Kirana, Oka Shinta Sekar (2024) Sintesis Nanopartikel Logam Ag, Au, dan Cu menggunakan Quercus infectoria Gall. Masters thesis, Institut Teknologi Sepuluh Nopember.

Text 6004222008-Master_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (3MB) | Request a copy

Abstract

Nanopartikel logam (Ag, Au, dan Cu) berhasil disintesis menggunakan tanaman manjakani (Quercus infectoria Gall, QIG) dengan memanfaatkan kandungan senyawa fenolik dalam ekstrak tanaman yang memiliki gugus pereduksi hidroksil sehingga mampu mereduksi ion logam sekaligus menstabilkan nanopartikel logam yang terbentuk. Sintesis nanopartikel logam dilakukan dengan memvariasikan rasio volume ion logam terhadap larutan QIG pada 1:1, 2:1, 4:1, dan 8:1 dengan kondisi pH ion logam berada pada pH 7, konsentrasi larutan ion logam dan larutan QIG dibuat sama, yaitu 100 ppm. Masing-masing nanopartikel logam dipilih rasio paling optimal melalui perubahan warna larutan dan absorbansi maksimum pada panjang gelombang tertentu. Rasio paling optimal adalah AgNPs 8:1, AuNPs 1:1, dan CuNPs 2:1 dengan absorbansi maksimum pada panjang gelombang 406-415 nm, 535-546 nm, dan 320-325 nm. AgNPs, AuNPs, dan CuNPs memiliki potensial zeta sebesar -18.57 mV, -20.77 mV, dan -22.98 mV. Analisis particle size analyzer (PSA) menunjukkan rata-rata diameter AgNPs, AuNPs, dan CuNPs adalah 108.0 nm, 125.6 nm, dan 197.6 nm sesuai dengan FESEM-EDX. Nanopartikel logam memiliki morfologi tertentu, yaitu AgNPs berbentuk memanjang dan lonjong, AuNPs berbentuk menyerupai rod dan masih terdapat beberapa partikel berbentuk bulat, serta CuNPs berbentuk menyerupai balok memanjang dengan kandungan unsur C dan O yang berasal dari QIG dan dikonfirmasi dengan FTIR yang utamanya menunjukkan keberadaan gugus hidroksil. Penelitian ini memberikan metode sintesis nanopartikel menggunakan QIG sebagai pengganti bahan kimia yang umumnya digunakan sebagai pereduksi ion logam dan penstabil nanopartikel logam sehingga pembentukkan nanopartikel logam dapat diatur dan proses sintesis nanopartikel logam dapat dilakukan pada kondisi relatif aman serta sederhana
========================================================================================================================================
Metal nanoparticles (Ag, Au, and Cu) were successfully synthesized using manjakani plants (Quercus infectoria Gall, QIG) by utilizing the phenolic compound content in plant extracts that have hydroxyl reducing groups so that they can reduce metal ions while stabilizing the formed metal nanoparticles. The synthesis of metal nanoparticles was carried out by varying the volume ratio of metal ions to QIG solution at 1:1, 2:1, 4:1, and 8:1 with the pH condition of the metal ions at pH 7, the concentration of the metal ion solution and QIG solution was made the same, which was 100 ppm. Each metal nanoparticle was selected for the most optimal ratio through changes in solution color and maximum absorbance at certain wavelengths. The most optimal ratios were AgNPs 8:1, AuNPs 1:1, and CuNPs 2:1 with maximum absorbance at wavelengths of 406-415 nm, 535-546 nm, and 320-325 nm. AgNPs, AuNPs, and CuNPs have zeta potentials of -18.57 mV, -20.77 mV, and -22.98 mV. Particle size analyzer (PSA) analysis showed that the average diameters of AgNPs, AuNPs, and CuNPs were 108.0 nm, 125.6 nm, and 197.6 nm according to FESEM-EDX. Metal nanoparticles have a certain morphology, namely AgNPs are elongated and oval, AuNPs are rod-shaped and there are still some round particles, and CuNPs are elongated block-shaped with C and O elements from QIG and confirmed by FTIR which mainly shows the presence of hydroxyl groups. This study provides a method for synthesizing nanoparticles using QIG as a substitute for chemicals that are generally used as metal ion reducers and metal nanoparticle stabilizers so that the formation of metal nanoparticles can be regulated and the synthesis process of metal nanoparticles can be carried out in relatively safe and simple conditions

Item Type:	Thesis (Masters)
Uncontrolled Keywords:	nanopartikel perak, nanopartikel emas, nanopartikel tembaga, Quercus infectoria gall
Subjects:	Q Science > QD Chemistry
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47101-(S2) Master Thesis
Depositing User:	Oka Shinta Sekar Kirana
Date Deposited:	10 Aug 2024 15:27
Last Modified:	26 Aug 2024 02:22
URI:	http://repository.its.ac.id/id/eprint/114170

Actions (login required)

View Item