Analisa Karakterisasi Sifat Kimia, Termal Dan Mekanis Bahan Limbah Padat Dari Pt. X

Pangaribuan, Prayudi Novem Insani (2022) Analisa Karakterisasi Sifat Kimia, Termal Dan Mekanis Bahan Limbah Padat Dari Pt. X. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511540000103-Undergraduate_Thesis.pdf Download (3MB)

Abstract

Pada dunia industri dalam menjalankan proses bisnis perusahaan sangat banyak dijumpai limbah seperti kertas kardus dan plastik bekas khususnya pada setiap perusahaan yang besar seperti industri makanan dan minuman. Di dalam aktifitas produksi makanan dan minuman, penggunaan kertas dan plastik sebagai kemasan dan pembungkus makanan masih sangat banyak digunakan. Karena jumlah yg begitu banyak dan kemasan dari pabrik yang pada umumnya hanya digunakan untuk satu kali pemakaian, sehingga setelah selesai dipakai kemasan tersebut menjadi limbah yang dapat langsung dibuang ke Tempat Pembuangan Akhir (TPA). Untuk pengelolaan limbah kertas dan kardus yang sering dijumpai pada saat ini yaitu dimanfaatkan menjadi Art Paper dan sering juga digunakan menjadi kerajinan tangan seperti keranjang sampah, vas bunga, tempat pensil, kartu ucapan, tas, dan lain sebagainya. Limbah kertas juga terdiri dari berbagai jenis di antaranya, kertas tulis, majalah, koran, karton atau pun pembungkus makanan. Sedangkan limbah sejenis plastik, pengolahannya masih sulit dilakukan. Maka dari itu penelitian ini dilakukan untuk mengetauhui karakterisasi material limbah padat agar dapat dilakukan daur ulang dan pengolahan yang lebih maksimal. Dan dari penelitian ini didapatkan hasil pengujian karakteristik dari tiga buah bahan limbah padat pada PT. X dengan tiga jenis pengujian. Dari uji FTIR didapatkan hasil bahwa pada limbah kertas kardus 59.77% teridentifikasi sebagai senyawa selafon, pada limbah kemasan plastik 92.51% teridentifikasi polipropilen isotaktik, dan pada limbah kemasan metalized 94.15% teridentifikasi senyawa polietilen. Dari hasil uji TGA pada limbah padat PT. X, dapat disimpulkan bahwa, sampel kertas kardus mengalami 2 kali dekomposisi di centang suhu 25°C�70°C, dan 250°C-550°C. Pada sampel kemasan plastik terjadi 2 kali dekomposisi di rentang suhu 80°C-100°C, dan 350°C-450°C. Dan pada kemasan metalized terjadi 1 kali dekomposisi pada rentang suhu 260°C-480°C. Dari hasil uji tarik, dapat didapatkan hasil bahwa, sampel kertas kardus horizontal memiliki kukuatan tarik maksimum sebesar sebesar 2.64 N/mm², dengan nilai elongasi sebesar 25.32 %, dan nilai modulus young sebesar 25.37 N/mm² dan pada sampel kertas kardus vertikal memiliki kukuatan tarik maksimum sebesar sebesar 1.93 N/mm², dengan nilai elongasi sebesar 25.32 %, dan nilai modulus young sebesar 28.05 N/mm². Pada sampel kemasan plastik memiliki kekuatan tarik maksimum sebesar 16.66 N/mm², dengan nilai elongasi sebesar 6.66 %, dan nilai modulus young sebesar 895.77 N/mm². Pada sampel kemasan metalized memiliki kekuatan tarik maksimum sebesar 22.56 N/mm², dengan nilai elongasi sebesar 25.32 %, dan nilai modulus young sebesar 543.46 N/mm².
================================================================================================================================
In the industrial world, in carrying out the company's business processes, there is a lot of waste such as cardboard and used plastic, especially in large companies such as the food and beverage industry. In food and beverage production activities, the use of paper and plastic as food packaging and wrapping is still very widely used. Due to the large number and packaging from the factory which are generally only used for one time use, so that after completion of use the packaging becomes waste that can be directly disposed of in the Final Disposal Site (TPA). For the management of paper and cardboard waste, which are often found today, they are used as Art Paper and are often also used for handicrafts such as waste baskets, flower vases, pencil cases, greeting cards, bags, and so on. Paper waste also consists of various types including writing paper, magazines, newspapers, cardboard or food wrapping. Meanwhile, plastic waste is still difficult to process. Therefore, this study was conducted to determine the characterization of solid waste materials so that they can be recycled and processed more optimally. And from this study, the results of characteristic testing of three materials were obtained with three types of tests. From the FTIR test, it was found that 59.77% of cardboard waste was identified as cellophane compounds, 92.51% of plastic packaging waste was identified as isotactic polypropylene, and 94.15% of metalized packaging waste identified polyethylene compounds. From the results of the TGA test on solid waste PT. X, it can be concluded that the cardboard samples underwent 2 decompositions in the temperature range of 25°C-70°C, and 250°C�550°C. In plastic packaging samples, decomposition occurred 2 times in the temperature range of 80°C-100°C, and 350°C-450°C. And in metalized packaging, decomposition occurs once in a temperature range of 260°C-480°C. From the tensile test results, it can be seen that the horizontal cardboard paper sample has a maximum tensile strength of 2.64 N/mm², with an elongation value of 25.32%, and a Young's modulus value of 25.37 N/mm² and the vertical cardboard sample has a tensile strength. maximum of 1.93 N/mm², with an elongation value of 25.32 %, and the value of Young's modulus of 28.05 N/mm². The plastic packaging sample has a maximum tensile strength of 16.66 N/mm², with an elongation value of 6.66%, and a Young's modulus of 895.77 N/mm². The metalized packaging sample has a maximum tensile strength of 22.56 N/mm², an elongation value of 25.32 %, and a Young's modulus of 543.46 N/mm².

Item Type:	Thesis (Other)
Additional Information:	RSMt 628.445 Pan a-1 • 2022
Uncontrolled Keywords:	Limbah padat, Karakterisasi Material, FTIR, TGA, Uji Tarik, Solid waste, Material Characterization, FTIR, TGA, Tensile Test
Subjects:	T Technology > TD Environmental technology. Sanitary engineering > TD789 Refuse and refuse disposal
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	11 Dec 2024 08:38
Last Modified:	11 Dec 2024 08:38
URI:	http://repository.its.ac.id/id/eprint/115952

Actions (login required)

View Item