Studi Pengaruh Variasi Arus Discharge Terhadap Performa Dan Karakteristik Elektrokimia Baterai Nimh Tipe La2Ni7 Buatan Jepang

Irianto, Adji Tri (1999) Studi Pengaruh Variasi Arus Discharge Terhadap Performa Dan Karakteristik Elektrokimia Baterai Nimh Tipe La2Ni7 Buatan Jepang. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111940000145-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2025. Download (4MB) | Request a copy

Abstract

Kenaikan produksi baterai juga diikuti oleh peningkatan limbah baterai bekas yang dapat mencemarkan lingkungan. Salah satu cara untuk mengurangi pencemaran lingkungan adalah dengan menggunakan baterai yang dapat diisi ulang. Salah satu jenis baterai isi ulang adalah baterai nikel metal hidrida(NiMH). Baterai NiMH memiliki rentang temperatur operasi yang cukup rendah sehingga aman digunakan pada kehidupan sehari-hari. Oleh karena itu, pada penelitian ini akan diteliti pengaruh aplikasi discharge yang berbeda terhadap kapasitas serta efek yang terjadi pada baterai NiMH ditinjau dari impedansi dan karakteristik elektrokimia.
Baterai yang digunakan dalam penelitian ini adalah baterai tipe AA NiMH tipe La2Ni7 buatan Jepang. Penelitian diawali dengan pengujian chrono potentiometry (CP) dengan dua variasi arus discharge, yakni 0,3 A dan 0,5 A sebanyak 50 siklus. Kemudian dilanjutkan dengan pengujian Electrochemical Impedance Spectroscopy (EIS) pada rentang frekuensi 10.000 Hz hingga 0,01 Hz untuk mengetahui perubahan nilai impedansi serta pengujian Cyclic Voltammetry (CV) pada potensial sweep 0 V hingga 1,8 V pada scan rate 0,0015 V/s untuk mengetahui karakteristik elektrokima pada baterai NiMH. Setelah itu, dilakukan uji X-Ray Diffraction (XRD) dan Scanning Electron Microscope(SEM) pada bagian elektroda negatif baterai NiMH untuk mengidentifikasi perubahan yang terjadi sebelum dan sesudah aplikasi arus discharge yang berbeda. Penurunan kapasitas yang signifikan diperoleh pada baterai yang dikenai arus discharge 0,5 A. Hal ini terlihat pada luasan cyclic voltammogram, yang menunjukkan nilai terkecil pada baterai dengan arus discharge 0,5 A. Selain itu, hambatan pada metal hidrida diperoleh nilai tertinggi pada baterai dengan arus discharge 0,5 A yang ditunjukkan dengan kenaikan hambatan sebesar 54,86% sehingga menyebabkan semakin mengecilnya kapasitas yang terbaca. Hal ini sejalan dengan hasil pengujian XRD yang diperoleh ukuran kristal terkecil pada spesimen baterai dengan arus discharge 0,5 A dan terlihat adanya pulverisasi pada morfologi permukaan serbuk metal hidrida yang erat kaitannya dengan kapasitas penyimpanan hidrogen.
================================================================================================================================
The increase in battery production is also followed by an increase in used battery waste that can pollute the environment. One way to reduce environmental pollution is to use rechargeable batteries. One type of rechargeable battery is nickel metal hydride (NiMH) batteries. NiMH batteries have a fairly low operating temperature range that is safe to use in everyday life. Therefore, this research will investigate the effect of different discharge applications on the capacity and effects that occur in NiMH batteries in terms of it’s impedance and electrochemical characteristics.
The battery used in this research is AA type NiMH battery type La2Ni7 made in Japan. The research begins with chrono potentiometry (CP) testing with two variations of discharge current, namely 0.3 A and 0.5 A for 50 cycles. Then proceed with Electrochemical Impedance Spectroscopy (EIS) testing in the frequency range of 10,000 Hz to 0.01 Hz to determine changes in impedance values and Cyclic Voltammetry (CV) testing at a potential sweep of 0 V to 1.8 V at a scan rate of 0.0015 V/s to determine the electrochemical characteristics of NiMH batteries. After that, X-Ray Diffraction (XRD) and Scanning Electron Microscope (SEM) tests were carried out on the negative electrode of NiMH batteries to identify changes that occurred before and after the application of different discharge currents. A significant decrease in capacity was obtained in the battery subjected to a discharge current of 0.5 A. This can be seen in the area of the cyclic voltammogram, which shows the smallest value in the battery with a discharge current of 0.5 A. In addition, the resistance of metal hydride obtained the highest value in the battery with a discharge current of 0.5 A which is indicated by an increase in resistance of 54.86% so as to cause the shrinking of the capacity read. This is in line with the results of XRD testing which obtained the smallest crystal size in the battery specimen with a discharge current of 0.5 A and visible pulverization on the surface morphology of metal hydride powder which is closely related to the hydrogen storage capacity.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Cyclic Voltammetry, Electrochemical Impedance Spectroscopy, NiMH Battery, Scanning Electron Microscope, Baterai NiMH, Chrono Potentiometry, Electrochemical Impedance Spectroscopy, X-Ray Diffraction
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2941 Storage batteries
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	Adji Tri Irianto
Date Deposited:	07 Aug 2023 03:49
Last Modified:	07 Aug 2023 03:49
URI:	http://repository.its.ac.id/id/eprint/103548

Actions (login required)

View Item