Optimalisasi fraksi volume TiO2 anatase dan rutile terhadap efisiensi DSSC (Dye Sensitized Solar Cell)

Lestari, Bibit (2014) Optimalisasi fraksi volume TiO2 anatase dan rutile terhadap efisiensi DSSC (Dye Sensitized Solar Cell). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2410100058_Undergraduate_Thesis.pdf Download (1MB)

Abstract

Sinergi antara fase anatase dan rutile TiO2 dapat meningkatkan pengumpulan cahaya dan efisiensi dari DSSC. Dye sensitized solar cell dibuat dari campuran fase anatase dan rutile TiO2 nanopartikel yang disintesis menggunakan metode co-precipitation dengan prekusor TiCl3. TiO2 dikalsinasi pada suhu 400 oC dan 1000 oC untuk mendapatkan fase anatase dan rutile. Ukuran partikel fase anatase dan rutile yang didapatkan masing-masing 30 nm dan 44,9 nm. Penelitian ini menggunakan pewarna alami yang mengandung pigmen anthosianin, yaitu kulit manggis dan Rhoeo spatachea yang diekstrak dengan pelarut ethanol menggunakan soklet. Pewarna alami dikarakterisasi menggunakan UV-Vis, dari hasil UV-Vis didapatkan absorpsi panjang gelombang 392,5 nm untuk kulit manggis dan untuk pewarna Rhoeo spatachea sebesar 432 nm dan 658 nm. Dari hasil pengujian di bawah sinar matahari, DSSC yang menghasilkan efisiensi terbaik adalah DSSC yang menggunakan rasio anatase/rutile sebesar 90%:10% dengan efisiensi 0,076% untuk pewarna kulit manggis dan 0,063% untuk pewarna Rhoeo spatachea. Sedangkan DSSC dengan yang menggunakan campuran pewarna kulit manggis dan Rhoeo spatachea (20%:80%) menghasilkan efisiensi 0,088%. Efisiensi tinggi yang dihasilkan oleh rasio 90%:10% dikarenakan luas permukaannya yang besar (155,654 m2/g) dan ukuran partikelnya yang kecil (9,11 nm).
=================================================================================================================================
A synergistic effect between anatase and rutile TiO2 is known to be able to improve light harvesting and efficiency of DSSC. Dye sensitized solar cell (DSSC) was fabricated using mixture of anatase–rutile phase of TiO2 nanoparticles prepared through co-precipitation method with TiCl3 precursors. TiO2 was calcined at temperatures of 400 oC and 1000 oC to obtain anatase and rutile phases, respectively. The particles size obtained were 30 nm and 44,9 nm for anatase and rutile, respectively. Present research use natural dye containing anthocyanin pigment, namely Garcinia mangostana and Rhoeo spatachea extracted using ethanol solvent in a soxhlet. These dyes werecharacterized by using UV-Vis resulting in optimum absorbance at wavelenghts of 392.5 and 423-658 nm for Garcinia mangostana andRhoeo spatachea, respectively. The best DSSC performance has anatase/rutile ratio of 90%:10%, with highest conversion efficiencies of 0,076% and 0,063% were obtained for samples sensitized with Garcinia mangostana extract and Rhoeo spatachea extract, respectively. While, DSSC employing mixed Garcinia mangostana and Rhoeo spatachea extract has efficiency of 0,088%. The ratio 90%:10% has the largest surface area (155, 654 m2/g) and smallest particle size (9,11 nm).

Item Type:	Thesis (Other)
Additional Information:	RSF 621.312 44 Les o-2014
Uncontrolled Keywords:	DSSC, anatase, rutile, kulit manggis, Rhoeo spatachea, Rasio, anatase, rutile, garcinia mangostana, Rhoeo spatachea, ratio
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2960 Dye-sensitized solar cells. Solar batteries. Solar cells
Divisions:	Faculty of Industrial Technology > Physics Engineering > 30201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	20 Jun 2023 07:47
Last Modified:	20 Jun 2023 07:47
URI:	http://repository.its.ac.id/id/eprint/98146

Actions (login required)

View Item