Karakterisasi Material Komposit Hybrid Fiberglass Woving 200 gr dan Kain Goni dari Serat Jute Bermatrik Epoxy Sebagai Material Cangkang Helm Sepeda Motor

Erlang, R. Muhammad Zharfan Riefqi (2023) Karakterisasi Material Komposit Hybrid Fiberglass Woving 200 gr dan Kain Goni dari Serat Jute Bermatrik Epoxy Sebagai Material Cangkang Helm Sepeda Motor. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02111640000174-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 September 2025. Download (3MB) | Request a copy

Abstract

Dunia industri saat ini sedang mengembangkan teknologi bahan karena menjadi faktor utama dalam pemenuhan kebutuhan bahan dengan karakteristik tertentu. Seiring dengan kemajuan teknologi, maka saat ini telah banyak digunakan dari bahan komposit dengan serat alam. Tidak hanya itu serat alam dianggap sebagai bahan yang ecofriendly, dapat diperbarui, tidak abrasive, memiliki ketahanan yang presisi dan proses pengerjaan yang mudahMenurut Maya (2018) produksi bahan berbasis serat 100% alami sebagai pengganti produk berbasis minyak bumi bukanlah solusi yang ekonomis. Solusi yang lebih layak adalah menggabungkan sumber daya minyak bumi dan sumber daya hayati untuk mengembangkan produk yang hemat biaya dengan aplikasi yang beragam. Pada penilitian ini akan menggunakan kain goni dari serat jute dan serat fiberglass dengan matriks epoksi. Variasi yang digunakan pada penelitian ini adalah urutan penumpukan dari lapisan komposit hybrid kain goni (G) dan fiberglass (F). Terdapat 3 variasi lapisan yang digunakan penelitian ini, pada variasi pertama terdapat 5 lapis Kain goni dengan urutan penumpukan G-G-G-G-G; variasi kedua terdapat 3 lapis kain goni dan 2 lapis serat fiberglass dengan urutan penumpukan F-G-G-G-F; variasi ketiga terdapat 3 lapis serat fiberglass dan 2 lapis kain goni dengan urutan penumpukan G-F-F-F-G. Orientasi sudut pada kedua material yang digunakan pada penilitian ini dengan arah sudut 0°/90°. Setelah dilakukan pengujian tarik didapatkan nilai sebagai berikut dengan variasi goni untuk nilai kekuatan tarik sebesar 57,27 Mpa, kekuatan yield sebesar 42,8 Mpa, dan modulus elastisitas sebesar 1933,37 Mpa. Variasi fiberglass-goni untuk nilai kekuatan tarik sebesar 81,54 Mpa, kekuatan yield sebesar 73,23 Mpa, dan modulus elastisitas sebesar 2346,18 Mpa. Variasi goni – fiberglass untuk nilai kekuatan tarik sebesar 117,04 Mpa, kekuatan yield sebesar 97,59 Mpa, dan modulus elastisitas sebesar 3322,63 Mpa
====================================================================================================================================
The industrial world is currently developing material technology because it is a major factor in meeting the needs of materials with certain characteristics. Along with technological advances, it is now widely used of composite materials with natural fibers. Not only that, natural fibers are considered as materials that are environmentally friendly, renewable, non-abrasive, have precise resistance and easy processing.. According to Maya (2018) the production of 100% natural fiber based materials as a substitute for petroleum-based products is not an economical solution. A more feasible solution is to combine petroleum and biological resources to develop cost-effective products with diverse applications. In this research, jute fiber and fiberglass fibers with an epoxy matrix will be used. The variation used in this study is the stacking sequence of the hybrid composite layers of hessian cloth (G) and fiberglass (F). There are 3 variations of layers used in this study, in the first variation there are 5 layers of burlap with the stacking sequence G-G-G-G-G; the second variation has 3 layers of burlap and 2 layers of fiberglass fibers in the stacking order F-G-G-G-F; The third variation has 3 layers of fiberglass and 2 layers of burlap with the stacking sequence G-F-F-F-G. The angular orientation of the two materials used in this research is at an angle of 0°/90°. After the tensile test was carried out, the following values were obtained with jute variations for a tensile strength value is 57.27 MPa, a yield strength is 42.8 MPa, and a modulus of elasticity is 1933.37 MPa. The fiberglass-jute variation for a tensile strength value is 81.54 Mpa, a yield strength is 73.23 Mpa, and a modulus of elasticity is 2346.18 Mpa. Jute – fiberglass variations for a tensile strength value of 117.04 Mpa, a yield strength is 97.59 MPa, and a modulus of elasticity is 3322.63 Mpa

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Komposit Alam, Serat Alam, Kain goni, Serat Fiberglass, Epoksi, Sungkup helm, Helm Full-face, SNI 1811-2007, Pengujian Tarik; Natural Composites, Natural Fibers, Jute Fabric, Fiberglass Fibers, Epoxy, Helmet Covers, Full-face Helmets, SNI 1811-2007, Tensile Testing
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL240.5 Composite materials
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	R Muhammad Zharfan Riefqi Erlang
Date Deposited:	23 Aug 2023 03:56
Last Modified:	23 Aug 2023 03:56
URI:	http://repository.its.ac.id/id/eprint/104117