Karakteristik Korosi CO2 Pada Baja Karbon Menggunakan Presipitat CaCO3 Dari Batu Kapur Kabupaten Tuban Sebagai Inhibitor Dengan Larutan NaCl

Amaanaturraafi, Zufar (2024) Karakteristik Korosi CO2 Pada Baja Karbon Menggunakan Presipitat CaCO3 Dari Batu Kapur Kabupaten Tuban Sebagai Inhibitor Dengan Larutan NaCl. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001201045_Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (12MB) | Request a copy

Abstract

Penelitian ini mengevaluasi pengaruh konsentrasi kalsium karbonat (CaCO3) dan laju aliran CO2 terhadap korosi pada baja karbon. Metode eksperimental dilakukan untuk memvariasikan kedua parameter tersebut, dengan fokus pada karakteristik produk korosi FeCO3. Menggunakan metode pencampuran larutan CaCl2 dan Na2CO3 melalui titrasi untuk menghasilkan presipitasi CaCO3 dari batu kapur yang berasal dari Kabupaten Tuban. Pengujian korosi baja karbon melalui perendaman menggunakan larutan NaCl sintesis 3 wt% selama tiga hari dengan variasi konsentrasi CaCO3 700 ppm dan 1000 ppm serta variasi laju aliran gas CO2 sebesar 1 liter/menit. Hasil penelitian ini menunjukkan data bahwa CaCO3 yang telah disintesis memiliki fasa kalsit. Laju korosi pada konsetrasi 700 ppm (laju aliran CO2 1 liter/menit dan 2 liter/menit) tidak menunjukkan penurunan yang signifikan dibandingkan dengan konsentrasi 1000 ppm (laju aliran CO2 1 liter/menit dan 2 liter/menit). Penurunan laju korosi yang signifikan disebabkan oleh wt% Fe3O4 dan Fe2O3 yang lebih kecil dibandingkan dengan wt% FeCO3 yang bersifat protektif. Produk korosi Fe3O4 dan Fe2O3 yang memiliki sifat berpori akan menyebabkan korosi di bawah permukaan FeCO3
==============================================================================================================================
This study evaluates the effect of calcium carbonate (CaCO3) concentration and CO2 flow rate on the corrosion of carbon steel. Experimental methods were conducted to vary both parameters, focusing on the characteristics of FeCO3 corrosion products. Using the method of mixing CaCl2 and Na2CO3 solutions through titration to produce CaCO3 precipitation from limestone from Tuban Regency. Carbon steel corrosion testing through immersion using 3wt% synthetic NaCl solution for three days with CaCO3 concentration variation of 700 ppm and 1000 ppm and CO2 gas flow rate variation of 1 liter/minute. The results of this study show data that CaCO3 that has been synthesized has a calcite phase. The corrosion rate at 700 ppm concentration (CO2 flow rate of 1 liter/minute and 2 liters/minute) did not show a significant decrease compared to the concentration of 1000 ppm (CO2 flow rate of 1 liter/minute and 2 liters/minute). The significant decrease in corrosion rate is due to the smaller wt% Fe3O4 and Fe2O3 compared to the protective wt% FeCO3. The corrosion products Fe3O4 and Fe2O3 which have porous properties will cause corrosion under the surface of FeCO3.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Inhibitor, Korosi CO2, Presipitat CaCO3, Corrosion CO2, CaCO3 Precipitate
Subjects:	Q Science > QC Physics Q Science > QC Physics > QC100 Crystals. Q Science > QC Physics > QC766.F3 Ferrites Q Science > QD Chemistry > QD1 Oxidation-reduction reaction.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Zufar Amaanaturraafi
Date Deposited:	05 Aug 2024 05:17
Last Modified:	27 Aug 2024 07:20
URI:	http://repository.its.ac.id/id/eprint/111955

Actions (login required)

View Item