Pengaruh Struktur Mikro Baja SA 210 Grade A1 Terhadap Penyerapan Hidrogen Menggunakan Metode Cyclic Voltammetry

Residena, Fariza Julio (2021) Pengaruh Struktur Mikro Baja SA 210 Grade A1 Terhadap Penyerapan Hidrogen Menggunakan Metode Cyclic Voltammetry. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111640000151-Undergraduate_Thesis.pdf - Accepted Version Download (7MB)

Abstract

Pipa baja karbon yang digunakan untuk mensirkulasi fluida air pada boiler yang kemudian dipanaskan menjadi uap panas sering kali mengalami kerusakan. Mekanisme kerusakan yang paling sering terjadi diakibatkan oleh hydrogen damage. Kerusakan akibat hydrogen damage dapat disebabkan oleh beberapa faktor, salah satu contohnya adalah penyerapan hidrogen kedalam struktur mikro baja karbon dan menyebabkan penggetasan hidrogen. Kerusakan ini dapat mengakibatkan kerugian yang sangat besar karena membuat sistem harus shutdown. Oleh karena itu perlu dilakukan penelitian mengenai pengaruh struktur mikro material baja terhadap penyerapan hidrogen.
Tahap penelitian dilakukan dengan beberapa langkah yang bertujuan untuk mengetahui pengaruh struktur mikro baja SA 210 grade A1 terhadap penyerapan hidrogen dan mengetahui perubahan struktur mikro baja SA 210 grade A1 akibat penyerapan hidrogen. Tahap awal adalah penyiapan spesimen menjadi tiga variasi struktur mikro. Kemudian dilakukan pengujian untuk mengetahui perubahan yang didapat sebelum dan setelah uji penyerapan hidrogen. Pengujian metalografi dilakukan untuk melihat struktur mikro awal dan perubahannya setelah dilakukan uji penyerapan hidrogen; pengujian kekerasan untuk mengetahui perubahan nilai kekerasan spesimen sebelum dan setelah uji penyerapan hidrogen; pengujian SEM-EDS hanya dilakukan X

setelah uji penyerapan hidrogen untuk melihat lapisan oksida dan unsur yang terkandung pada spesimen.
Dalam penelitian ini yang ditujukan untuk mengetahui pengaruh struktur mikro baja SA 210 grade A1, yang digunakan sebagai pipa baja pada waterwall tube, terhadap penyerapan hidrogen dan pengaruh pengujian Electrochemical Hydrogenation Test terhadap sifat mekaniknya. Pada penelitian ini didapatkan beberapa kesimpulan yaitu struktur mikro dan perlakuan terhadap spesimen dapat mempengaruhi penyerapan hidrogen, dibuktikan dengan grafik CV before-after H-absorption pada setiap variasi spesimen uji dan spesimen kode N-2 dengan variasi perlakuan normalizing memiliki kemampuan absorpsi konsentrasi hidrogen yang paling tinggi, dibandingkan dengan spesimen kode BM-2 dan Q-2. Hal ini berarti spesimen kode Q-2 dengan variasi perlakukan quenching memiliki ketahanan yang paling tinggi terhadap hydrogen damage.
==================================================================================================================================
The carbon steel pipe used to circulate air-fluid at a boiler which is then heated into hot steam is often damaged. The worst damage was caused by hydrogen damage. Damage due to hydrogen damage can be caused by several factors, one of the causes is the absorption of hydrogen in the microstructure of carbon steel and causes hydrogen embrittlement. This damage can result in huge losses because it makes the system have to shut down. Therefore, it is necessary to do research on the effect of the microstructure of steel materials on hydrogen absorption.
The research phase was carried out with several steps aimed at seeing the effect of the microstructure of SA 210 grade A1 Steel on hydrogen absorption and changes in the microstructure of SAE 210 grade A1 due to hydrogen. The initial stage is to prepare the specimen into three variations of the microstructure. Metallographic testing is done to see the initial microstructure used as a variation of the test; hardness testing to measure changes in hardness before and after the hydrogen absorption test; SEM-EDS testing is only carried out after the hydrogen absorption test to see the oxide layer and elements contained in the specimen.
In this study, this research aims to determine the effect of the microstructure of SA 210 grade A1 Steel, which is used as a steel pipe in the water-wall tube, on the absorption of hydrogen and the XII

effect of the Electrochemical Hydrogenation Test on its mechanical properties. Some conclusions were obtained that the microstructure and treatment of specimens could affect the absorption of hydrogen, as evidenced by the CV before-after H-absorption graph for each variation of the test specimens and N-2 code specimens with normalizing treatment variations had the highest absorption ability of hydrogen concentration, compared with specimens coded BM-2 and Q-2. This means that specimen coded Q-2 with a variety of quenching treatments have the highest resistance to hydrogen damage.

Item Type:	Thesis (Other)
Additional Information:	RSM 671.36 Res p-1 2021
Uncontrolled Keywords:	struktur mikro, penyerapan hidrogen, electrochemical hydrogenation test, cyclic voltammetry, baja SA 210 grade A1, microstructure, hydrogen absorption, electrochemical hydrogenation test, cyclic voltammetry, SA 210 grade A1 steel
Subjects:	T Technology > TN Mining engineering. Metallurgy > TN752.I5 Steel--Heat treatment
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	- Davi Wah
Date Deposited:	13 Jun 2023 06:10
Last Modified:	13 Jun 2023 06:10
URI:	http://repository.its.ac.id/id/eprint/98098

Actions (login required)

View Item