pellets using Screw extruder Machine ( Plastomill 4C150 Labo brand ) in the laboratory of Metallurgical and materials engineering ITS. Next, pellets will be tested using DSC to analyses the properties of thermal and microscope tested to obtain information voids on the su rface of the pellet. The results of this experimental study is obtained by melting temperature variations in the composition are 163.6 oC 164.2 oC 163.3 oC, and 163.1 oC. While on the surface structure obtained number of voids, that are 7.215%, 14.279%, 18.205% , and% 26.569. From the results above, it can be noted that the quality of the pellets both with least number of voids is on pellet bio-composite A
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSM 620.192 042 23 Ard s |
| Uncontrolled Keywords: | Polypropylene, Sekam Padi ,Maleic Anhydrite, Biokomposit |
| Subjects: | T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials T Technology > TP Chemical technology > TP1140 Polymers |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis |
| Depositing User: | EKO BUDI RAHARJO |
| Date Deposited: | 09 May 2020 02:10 |
| Last Modified: | 09 May 2020 02:10 |
| URI: | http://repository.its.ac.id/id/eprint/75946 |