Sintesis NiO/Aluminosilikat Mesopori dengan Dual Templat P123 dan Nanoselulosa untuk Reaksi Deoksigenasi Minyak Nyamplung

Fernanda, Ingelia Yuan (2024) Sintesis NiO/Aluminosilikat Mesopori dengan Dual Templat P123 dan Nanoselulosa untuk Reaksi Deoksigenasi Minyak Nyamplung. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004201010-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 October 2026. Download (6MB) | Request a copy

Abstract

Aluminosilkat disintesis dari templat P123 dan nanoselulosa untuk mengetahui pengaruh variasi templat terhadap karakteristik material dan aktivitas katalitiknya pada reaksi deoksigenasi menggunakan minyak nyamplung. Sintesis aluminosilikat dilakukan dengan kombinasi metode sol-gel dan hidrotermal dengan variasi P123 : nanoselulosa yaitu 1:0; 0,75:0,25; 0,50;0,50; dan 0,25;0,75. Selanjutnya, dilakukan impregnasi nikel pada support aluminosilikat dengan metode ultrasonik. Hasil karakterisasi XRD menunjukkan terdapat puncak pada 2ϑ = 37°, 43°, dan 63° yang mengindikasikan bahwa NiO tersebar pada permukaan aluminosilikat mesopori. Analisis FESEM menunjukkan bahwa terdapat perubahan morfologi dari bentuk cacing ke bentuk bulat. Berdasarkan analisis TEM sampel Ni/AlMS(0,25) menghasilkan pori heksagonal teratur. Karakterisasi adsorpsi-desorpsi N2¬ menghasilkan pori meso pada seluruh katalis. Luas permukaan, volume dan diameter pori terbesar dimiliki oleh Ni/AlMS(0,25) sebesar 315,294 m2/g; 0,546 cm3/g; 7,032 nm. Katalis diuji aktivitas katalitiknya dengan reaksi deoksigenasi menggunakan minyak nyamplung sebagai bahan baku. Dari seluruh katalis, Ni/AlMS(0,25) menghasilkan yield produk cair tertinggi yaitu 66,37% karena luas permukaan dan volume porinya yang besar. Seluruh katalis menunjukkan selektivitas karbon yang tinggi pada C15-C17 dengan produknya yaitu pentadekana dan 8-heptadekena.
=================================================================================================================================
Aluminosilicate was synthesized from P123 templates and nanocellulose to determine the influence of template variations on the material characteristics and its catalytic activity on the deoxygenation reaction using the oil. Aluminosilicate synthesis was performed using a combination of sol-gel and hydrothermal methods with P123 variations: nanosellulose is 1:0; 0,75:0,25; 0,50:0,50; and 0,25:0,75. Next, nickel impregnation is performed on an aluminosilicate support by the ultrasonic method. The XRD characterization results show a peak at 2θ = 37°, 43°, and 63°, indicating that NiO is scattered on the surface of mesoporous aluminosilicate. FESEM analysis showed that there was a morphological change from worm shape to round shape. Based on TEM analysis, the Ni/AlMS(0,25) sample produces regular hexagonal pores. The characterization of N2 adsorption-desorption produces mesopores on the whole catalyst. The largest surface area, volume, and porous diameter are possessed by Ni/AlMS(0,25) at 315,29 m2/g, 0,546 cm3/g, and 7,032 nm, respectively. The catalyst tested its catalytic activity with a deoxygenation reaction using nyamplung oil as a raw material. Of all the catalysts, Ni/AlMS (0.25) has the highest liquid product yield of 66.37% due to its large surface area and volume. The whole catalyst showed high carbon selectivity in C15-C17, with the product are pentadecane and 8-heptadecene.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Aluminosilikat Mesopori, Nanoselulosa, Deoksigenasi, Minyak Nyamplung, Biofuel, Mesoporous Aluminosilicate, Nanocellulose, Deoxygenation, Nyamplung oil
Subjects:	Q Science > QD Chemistry > QD501 Catalysis. Catalysts.
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User:	Ingelia Yuan Fernanda
Date Deposited:	15 Aug 2024 01:20
Last Modified:	15 Aug 2024 01:20
URI:	http://repository.its.ac.id/id/eprint/114218