Pradana, Rizky Bagus (2016) Studi Eksperimen Pengaruh Tekanan Dan Waktu Sandblasting Terhadap Kekasaran Permukaan, Biaya, Dan Kebersihan Pada Plat Baja Karbon Rendah Di Pt Swadaya Graha. Undergraduate thesis, Institut Teknologi Sepuluh Nopember Surabaya.
Preview |
Text
2114105050-Undergraduate_Thesis.pdf - Published Version Download (1MB) | Preview |
Abstract
Suatu perusahaan yang bergerak di bidang industri
manufaktur pasti membutuhkan proses finishing guna untuk
mendapatkan hasil yang maksimal dalam pembuatan produk.
Dalam proses ini membutuhkan peralatan yang mampu untuk
memenuhi kebutuhan utama yaitu proses finishing. Pemilihan
mesin dan alat yang sesuai dapat membantu kemudahan,
keringanan biaya, serta kecepatan dalam pengerjaan.
Berhubungan dengan hal tersebut proses sandblasting sangat
sesuai karena proses ini dapat mengerjakan benda kerja dengan
ukuran yang besar dan rumit, seperti chasis, bagian dinding kapal,
pesawat, mobil dan gerbong kereta akan menjadi mudah dan
cepat.
Proses sandblasting ini dilakukan untuk mendapatkan
nilai kekasaran yang baik. Parameter yang digunakan adalah
tekanan kompressor 4 bar, 5 bar, dan 6 bar dengan waktu
sandblasting 10 detik, 15 detik, dan 20 detik pada material baja
karbon yang memiliki dimensi 250 mm x 250 mm x 6 mm. Nilai kekasaran yang diinginkan sesuai dengan spek yang tertera di cat
Jotun. Nilai kekasaran dari cat Jotun berkisar antara 30 - 85μm.
Pada eksperimen ini, metode eksperimen RAL (Rancangan Acak
Lengkap) digunakan untuk mendapatkan rancangan yang sesuai
serta menggunakan ANOVA (Analysis Of Variance) sebagai hasil
analisa mendapatkan kombinasi yang sesuai dengan standart
perusahaan antara tekanan dan waktu yang berbeda.
Hasil yang dilakukan penelitian ini, menunjukkan bahwa
kekasaran terendah terdapat pada tekanan kompressor 4 bar
dengan waktu sandblasting 10 detik yaitu 45,5μm. Sedangkan
kekasaran tertinggi terdapat proses sandblasting dengan tekanan
kompressor 6 bar dengan waktu sandblasting 20 detik yaitu 76μm.
Pada proses sandblasting yang dilakukan didapat biaya termurah
pada tekanan kompressor 4 bar dengan waktu sandblasting 10
detik yaitu Rp 2.996,- dan biaya tertinggi pada tekanan
kompressor 6 bar dengan waktu sandblasting 20 detik yaitu Rp
4.674,-. Proses sandblasting menghasilkan kebersihan terendah
pada tekanan kompressor 4 bar dengan waktu sandblasting 10
detik yaitu Sa 2 dan kebersihan tertinggi pada tekanan kompressor
5 bar dengan waktu sandblasting 15 detik, tekanan komprssor 6
bar dengan waktu sandblasting 20 detik
============================================================================================
A company engaged in the manufacturing industry
definitely requires a finishing process in order to get maximum
results in the manufacture of products. In these processes require
equipment that is able to meet the main needs is the finishing
process. Selection of appropriate machinery and tools that can
help ease, fee waivers, and speed in execution. Dealing with such
matters sandblasting process is very suitable for this process can
work on workpieces with a large size and complex, such as chassis,
parts of the walls of the ship, plane, car and train cars will be
easier and faster.
Sandblasting process is performed to obtain a good
roughness value. The parameters used are pressure compressor 4
bars, 5 bars, and 6 bar with sandblasting time of 10 seconds, 15
seconds, and 20 seconds on carbon steel material which has
dimensions of 250 mm x 250 mm x 6 mm. Desired roughness value
in accordance with the specification listed in Jotun paint. Jotun
paint roughness value of between 30 - 85μm. In this experiment,
the experimental method RAL (Complete Random Design) is used
to obtain the appropriate design and using ANOVA (Analysis Of Variance) as a result of the analysis get the combination in
accordance with company standards of pressure and a different
time.
The results of this research, shows that the roughness was
lowest for the compressor pressure of 4 bar with a time of 10
seconds is 45,5μm sandblasting. While the highest roughness there
is a process of sandblasting with 6 bar pressure compressor with a
time of 20 seconds sandblasting is 76μm. In the process of
sandblasting is done obtained the lowest costs at a pressure of 4
bar compressor with a time of 10 seconds sandblasting is Rp 2,996,
- and the highest cost at a pressure of 6 bar compressor with a time
of 20 seconds sandblasting is Rp 4,674, -. Sandblasting process
produces the lowest cleanliness at a pressure of 4 bar compressor
with a time of 10 seconds is sandblasting Sa 2 and the highest
hygiene at a pressure of 5 bar compressor with a time of 15 seconds
sandblasting, komprssor pressure of 6 bar with sandblasting time
of 20 seconds.
| Item Type: | Thesis (Undergraduate) |
|---|---|
| Additional Information: | RSM 621.54 Pra s-1 |
| Uncontrolled Keywords: | ANOVA, Kebersihan Permukaan, Kekasaran Permukaan, Kombinasi tekanan kompressor, Sandblasting. |
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA467 Iron and Steel Corrosion and protection against corrosion T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment |
| Divisions: | Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis |
| Depositing User: | EKO BUDI RAHARJO |
| Date Deposited: | 16 Jul 2020 02:35 |
| Last Modified: | 16 Jul 2020 02:35 |
| URI: | http://repository.its.ac.id/id/eprint/76387 |
Actions (login required)
 |
View Item |