Deteksi Kelembapan Berbasis Serat Optik Singlemode - Multimode - Singlemode (SMS) dengan Lapisan TiO2 dan TiO2/rGO menggunakan Metode Dip Coating

Pintaloka, Andyra Manikam (2024) Deteksi Kelembapan Berbasis Serat Optik Singlemode - Multimode - Singlemode (SMS) dengan Lapisan TiO2 dan TiO2/rGO menggunakan Metode Dip Coating. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201066_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (3MB) | Request a copy

Abstract

Deteksi kelembapan berbasis serat optik (SMS) dengan lapisan TiO2 dan TiO2/rGO menggunakan metode dip coating ini bertujuan untuk mengetahui pengaruh coating larutan TiO2 dan TiO2/rGO terhadap karakteristik dan sensitivitas deteksi kelembapan berbasis serat optik SMS. Proses pembuatan larutan dilakukan dengan melarutkan serbuk bahan ke dalam aquades dan dilakukan autoclave selama 2 jam. Selanjutnya larutan dilapiskan pada serat optik SMS dengan metode dip coating. Kemudian dilakukan pengujian karakteristik dari serat optik SMS dengan lapisan dan tanpa lapisan menggunakan Optical Spectrum Analyzer (OSA). Pengujian dilakukan untuk variasi kelembapan 40 – 84% dengan kenaikan 2%. Hasil penelitian menunjukkan bahwa serat optik SMS setelah pelapisan TiO2 dan rGO, memiliki sensitivitas lebih tinggi daripada tanpa pelapisan. Sedangkan berdasarkan panjang gelombang, pelapisan TiO2/rGO mempunyai sensitivitas yang lebih tinggi dibandingkan dengan hanya dilapisi TiO2 dan rGO. Peningkatan sensitivitas dapat disebabkan dengan peningkatan interaksi antara lapisan pelapis dengan molekul air, yang menghasilkan perubahan indeks bias yang lebih signifikan dan mempengaruhi transmisi cahaya melalui serat optik.
==============================================================================================================================
The detection of humidity based on optical fibers (SMS) with TiO2 and TiO2/rGO coatings using the dip coating method aims to determine the effect of coating solutions of TiO2 and TiO2/rGO on the characteristics and sensitivity of humidity detection based on SMS optical fibers. The process of making the solution involves dissolving the powder material into distilled water and autoclaving for 2 hours. The solution is then coated onto the SMS optical fiber using the dip coating method. Subsequently, the characteristics of the SMS optical fiber with and without the coating are tested using an Optical Spectrum Analyzer (OSA). The testing is conducted for humidity variations ranging from 40% to 84% with an increase of 2%. The results of the research show that the SMS optical fiber after coating with TiO2 and TiO2/rGO has higher sensitivity than without coating. Furthermore, based on the wavelength, the TiO2/rGO coating has higher sensitivity compared to only TiO2 and rGO coatings. The increase in sensitivity can be attributed to the enhanced interaction between the coating layer and water molecules, which results in a more significant change in the refractive index and affects the light transmission through the optical fiber.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Dip Coating, Singlemode – Multimode – Singlemode Fiber, reduced Graphene Oxide, Titanium Dioksida, Kelembapan, Titanium Dioxide, Moisture
Subjects:	Q Science > QC Physics > QC448 Fiber optics.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Andyra Manikam Intan Pintaloka
Date Deposited:	29 Aug 2024 03:41
Last Modified:	29 Aug 2024 03:41
URI:	http://repository.its.ac.id/id/eprint/110407