Optimasi Pelindian Emas Dari Campuran Logam dan Sintesisnya Menjadi Nanopartikel Emas Menggunakan Pereduksi Ekstrak Manjakani

Simanjuntak, Imelda Priskila (2024) Optimasi Pelindian Emas Dari Campuran Logam dan Sintesisnya Menjadi Nanopartikel Emas Menggunakan Pereduksi Ekstrak Manjakani. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 5004201047-Undergraduate_Thesis.pdf] Text
5004201047-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2026.

Download (2MB) | Request a copy

Abstract

Pelindian emas dengan klorinasi adalah salah satu metode non sianida yang memiliki keunggulan lebih ramah lingkungan, proses yang sederhana, dan biaya murah dibandingkan dengan pelindian dengan sianida. Penelitian ini mengevaluasi pelindian emas dengan asam klorida (HCl) sebagai pelartut dan natrium hipoklorit (NaClO) sebagai oksidator untuk memperoleh kembali emas yang tercampur dengan logam lain yakni tembaga, timbal, perak, dan besi. Parameter yang dipelajari untuk perolehan emas adalah variasi konsentrasi HCl 1,0; 3,0; 5,0 dan 7,0M, variasi konsentrasi NaClO 0,1; 0,5; 1,0; dan 1,5M, variasi waktu pelindian selama 1, 2, 3, dan 4 jam, dan variasi temperatur pada 25, 50, 75, dan 100ᵒC. dalam larutan. Hasil penelitian menunjukkan bahwa kondisi optimum dalam ekstraksi emas menghasilkan konsentrasi emas sebesar 213,18 ppm. Keadaan ini dicapai pada waktu 3 jam, suhu 50ᵒC dengan konsentrasi HCl dan NaClO masing-masing sebesar 5M dan 1M. Jumlah perolehan emas dalam larutan klorida bergantung pada waktu sebagai faktor utama, diikuti oleh konsentrasi asam klorida dan natrium hipoklorit, serta suhu larutan pada saat pelindian. Emas yang terlarut dalam larutan lindi dapat direduksi menjadi nanopartikel emas dengan ekstrak manjakani sebagai agen pereduksi dan penstabil. Pembentukan nanopartikel emas dikarakterisasi dengan spektrofotometri UV-Vis dengan puncak spektrum UV-Vis pada panjang gelombang 864 nm dan nilai adsorbansi sebesar 1,003. Persen emas yang didapat setelah proses adsorpsi mencapai 6,69%.
=====================================================================================================================================
Gold leaching with chlorination is one of the non-cyanide methods that has the benefits of being more environmentally friendly, a simple process, and low cost compared to cyanide leaching. This study evaluates gold leaching using hydrochloric acid (HCl) as a solvent and sodium hypochlorite (NaClO) as an oxidizer to recover gold mixed with other metals, namely copper, lead, silver, and iron. The parameters studied for gold recovery were variation of HCl concentration of 1,0; 3,0; 5,0; and 7,0M, variation of NaClO concentration of 0,1; 0,5; 1,0; and 1.5M, variation of leaching time for 1, 2, 3, and 4 hours, and variation of temperature at 25, 50, 75, and 100ᵒC in solution. The results showed that the optimum conditions in gold extraction resulted in a gold concentration of 213.18 ppm. This was achieved at 3 hours, 50ᵒC with HCl and NaClO concentrations of 5M and 1M, respectively. The amount of gold recovery in chloride solution depends on time as the main factor, followed by the concentration of hydrochloric acid and sodium hypochlorite, and the temperature of the solution at the time of leaching. Gold dissolved in the leach solution can be reduced to gold nanoparticles using manjakani extract as a reducing and stabilizing agent. The formation of gold nanoparticles was characterized using UV-Vis spectrophotometry with a peak UV-Vis spectrum at a wavelength of 864 nm and an adsorbance value of 1,003. The percent gold gained after the adsorption process reached 6,69%.

Item Type: Thesis (Other)
Uncontrolled Keywords: Adsorpsi, Emas, Nanopartikel, Pelindian klorinasi, Adsorption, Gold, Nanoparticles, Chlorination leaching.
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Imelda Priskila Simanjuntak
Date Deposited: 12 Aug 2024 08:33
Last Modified: 27 Aug 2024 07:04
URI: http://repository.its.ac.id/id/eprint/114689

Actions (login required)

View Item View Item