Studi Experimental Perbandingan Pengujian Indentasi Brinell Dan Analisa Elemen Hingga Untuk Mendapatkan Sifat Mekanik Pada Baja Paduan Aisi 4340

Fanani, Moh.Afif (2009) Studi Experimental Perbandingan Pengujian Indentasi Brinell Dan Analisa Elemen Hingga Untuk Mendapatkan Sifat Mekanik Pada Baja Paduan Aisi 4340. Other thesis, Institut Teknologi Sepuluh Nopember Surabaya.

Text 2104100117-Undergraduate_Thesis.pdf - Accepted Version Download (42MB)

Abstract

Dalam bidang industri, sifat mekanik material sangat menentukan dalam pembuatan produk. Untuk mengetahui sifat material biasanya dilakukan dengan tensile test. Pengujian ini biasanya memakan waktu, merusak dan membutuhkan persiapan spesimen yang khusus. Disamping itu, apabila ingin mengetahui sifat mekanik dari material yang sudah mencapai proses akhir (finishing) akan kesulitan dengan memakai tensile test. Karena sebab itu dikembangkan suatu metode untuk dapat memperoleh sifat mekanik yang relatif cepat dan tanpa harus merusak benda uji. Pengujian dengan indentasi (penekanan) menjadi salah satu alternatif karena metode ini mudah dilakukan dan membutuhkan spesimen yang tidak terlalu besar. Dalam penelitian ini pengujian yang dipakai adalah pengujian indentasi metode brinell dengan tiga variasi beban yaitu 31,25kgf 62,5kgf dan 187,5kgf. Hasil pengujian indentasi digunakan untuk verifikasi metode elemen hingga. Hasil yang diperoleh dari pengujian analisa elemen hingga dan pengujian brinell akan dibandingkan dengan hasil pengujian tarik. Dari penelitian ini dapat diketahui bahwa pengujian indentasi dengan metode brinell dan perhitungan dengan metode elemen hingga menghasilkan karakter sifat mekanik yang relatif sama pada beban 187,5 kgf. Hasil kedua pengujian tersebut juga menghasilkan sifat mekanik yang mendekati sifat mekanik dari pengujian tarik untuk baja paduan AISI 4340
====================================================================================================================================
In the industrial sector, the mechanical properties of materials are very important in making products. To determine the properties of the material, a tensile test is usually carried out. These tests are usually time consuming, destructive and require special specimen preparation. Apart from that, if you want to know the mechanical properties of material that has reached the final process (finishing), it will be difficult to use a tensile test. For this reason, a method was developed to obtain mechanical properties relatively quickly and without having to damage the test object. Testing by indentation (pressure) is an alternative because this method is easy to carry out and requires specimens that are not too large. In this research, the test used was the Brinell method indentation test with three load variations, namely 31.25kgf, 62.5kgf and 187.5kgf. The indentation test results are used to verify the finite element method. The results obtained from finite element analysis tests and Brinell tests will be compared with the tensile test results. From this research it can be seen that indentation testing using the Brinell method and calculations using the finite element method produce relatively similar mechanical properties at a load of 187.5 kgf. The results of these two tests also produced mechanical properties that were close to the mechanical properties of the tensile test for AISI 4340 alloy steel

Item Type:	Thesis (Other)
Additional Information:	RSM 553.72 Fan s-1 2009
Uncontrolled Keywords:	Sifat mekanik, Pengujian indentasi, Analisa elemen hingga, Pengujian tarik; Mechanical properties, Indentation test, Finite element analysis, Tensile test
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA347 Finite Element Method T Technology > TA Engineering (General). Civil engineering (General) > TA460 Metals--Fatigue.
Divisions:	Faculty of Industrial Technology > Mechanical Engineering > 21201-(S1) Undergraduate Thesis
Depositing User:	EKO BUDI RAHARJO
Date Deposited:	25 Oct 2023 04:13
Last Modified:	25 Oct 2023 04:13
URI:	http://repository.its.ac.id/id/eprint/104993