ANALISIS PENGARUH VARIASI CARBON SUPPORT DAN HEAT TREATMENT TERHADAP STRUKTUR DAN SIFAT ELEKTROKIMIA KATALIS BERBASIS Pt UNTUK PEMFC

Daniyanto, Eric (2024) ANALISIS PENGARUH VARIASI CARBON SUPPORT DAN HEAT TREATMENT TERHADAP STRUKTUR DAN SIFAT ELEKTROKIMIA KATALIS BERBASIS Pt UNTUK PEMFC. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5011201084_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (2MB)

Abstract

Penelitian terkait pengembangan PEMFC mempunyai bebrapa cakupan diantaranya adalah penyangga katalis hingga ketersediaan katalis Pt itu sendiri. Pada penelitian ini terdapat beberapa variasi yang dapat memberikan pemanfaatan terbaru terkait material penyangga katalis diatas. Sintesis Pt/C dengan bahan dari CNT, Carbon Black, Carbon Melamine menggunakan asam format yang diendapkan selama 2 hari. Penggunaan bahan nitrogenous organic dapat menjadi pandangan lain dalam pembuatan material penyangga katlis PEMFC. Salah Satu yang ditunjukan pada Pt/Carbon Melamin yang memiliki peforma single cell hingga 0,4218 W/cm2 dan pengujian pada temperatur lebih tinggi mendapatkan nilai 0,42417 W/cm2 serta memiliki ketahanan dalam pemberian beban yang lebih tinggi. Pada pengujian Electrochemical Surface Area menunjukan kemampuan yang lebih baik dari Pt/C dengan nilai 70,739 m2/gpt serta memiliki number electron yang mendekati Pt/C yakni 3,641. Katalis Pt/CNT pada hasil pengujian XRD memiliki ukuran rataan ukuran kristal terkecil yakni sebesar 9,232 nm. Dan telah berhasilnya mendeposisikan platina ke beberapa substrat karbon dari CNT, Act-CNT, CNT HT, Act-CNT HT, Carbon Black, dan Carbon Melamine yang dibuktikan pada terbentuknya puncak puncak Pt pada karakterisasi XRD. Pada proses post heat treatment terjadi peningkatan ukuran rataan kristal dari sampel sebelum dilakukan treatment tersebut.
===========================================================
Abstract
Research related to PEMFC development has several scopes including catalyst buffers to the availability of Pt catalyst itself. In this research, there are several variations that can provide the latest utilization related to the catalyst buffer material above. This researchs Pt / C synthesis with materials from CNT, Carbon Black, Carbon Melamine using formic acid. The use of organic nitrogenous materials can be another view in the manufacture of PEMFC catalyst buffer materials. One that is shown in Pt / Carbon Melamine which has a single cell performance of up to 0,4218 W/cm2 and testing at higher temperatures gets a value of 0,42417 W/cm2 and has resistance in giving higher loads. The Electrochemical Surface Area test shows a better ability than Pt/C with a value of 70,739 m2/gpt and has an electron number close to Pt/C which is 3,641. The Pt/CNT catalyst in the XRD test results has the smallest average crystal size of 9,232 nm. And the success of platinum deposition to several carbon substrates from CNT, Ac-CNT, CNT HT, Ac-CNT HT, Carbon Black, and Carbon Melamine as evidenced by the formation of Pt peak on XRD characterization. In the post heat treatment process there is an increase in the average size of the crystals from the sample before the treatment.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Carbon Support, CNT, Heat Treatment, Electrochemical Peformance, PEMFC
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA455 Carbon. Nanotubes.
Divisions:	Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Eric Daniyanto
Date Deposited:	08 Aug 2024 02:01
Last Modified:	08 Aug 2024 02:01
URI:	http://repository.its.ac.id/id/eprint/111222