Review Jenis Material Radiopak dan Pengaruh Penambahannya Terhadap Sifat Mekanik Dan Biokompatibilitas Material Untuk Pengganti Nucleus Pulposus

Fitriana, Rosa Dewi (2020) Review Jenis Material Radiopak dan Pengaruh Penambahannya Terhadap Sifat Mekanik Dan Biokompatibilitas Material Untuk Pengganti Nucleus Pulposus. Undergraduate thesis, Institut Teknologi Sepuluh Nopember.

[img] Text
02511640000032-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (1MB) | Request a copy

Abstract

Metode diskektomi atau fusi tulang yang digunakan untuk menangani penyakit tulang belakang akibat degenerasi intervertebral disc (IVD) berpotensi memperburuk kondisi disk. Sehingga, mulai dikembangkan solusi alternatif untuk mengatasi masalah tersebut yaitu dengan penggantian nucleus pulposus, salah satu bagian dari IVD dengan anatomi paling sederhana. Salah satu kriteria yang harus dimiliki material pengganti nucleus pulposus adalah sifat radiopak agar dapat terlihat pada radiografi dan mempermudah perawatan. Beberapa material radiopak yang banyak digunakan adalah ZrO2, BaSO4, yodium, dan Bi2O3. Pada review ini dilakukan analisis mengenai pengaruh penambahan material radiopak pada material untuk pengganti nucleus pulposus dengan meninjau hasil pemindaian sinar-x, kekuatan mekanik, dan juga biokompatibilitas. Keempat jenis material radiopak tersebut dapat menghasilkan gambar yang kontras dan jelas pada pemindaian sinar-x, meningkatkan kekuatan tarik dan modulus young, namun menurunkan kekuatan tekan, hanya yodium yang meningkatkan kekuatan tekan. Dari pengujian biokompatibilitas, material radiopak tersebut menunjukkan biokompatibilitas yang cukup baik dari pengujian secara in vivo maupun in vitro. ================================================================================================================== Discectomy or bone fusion procedure that are used to cure the lower back pain due to intervertebral disc degeneration potentially worsening the condition of the disc. Thus, an alternative solution was developed to overcome this problem by replacing the nucleus pulposus, the simplest part of intervertebral disc. One of the criteria that must be possessed by the nucleus pulposus replacement material is the radiopaque, so that the material can be seen on radiograph and simplifies the implantation process. Some of the most commonly used radiopacifiers are zirconium oxide, barium sulphate, iodine, and bismuth oxide. This paper review analyzes the effect of adding radiopacifiers to nucleus pulposus replacement material by considering the results of x-ray scanning, mechanical properties, and biocompatibility. These radiopacifiers can provide adequate radiopacity, increase tensile strength and Young modulus, but decrease compressive strength. Only iodine that increase the compressive strength. According to biocompatibility test, these radiopacifiers exhibit good biocompatibility in vivo and in vitro.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: biokompatibilitas, intervertebral disc (IVD), material radiopak, nucleus pulposus, sifat mekanik, biocompatibility, intervertebral disc (IVD), mechanical properties, nucleus pulposus, radiopacifier.
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials.
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Rosa Dewi Fitriana
Date Deposited: 12 Aug 2020 03:29
Last Modified: 12 Aug 2020 03:29
URI: http://repository.its.ac.id/id/eprint/77570

Actions (login required)

View Item View Item