Studi Pengaruh Arus Discharge Terhadap Sifat Elektrokimia Baterai Ni-MH Tipe AB5 Produksi Negara Jepang

Hutagalung, Irfan Satria Putra (2023) Studi Pengaruh Arus Discharge Terhadap Sifat Elektrokimia Baterai Ni-MH Tipe AB5 Produksi Negara Jepang. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111940000077-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (5MB) | Request a copy

Abstract

Untuk mengurangi dampak limbah akibat pemakaian baterai primer, maka digunakanlah baterai rechargeable. Salah satu baterai rechargeable adalah baterai NiMH. Akan tetapi di Indonesia baterai Nickel Metal Hydride (Ni-MH) ini masih jarang digunakan. Baterai Ni-MH butuh untuk diteliti lebih lanjut terkait efek pemakaiannya. Tujuan penelitian ini adalah untuk mengetahui bagaimana pengaruh dari penggunaan arus 0,3 A dan 0,5 A terhadap baterai Ni-MH. Metode analisa dalam penelitian ini diawali dengan pengujian Chronopotentiometry dengan variasi arus 0,3 dan 0,5 A. Setelah itu dilakukan pengujian Cyclic Voltammetry untuk mengetahui karakteristik reaksi reduksi dan oksidasi dari baterai Ni-MH. Lalu, dilakukan pengujian Electrochemical Impedance Spectroscopy untuk mengetahui nilai impedansi dan kinematika reaksi dari baterai. Setelah itu metal hydride diuji Scanning Electron Microscope dan X-Ray Diffraction untuk mengetahui perubahan dari hydride terhadap perlakuan arus. Ketidakstabilan kapasitas baterai dihasilkan pada kedua penggunaan arus discharge 0,3 dan 0,5 A, dimana ketidakstabilan lebih besar ditemui pada arus discharge 0,5 A. Sementara penurunan area voltammogram lebih besar sebesar 14,567% pada arus discharge 0,5 A didapatkan dari pengujian cyclic voltammetry. Arus discharge yang lebih besar menandakan lebih cepatnya kapasitas yang terpakai sehingga diikuti dengan adanya pengecilan kurva voltammogram. Pada uji EIS, didapatkan nilai Warburg yang lebih besar pada arus 0,5 A menandakan nilai difusi hidrogen yang lebih kecil yang berarti pergerakan hidrogen menjadi lebih terbatas. Hal ini sejalan dengan adanya penurunan ukuran crystallite yang lebih besar dan juga penurunan diameter metal hydride sebesar 67 % akibat pulverization yang lebih signifikan pada arus 0,5 A.
=================================================================================================================================
To reduce the impact of waste due to the use of primary batteries, rechargeable batteries are used. One of the rechargeable batteries is NiMH battery. However, in Indonesia Nickel Metal Hydride (Ni-MH) batteries are still rarely used. Ni-MH batteries need to be studied further regarding the effects of their use. The purpose of this study is to determine how the effect of using a current of 0,3 A and 0,5 A on Ni-MH batteries. The analysis method in this study begins with Chronopotentiometry testing with current variations of 0,3 and 0,5 A. After that, Cyclic Voltammetry testing is carried out to determine the characteristics of the reduction and oxidation reactions of Ni-MH batteries. Then, Electrochemical Impedance Spectroscopy testing was carried out to determine the impedance value and reaction kinematics of the battery. After that, the metal hydride was tested by Scanning Electron Microscope and X-Ray Diffraction to determine changes in hydride against discharge current. Battery capacity instability is produced in both the use of discharge currents 0,3 and 0,5 A, where greater instability is found at a discharge current of 0,5 A. While the decrease in voltammogram area is greater than 14.567% at a discharge current of 0,5 A obtained from cyclic voltammetry testing. A larger discharge current indicates a faster capacity used so that it is followed by a narrowing of the voltammogram curve. In the EIS test, the greater Warburg value obtained at a current of 0,5 A indicates a smaller hydrogen diffusion value which means that the movement of hydrogen becomes more limited. This is in line with the larger decrease in crystallite size and also a 67% decrease in metal hydride diameter due to more significant pulverization at a current of 0,5 A.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Cyclic Voltammetry, Electrochemical Impedance Spectrocsopy, Ni-MH, Scanning Electron Microscope, X-Ray Diffraction.
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2941 Storage batteries
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Irfan Satria Putra Hutagalung
Date Deposited:	08 Dec 2023 06:22
Last Modified:	08 Dec 2023 06:22
URI:	http://repository.its.ac.id/id/eprint/102119

Actions (login required)

View Item