Pengaruh Variasi Interlocking Depth Parameter & Structure Orientation Terhadap Kekuatan Tarik Produk 3d Print Berbahan Filamen PLA

Santoso, Rafif Hilmy (2024) Pengaruh Variasi Interlocking Depth Parameter & Structure Orientation Terhadap Kekuatan Tarik Produk 3d Print Berbahan Filamen PLA. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038201030_Undergraduated_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (5MB) | Request a copy

Abstract

Perkembangan teknologi dalam segmen additive manufacturing (AM), bertumbuh secara pesat. Salah satu perkembangan yang mencolok ialah konsep interlaced interlocking pada pencetakan multimaterial additive manufacturing. Pada penelitian ini dilakukan pengujian sambungan pada manufaktur aditif khususnya sambungan dengan variasi kedalaman struktur dan orientasi interlock terhadap kekuatan tarik material pada filamen PLA dengan analisa statistik menggunakan ANOVA. Variasi yang digunakan dalam penelitian ini menggunakan interlocking depth 2, 4, 6, dan 8. Sementara untuk variasi interlocking structure orientation menggunakan 45˚ dan 90˚. Hasil dari penelitian ini menunjukkan bahwa kekuatan tarik tertinggi terdapat pada parameter interlocking depth 4 dan interlocking structure orientation 45˚ dimana nilainya sebesar 29,04 MPa sedangkan untuk kekuatan tarik terendah terdapat pada parameter interlocking depth 8 dan interlocking structure orientation 90˚ dengan nilainya sebesar 12,48 MPa. Hasil analisa ANOVA menunjukkan bahwa penggunaan parameter yang paling optimal dengan menggunakan variasi interlocking depth 2 dan 4 dengan nilai 26,56 dan 25,27 serta variasi interlocking structure orientation 45˚ dengan nilai 27,34. Hal tersebut membuktikan bahwa terdapat pengaruh yang signifikan pada variasi interlocking depth dan interlocking structure orientation
===============================================================================================================
Technological developments in the additive manufacturing (AM) segment are growing rapidly. One of the most notable developments is the concept of interlaced interlocking in multimaterial additive manufacturing. In this study, the joints in additive manufacturing were tested, especially joints with variations in structural depth and interlock orientation on the tensile strength of materials on PLA filaments with statistical analysis using ANOVA. The variations used in this study used interlocking depths of 2, 4, 6, and 8. While for variations in interlocking structure orientation using 45˚ and 90˚. The results of this study show that the highest tensile strength is found in the parameters of interlocking depth 4 and interlocking structure orientation 45˚ where the value is 29.04 MPa while the lowest tensile strength is found in the parameters of interlocking depth 8 and interlocking structure orientation 90˚ with a value of 12.48 MPa. The results of ANOVA analysis show that the most optimal use of parameters using interlocking depth variations 2 and 4 with values of 26.56 and 25.27 and interlocking structure orientation variation 45˚ with a value of 27.34. This proves that there is a significant effect on the variation of interlocking depth and interlocking structure orientation.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Additive Manufacturing, Interlaced Interlock, Tensile Test, PLA
Subjects:	T Technology > TS Manufactures > TS171 Product design T Technology > TS Manufactures > TS183 Manufacturing processes. Lean manufacturing.
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Rafif Hilmy Santoso
Date Deposited:	01 Aug 2024 02:10
Last Modified:	01 Aug 2024 02:10
URI:	http://repository.its.ac.id/id/eprint/111262