Sulistyowati, Vira Meilina (2024) Pengaruh Komposit PMMA/Zirkon Sebagai Selubung Sensor Optical Fiber Tip Berstruktur Singlemode-Multimode Step Index Pada Pengukuran Larutan Glukosa. Other thesis, Institut Teknologi Sepuluh Nopember.
![[thumbnail of 5009201120-Undergraduate_Thesis.pdf]](http://repository.its.ac.id/style/images/fileicons/text.png) |
Text
5009201120-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (6MB) | Request a copy |
Abstract
Diabetes adalah penyakit yang berkembang dengan pesat di seluruh dunia dan
menjadikannya masalah kesehatan yang besar. Kadar glukosa harus selalu diperhatikan agar
tidak menimbulkan hiperglikemia dan hipoglikemia yang dapat mengakibatkan diabetes.
Pengembangan biosensor berupa deteksi dan pengukuran kadar glukosa menggunakan strategi
optik dinilai cocok karena noninvasif, cepat, dan sensitif. Pada penelitian ini dirancang sensor
konsentrasi berdasarkan indeks bias dengan menggunakan fiber tip singlemode-multimode
step index 2.8 cm yang dilapisi oleh coating komposit PMMA/zirkon. Coating komposit
PMMA/zirkon dapat meningkatkan sensitivitas sensor karena material zirkon yang memiliki
nilai CTE yang rendah dan indeks bias yang lebih tinggi. Pengukuran didasarkan pada
perubahan daya dan spektrum puncak panjang gelombang dengan menggunakan optical
power meter dan optical spectrum analyzer. Pada Penelitian ini memiliki tujuan untuk
menganalisis pengaruh coating PMMA/zirkon pada respon optical fiber tip sensor. Hasil
pengukuran terhadap pengukuran konsentrasi glukosa didapatkan sensitivitas tertinggi, yaitu
pada fiber tip sensor coating 1% dengan nilai 0.36853 dBm/%. Pengukuran terhadap
pengaruh suhu diperoleh linieritas tertinggi, yaitu pada fiber tip sensor coating 1% dengan
nilai 0.91408. Pergeseran spektrum panjang gelombang terkecil baik terhadap suhu maupun
konsentrasi terjadi pada fiber tip sensor coating 1%. Seiring dengan bertambahnya
konsentrasi zirkon pada lapisan fiber tip sensor dapat meningkatkan karakteristik sensor
berupa mengingkatnya sensitivitas dan linieritas serta mengurangi pergeseran nilai puncak
panjang gelombang akibat pengaruh suhu.
========================================================================================================================
Diabetes is a rapidly growing disease worldwide and has become a major health
problem. Glucose levels should always be monitored to avoid causing hyperglycemia and
hypoglycemia which can lead to diabetes. The development of a biosensor in the form of
sensing and measuring glucose levels using an optical strategy is considered suitable as it is
non-invasive, rapid and sensitive. In this research, a refractive index-based concentration
sensor was designed using a singlemode-multimode step index 2.8 cm fiber tip coated with a
PMMA/zircon composite coating. The PMMA/zircon composite coating can increase the
sensitivity of the sensor because the zircon material has a lower CTE value and higher
refractive index. Measurements are based on changes in power and peak wavelength spectrum
using an optical power meter and optical spectrum analyzer. In this study, we examine the
effect of PMMA/zircon coating on the optical response of the fiber tip sensor. The glucose
concentration measurement results showed that the highest sensitivity was at 1% of the fiber
tip sensor coating with a value of 0.36853 dBm/%. Measurements of the temperature effect
achieved the highest linearity, especially on the 1% fiber tip sensor coating, with a value of
0.91408. The smallest shift in the wavelength spectrum occurs at coating 1% of the fiber tip
sensor. As the concentration of zircon in the fiber tip layer of the sensor increases, the sensor
characteristics can be improved in the form of increased sensitivity and linearity and reduced
shifts in peak of wavelength due to the influence of temperature.