Penyerapan Karbon Dioksida Pada Beton dan Pengaruhnya Terhadap Sifat Mekanik dan Durabilitas Beton

Al Kautsar, Kevin (2024) Penyerapan Karbon Dioksida Pada Beton dan Pengaruhnya Terhadap Sifat Mekanik dan Durabilitas Beton. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6012221014-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (3MB)

Abstract

Emisi CO2 yang tinggi selama produksi beton telah membuatnya menjadi tantangan signifikan dalam upaya mengurangi dampak perubahan iklim. Oleh karena itu, penelitian ini bertujuan untuk menganalisis pengaruh penggunaan bahan semen seperti Fly ash (FA), Bottom ash (BA), dan Spent bleaching earth (SBE) dalam komposisi beton terhadap penyerapan karbon dioksida (CO2). Metodologi penelitian melibatkan persiapan awal mortar beton untuk menentukan campuran yang paling optimal dari FA, BA, dan SBE dalam hal penyerapan CO2. Persentase campuran FA, BA, dan SBE yang digunakan masing-masing adalah 5%, 10%, dan 15%. Selanjutnya, beton konvensional diproduksi dan dibandingkan dengan beton yang telah menyerap CO2. Sampel beton ini kemudian diuji terhadap kuat tekan dan durabilitas, termasuk penyerapan air dan infiltrasi klorida. Hasil yang didapatkan bahwa variasi optimal untuk beton FA adalah 10%, BA 5%, dan SBE 5%. Dari hasil uji tekan didapatkan bahwa kuat tekan beton untuk variasi kontrol, FA, dan BA mengalami kenaikan sedangkan SBE mengalami penurunan setelah beton teradsorbsi CO2. Pada pengujian penyerapan air dan infiltrasi klorida, beton yang telah teradsorbsi CO2 mengalami penurunan pada semua variasinya. Maka penyerapan CO2 pada beton dapat meningkatkan durabilitasnya.
========================================================
The high CO2 emissions during concrete production have posed a significant challenge in efforts to mitigate climate change impacts. Therefore, this study aims to analyze the influence of using cementitious materials such as Fly Ash (FA), Bottom Ash (BA), and Spent Bleaching Earth (SBE) in concrete composition on carbon dioxide (CO2) absorption. The research methodology involves the initial preparation of concrete mortar to determine the optimal mix of FA, BA, and SBE in terms of CO2 absorption. The percentages of FA, BA, and SBE used in the mix are 5%, 10%, and 15%, respectively. Subsequently, conventional concrete is produced and compared with CO2-absorbed concrete. These concrete samples are then tested for compressive strength and durability, including water absorption and chloride infiltration. The results indicate that the optimal variations for concrete are 10% FA, 5% BA, and 5% SBE. The compressive strength tests reveal that the compressive strength of the control, FA, and BA variations increased, while the SBE variation decreased after CO2 adsorption. In the water absorption and chloride infiltration tests, the CO2-adsorbed concrete showed a decrease across all variations. Hence, CO2 absorption in concrete can enhance its durability.

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	Kata Kunci: Beton, Durabilitas Beton, Karbon Dioksida (CO2), Kuat Tekan Beton, Penyerapan CO2 ===== Keywords: Carbon Dioxide (CO2), Concrete, Concrete Compressive Strength, Concrete Durability, CO2 Sequestration
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing. T Technology > TA Engineering (General). Civil engineering (General) > TA418.9 Composite materials. Laminated materials. T Technology > TA Engineering (General). Civil engineering (General) > TA455 Carbon. Nanotubes. T Technology > TP Chemical technology > TP245.C3 Calcium carbonate. T Technology > TP Chemical technology > TP883 Portland cement.
Divisions:	Faculty of Civil Engineering and Planning > Civil Engineering > 22101-(S2) Master Thesis
Depositing User:	Kevin Al Kautsar
Date Deposited:	01 Aug 2024 16:18
Last Modified:	01 Aug 2024 16:18
URI:	http://repository.its.ac.id/id/eprint/109957