Tardas, Mikhael (2015) Analisis Penggunaan Limbah Batu Bara Tersolidifikasi Sebagai Material Pengganti Filler Dalam Campuran Aspal Beton. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.
Preview |
Text (Access closed by author)
3111100140-Undergraduate_Thesis.pdf - Accepted Version Download (1MB) | Preview |
Abstract
Penggunaan limbah batu bara yang sudah banyak
digunakan sebagai material pengganti filler dalam campuran
aspal beton.Limbah batu bara yang tersolidfikasi perlu diteliti
karakteristiknya apabila dicampur dalam aspal beton. Tujuan
dari penelitian ini adalah mengetahui bagaimana mencampurkan
limbah batu bara tersolidifikasi atau geopolimer dalam hotmix
asphalt. Disamping itu untuk mendapatkan hasil analisis
pencampuran geopolimer untuk mendapatkan perbandingan nilai
stabilitas dan kelelehan dari campuran yang menggunakan
geopolimer dan campuran yang tidak menggunakan geopolimer.
Nilai stabilitas dan kelelehan dari campuran ini akan menentukan
baik tidaknya geopolimer digunakan sebagai material dalam
perkerasan lentur. Dalam penelitian ini,tahap awal adalah
mencari kelayakan dari material yang digunakan seperti agregat
kasar, agregat halus, filler dan aspal. Setelah semua material
memenuhi persyaratan dilanjutkan dengan tahap mencari mix
desain awal. Mix desain ini tanpa menggunakan filler geopolimer
dan menggunakan perkiraan kadar aspal. Dari penelitian ini
didapatkan hasil bahwa penggunaan geopolimer meningkatkan
stabilitas dalam campuran aspal namun mengurangi nilai kelelehan dan menambah rongga di dalam campuran. Walaupun
nilai kelelehannya turun dan rongga di dalam campurannya
semakin banyak, hasil yang di dapat masih memenuhi spesifikasi
mínimum campuran aspal beton dengan tingkat lalu lintas berat.
==================================================================================================================
Using of coal waste as an alternative filler material has
been used in asphalt concrete mix. A research must need to see
the characteristic of coal waste that has been solidificate as filler
mixed in asphalt concrete. The reason of this research is there are
significant improvement of mixing coal waste as a filler in asphalt
concrete, in addition to utilize waste material as a substitute
material in road pavement. This feasibility study elaborates how
to combine a geoplymer in asphalt hotmix and to obtain the
analysis of geopolymer mixture regarding flexible pavement to get
comparative stability and melting value by geopolymer and nongeoplymer mixtures. Stability and melting value from this mixture
will determine the quality of geoploymer as an alternative
material for flexible pavement. The first step in this study is to find
feasibility of material that will be use for asphalt concrete mix
like, coarse aggregate, fine aggregate, filler, and asphalt. After all
material sufficient for specification the next step is to search for
outset mix design. This mix design not include geopolymer as
filler and still use estimate composition of asphalt. Result of this
study show that geopolymer can be used as filler in asphalt
concrete because it increase the stability of the mix. Although it
decrease flow and increase void in mix, the values are sufficient for the mínimum specification for heavy load traffic for asphalt
concrete.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSS 666.893 Tar a |
| Uncontrolled Keywords: | Geopolimer; hot mix asphalt; limbah batu bara; filler alternatif |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA443.A7 Asphalt |
| Divisions: | Faculty of Civil Engineering and Planning > Civil Engineering > 22201-(S1) Undergraduate Thesis |
| Depositing User: | ansi aflacha |
| Date Deposited: | 13 May 2020 05:55 |
| Last Modified: | 18 Apr 2024 10:38 |
| URI: | http://repository.its.ac.id/id/eprint/75977 |
Actions (login required)
 |
View Item |