Analisis Pengaruh Rasio Katalis:CPO dan Jenis Katalis (γ-Al2O3, HZSM-5, ZEOLIT USY) Pada Proses Catalytic Cracking CPO Terhadap Yield dan Viskositas Biogasoline

Hamdi, Haris Al (2023) Analisis Pengaruh Rasio Katalis:CPO dan Jenis Katalis (γ-Al2O3, HZSM-5, ZEOLIT USY) Pada Proses Catalytic Cracking CPO Terhadap Yield dan Viskositas Biogasoline. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511940000041-Undergraduate_Thesis.pdf Download (4MB)

Abstract

Bahan bakar fosil merupakan salah satu sumber energi yang berfungsi sebagai energi penggerak alat transportasi sehari-hari yang angka kebutuhannya terus mengalami peningkatan dari tahun ke tahun namun berbanding terbalik dengan jumlah produksi minyak bumi di Indonesia yang cenderung mengalami penurunan selama sepuluh tahun terakhir karena sumur-sumur utama produksi minyak bumi umurnya sudah tua sehingga berpotensi terjadi kelangkaan bahan bakar fosil. Untuk mengatasi hal tersebut, salah satu inovasi yang dapat dikembangkan adalah dengan meningkatkan produksi bahan bakar alternatif biogasoline dari Crude Palm Oil (CPO). Metode pada penelitian ini menggunakan catalytic cracking sehingga dapat merengkah hidrokarbon kompleks dari CPO menjadi hidrokarbon yang lebih sederhana dan sesuai dengan bensin. Tujuan dari penelitian ini adalah untuk menganalisis pengaruh rasio katalis:cpo dan jenis katalis terhadap yield dan viskositas biogasoline menggunakan katalis γ-Al2O3, HZSM, USY. Dalam penelitian ini, proses catalytic cracking dilakukan menggunakan alat destilasi dan sumber energi menggunakan heating mantle dengan variasi katalis γ-Al2O3, HZSM, USY dan rasio 1:125, 1:100, 1:75, 1:50. Sampel yang telah diperoleh akan diuji dengan beberapa pengujian seperti Fourier Transform Infra Red (FTIR), Gas Chromatography – Mass Spectroscopy (GC-MS) dan juga viskositas. Diperoleh hasil analisis bahwa semakin tinggi rasio katalis:cpo semakin menurunkan nilai yield biogasoline dan viskositas dari biogasoline. Nilai yield biogasoline tertinggi diperoleh ketika menggunakan USY dengan rasio katalis 1:125 yaitu sebesar 17,09%. Sedangkan untuk nilai viskositas terendah adalah sebesar 1,86 Cst yang diperoleh menggunakan γ-Al2O3 dengan rasio katalis 1:125.
============================================================
Fossil fuels are one of the energy sources that serve as the driving force for daily transportation needs, with their demand increasing year by year. However, this is in contrast to the declining production of crude oil in Indonesia over the past ten years, mainly due to aging oil wells, which could potentially lead to a scarcity of fossil fuels. To address this issue, one innovative solution that can be developed is to increase the production of alternative fuel, biogasoline, from Crude Palm Oil (CPO). The method used in this research is catalytic cracking, which allows for the conversion of complex hydrocarbons from CPO into simpler hydrocarbons suitable for gasoline. The objective of this research is to analyze the influence of catalyst composition and type on the yield and viscosity of biogasoline using γ-Al2O3, HZSM, and USY catalysts. In this study, the catalytic cracking process is conducted using a distillation apparatus, and the energy source is provided by a heating mantle, with variations in γ-Al2O3, HZSM, and USY catalysts and compositions of 1:125, 1:100, 1:75, 1:50. The obtained samples will undergo several tests such as Fourier Transform Infrared (FTIR) analysis, Gas Chromatography – Mass Spectroscopy (GC-MS), and viscosity measurement. The analysis results show that an increase in catalyst composition leads to a decrease in liquid yield and viscosity of biogasoline. The highest biogasoline yield is obtained when using USY catalyst with a 1:125 catalyst ratio, which is 17.09%. Meanwhile, the lowest viscosity value of 1.86 cSt is achieved using γ-Al2O3 catalyst with a 1:125 catalyst ratio.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Biogasoline, HZSM-5, USY, Viscosity, γ-Al2O3, Biogasolin, HZSM-5, USY, Viskositas, γ-Al2O3
Subjects:	T Technology > TP Chemical technology > TP1140 Polymers
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Haris Al Hamdi
Date Deposited:	26 Jul 2023 01:41
Last Modified:	26 Jul 2023 01:41
URI:	http://repository.its.ac.id/id/eprint/99283

Actions (login required)

View Item