Sintesis dan Karakterisasi Membran Komposit Berbasis Pengisi Fe3O4 Berpendukung Mikrokristalin Selulosa dari Kayu Sengon (Albizia Chinensis) untuk Pengurangan Kadar Metilen Biru dalam Air

Kusumaningtyas, Dyah Gayatri (2024) Sintesis dan Karakterisasi Membran Komposit Berbasis Pengisi Fe3O4 Berpendukung Mikrokristalin Selulosa dari Kayu Sengon (Albizia Chinensis) untuk Pengurangan Kadar Metilen Biru dalam Air. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 5004201154_Undergraduate_Thesis.pdf] Text
5004201154_Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only until 1 October 2026.

Download (6MB) | Request a copy

Abstract

Air limbah industri mengandung 17 – 20% pewarna yang menimbulkan masalah besar. Metilen Biru (MB) merupakan pewarna yang umum digunakan dan memiliki dampak buruk pada kesehatan manusia serta pencemaran linkungan.Fe3O4/MKS merupakan komposit yang mempunyai potensi baik sebagaibahan pengisi membran karena toksisitasnya yang rendah, ramah lingkungan, memiliki stabilittas termal dan sifat kimia yang baik, ketahanan terhadap fouling yang baik serta memiliki kemampuan baik dalam kinerja membran sehingga dapat meningkatkan fluks air. Mikrokistalin selulosa (MKS) telah berhasil diisolasi dari kayu sengon (Albizia Chinensis) yang merupakan biomassa dengan kandungan selulosa tinggi dan kandungan lignin yang rendah. MKS telah menunjukkan karakteristik pola difraksi sinar – X pada 2θ = 15,5;23,0 dan 35,0o yang sesuai dengan puncak khas selulosa dan pada 2θ = 30,27, 35,72; 43,50; 53,86; 57,58; 63,20 dan 74,80o yang merupakan puncak khas pada serapan Fe3O4 juga puncak serapan FTIR yang sesuai dengan puncak khas selulosa dan Fe3O4. Membran ultrafiltrasi terdiri dari matriks selulosa asetat yang dibuat dengan metode inversi fasa. Hasil karakterisasi membran menunjukkan bahwa penambahan komposit Fe3O4/MKS dari kayu sengon dapat menurunkan sudut kontak dari 68 menjadi 55,68o dan porositas membran dari 82 menjadi 88%. Penurunan sudut kontak menunjukkan peningkatan hidrofilisitas membran dengan peningkatan fluks air dari 49 menjadi 142 L/m2.h. Pada pemisahan MB, membran komposit dengan filler Fe3O4/MKS menunjukkan kinerja yang lebih baik dibandingkan membran tanpa Fe3O4/MKS, dengan peningkatan fluks air dari 125,5 menjadi 1453 L/m2.h dan rejeksi MB dari 43,5 menjadi 95,3%.
==============================================================================================================================
Industrial wastewater contains 17-20% dyes, which pose significant issues. Methylene blue (MB) is the most commonly used dye dan contributes to human health risks dan environmental pollution. Fe3O4/MCC is a composite that has great potential as a membrane filler because of its low toxicity, environmental friendliness, good thermal dan chemical stability, good fouling resistance dan ability to improve membrane performance increasing water flux. MCC has been successfully isolated from sengon wood (Albizia Chinensis) which is a biomass with high cellulose dan low lignin content. MCC has shown characteristic X-ray diffraction patterns at 2θ = 15,5; 23,0 dan 35,0o which correspond to typical peaks of cellulose dan at 2θ = 30,27, 35,72, 43,50; 53,86; 57,58; 63,20 dan 74,80o which correspond to typical peaks of Fe3O4. FTIR absorption peaks which correspond to typical peaks of cellulose dan Fe3O4. The ultrafiltration membrane is composed of a cellulose acetate matrix prepared by the phase inversion method. The characterization results have shown that the addition of Fe3O4/MCC from sengon wood can reduce the contact angle from 68 to 55,68o dan membrane porosity from 82 to 88%. A decrease in the contact angle indicates an increase in membrane hydrophilicity as evidenced by an increase in water flux from 49 to 142 L/m2.h. In MB separation, the composite membrane with Fe3O4/MCC filler has shown better performance than the membrane without Fe3O4/MCC, with increased water flux from 125,5 to 1453 L/m2.h dan MB rejection from 43,5 to 95,3%.

Item Type: Thesis (Other)
Uncontrolled Keywords: Fe3O4/MKS, Kayu sengon, Limbah pewarna, Membran komposit Composite membrane, Fe3O4/MCC, Sengon Wood, Dye Wastewater
Subjects: Q Science > QD Chemistry > QD320 Cellulose. Hydrolysis
Q Science > QD Chemistry > QD63.S4 Separation (Technology)
Divisions: Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis
Depositing User: Dyah Gayatri Kusumaningtyas Sukendro
Date Deposited: 27 Aug 2024 02:06
Last Modified: 27 Aug 2024 02:06
URI: http://repository.its.ac.id/id/eprint/114751

Actions (login required)

View Item View Item