Studi Pengaruh Waktu Pemanasan Sensitisasi Terhadap Struktur Mikro Dan Sifat Mekanik Stainless Steel 304 Pada Temperatur 600Oc

Suganda, Thomas Alvin (2022) Studi Pengaruh Waktu Pemanasan Sensitisasi Terhadap Struktur Mikro Dan Sifat Mekanik Stainless Steel 304 Pada Temperatur 600Oc. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 02511840000073_UndergraduateThesis.pdf Download (6MB)

Abstract

Stainless steel 304 merupakan salah satu jenis stainless steel austenitik yang umum digunakan di industri karena memiliki sifat mekanik yang baik, serta memiliki rentang temperatur kerja yang luas. Akan tetapi, pada temperatur yang tinggi, stainless steel 304 rentan mengalami fenomena yang disebut sensitisasi yang dapat mempengaruhi sifat mekanik dan struktur mikro. Oleh karena itu, diperlukan adanya penelitian mengenai sensitisasi stainlesssteel 304 yang diberi perlakuan berupa pemanasan pada temperatur 600oC dengan variasi waktu yaitu 3, 5, dan 7 jam dengan pendinginan yang dilakukan di luar furnace dengan media udara, serta satu spesimen tanpa sensitisasi. Pengujian yang dilakukan adalah pengujian tarik dan kekerasan untuk mendapatkan sifat mekanik dari spesimen, serta metalografi untuk mengamatistruktur mikro dari spesimen. Hasil pengamatan metalografi menunjukkan adanya pengaruh waktu sensitisasi terhadap struktur mikro dari stainless steel 304 yaitu menyebabkan perubahan strukturdari step menjadi dual kemudian ditch. Sementara itu, terjadi perubahan pada ketebalan batas butir akibat adanya perlakuan panas. Ketebalan batas butir meningkat dari 0,574 μm menjadi 0,760 μm, 1,164 μm, dan 1,651 μm. Variasi waktu sensitisasi juga menyebabkan perubahan sifat mekanik. Kekerasan dari spesimen stainless steel 304 mengalami peningkatan dari 163,30 HV menjadi 183,85 HV, 188,10 HV, dan 212,20 HV. Waktu sensitisasi yang semakin panjang juga menyebabkan tren peningkatan kekuatan tarik dari spesimen stainlesssteel 304 dari 656 MPa menjadi 673,5 MPa, 665 MPa, dan 680 MPa. Kekuatan luluh juga mengalami tren peningkatan dari 323 MPa menjadi 325 MPa. Sementara itu, keuletan dari spesimen SS304 mengalami penurunan dari 51,60% menjadi 48,91%, 48,83%, dan 48,70% akibat adanya perlakuan panas.
================================================================================================================================
Stainless steel 304 is one type of austenitic stainless steel that is commonly used in industry because it has good mechanical properties, and has a wide working temperature range. However, at high temperatures, stainless steel 304 is prone to a phenomenon called sensitization that can affect its mechanical properties and microstructures. Therefore, it is necessary to have research on the sensitization of stainless steel 304 which is heat treated at temperature of 600oC with various holding time of 3, 5, and 7 hours, as well as one as received speciment. Coolingprocess was carried out outside the furnace with air media. The tests carried out are tensile and hardness testing to analyze the mechanical properties of the specimen, as well as metallography to observe the microstructure of the specimen. The results of metallographic observations showed that there was an influence of holding time on the microstructure of stainless steel 304, which caused a change in structure from step to dua, and then ditch structure. Moreover, there is a change in the thickness of the grain boundary due to heat treatment. The grain boundary thickness is increased from 0.574 μm to 0.760 μm, 1.164 μm, and 1.651 μm. Variations in holding time also cause changes in mechanical properties. The hardness of the 304 stainless steel specimen increased from 163.30 HV to 183.85 HV, 188.10 HV, and 212.20 HV. The increase of holding time has also led to a trend of increasing the tensile strength of 304 stainless steel specimens from 656 MPa to 673.5 MPa, 665 MPa, and 680 MPa. Yield strength also experienced an increasing trend from 323 MPa to 325 MPa. Meanwhile, the ductility of the SS304 specimens decreased from 51.60% to 48.91%, 48.83%, and 48.70% due to sensitization.

Item Type:	Thesis (Other)
Additional Information:	RSMt 672.37 Sug s-1 2022
Uncontrolled Keywords:	Austenitic stainless steel, presipitasi kromium karbida, sensitisasi, sifat mekanik, struktur mikro
Subjects:	T Technology > TS Manufactures > TS320 Steel--Metallurgy.
Divisions:	Faculty of Industrial Technology > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User:	Mr. Marsudiyana -
Date Deposited:	17 Dec 2024 07:24
Last Modified:	17 Dec 2024 07:24
URI:	http://repository.its.ac.id/id/eprint/116002