Studi Eksperimen Pengaruh Tekanan Dan Waktu Sandblasting Terhadap Kekasaran Permukaan, Biaya, Dan Kebersihan Pada Plat Baja Karbon Rendah Di Pt Swadaya Graha

Pradana, Rizky Bagus (2016) Studi Eksperimen Pengaruh Tekanan Dan Waktu Sandblasting Terhadap Kekasaran Permukaan, Biaya, Dan Kebersihan Pada Plat Baja Karbon Rendah Di Pt Swadaya Graha. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.

[img]
Preview
Text
2114105050-Undergraduate_Thesis.pdf - Published Version

Download (1MB) | Preview

Abstract

Suatu perusahaan yang bergerak di bidang industri manufaktur pasti membutuhkan proses finishing guna untuk mendapatkan hasil yang maksimal dalam pembuatan produk. Dalam proses ini membutuhkan peralatan yang mampu untuk memenuhi kebutuhan utama yaitu proses finishing. Pemilihan mesin dan alat yang sesuai dapat membantu kemudahan, keringanan biaya, serta kecepatan dalam pengerjaan. Berhubungan dengan hal tersebut proses sandblasting sangat sesuai karena proses ini dapat mengerjakan benda kerja dengan ukuran yang besar dan rumit, seperti chasis, bagian dinding kapal, pesawat, mobil dan gerbong kereta akan menjadi mudah dan cepat. Proses sandblasting ini dilakukan untuk mendapatkan nilai kekasaran yang baik. Parameter yang digunakan adalah tekanan kompressor 4 bar, 5 bar, dan 6 bar dengan waktu sandblasting 10 detik, 15 detik, dan 20 detik pada material baja karbon yang memiliki dimensi 250 mm x 250 mm x 6 mm. Nilai kekasaran yang diinginkan sesuai dengan spek yang tertera di cat Jotun. Nilai kekasaran dari cat Jotun berkisar antara 30 - 85μm. Pada eksperimen ini, metode eksperimen RAL (Rancangan Acak Lengkap) digunakan untuk mendapatkan rancangan yang sesuai serta menggunakan ANOVA (Analysis Of Variance) sebagai hasil analisa mendapatkan kombinasi yang sesuai dengan standart perusahaan antara tekanan dan waktu yang berbeda. Hasil yang dilakukan penelitian ini, menunjukkan bahwa kekasaran terendah terdapat pada tekanan kompressor 4 bar dengan waktu sandblasting 10 detik yaitu 45,5μm. Sedangkan kekasaran tertinggi terdapat proses sandblasting dengan tekanan kompressor 6 bar dengan waktu sandblasting 20 detik yaitu 76μm. Pada proses sandblasting yang dilakukan didapat biaya termurah pada tekanan kompressor 4 bar dengan waktu sandblasting 10 detik yaitu Rp 2.996,- dan biaya tertinggi pada tekanan kompressor 6 bar dengan waktu sandblasting 20 detik yaitu Rp 4.674,-. Proses sandblasting menghasilkan kebersihan terendah pada tekanan kompressor 4 bar dengan waktu sandblasting 10 detik yaitu Sa 2 dan kebersihan tertinggi pada tekanan kompressor 5 bar dengan waktu sandblasting 15 detik, tekanan komprssor 6 bar dengan waktu sandblasting 20 detik ============================================================================================ A company engaged in the manufacturing industry definitely requires a finishing process in order to get maximum results in the manufacture of products. In these processes require equipment that is able to meet the main needs is the finishing process. Selection of appropriate machinery and tools that can help ease, fee waivers, and speed in execution. Dealing with such matters sandblasting process is very suitable for this process can work on workpieces with a large size and complex, such as chassis, parts of the walls of the ship, plane, car and train cars will be easier and faster. Sandblasting process is performed to obtain a good roughness value. The parameters used are pressure compressor 4 bars, 5 bars, and 6 bar with sandblasting time of 10 seconds, 15 seconds, and 20 seconds on carbon steel material which has dimensions of 250 mm x 250 mm x 6 mm. Desired roughness value in accordance with the specification listed in Jotun paint. Jotun paint roughness value of between 30 - 85μm. In this experiment, the experimental method RAL (Complete Random Design) is used to obtain the appropriate design and using ANOVA (Analysis Of Variance) as a result of the analysis get the combination in accordance with company standards of pressure and a different time. The results of this research, shows that the roughness was lowest for the compressor pressure of 4 bar with a time of 10 seconds is 45,5μm sandblasting. While the highest roughness there is a process of sandblasting with 6 bar pressure compressor with a time of 20 seconds sandblasting is 76μm. In the process of sandblasting is done obtained the lowest costs at a pressure of 4 bar compressor with a time of 10 seconds sandblasting is Rp 2,996, - and the highest cost at a pressure of 6 bar compressor with a time of 20 seconds sandblasting is Rp 4,674, -. Sandblasting process produces the lowest cleanliness at a pressure of 4 bar compressor with a time of 10 seconds is sandblasting Sa 2 and the highest hygiene at a pressure of 5 bar compressor with a time of 15 seconds sandblasting, komprssor pressure of 6 bar with sandblasting time of 20 seconds.

Item Type: Thesis (Undergraduate)
Additional Information: RSM 621.54 Pra s-1
Uncontrolled Keywords: ANOVA, Kebersihan Permukaan, Kekasaran Permukaan, Kombinasi tekanan kompressor, Sandblasting.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion
T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions: Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User: EKO BUDI RAHARJO
Date Deposited: 16 Jul 2020 02:35
Last Modified: 16 Jul 2020 02:35
URI: http://repository.its.ac.id/id/eprint/76387

Actions (login required)

View Item View Item