Validasi Metode Penetapan Kadar Seng (Zn) dan Besi (Fe) Dalam Certified Reference Material (CRM) NCS HC 28927 Copper Alloy Menggunakan Inductively Coupled Plasma Optical Emission Spectrometry (ICP – OES)

Latifah, Dwi Riana (2025) Validasi Metode Penetapan Kadar Seng (Zn) dan Besi (Fe) Dalam Certified Reference Material (CRM) NCS HC 28927 Copper Alloy Menggunakan Inductively Coupled Plasma Optical Emission Spectrometry (ICP – OES). Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5004211069-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only until 1 April 2027. Download (2MB) | Request a copy

Abstract

Validasi metode adalah proses penilaian terhadap parameter tertentu untuk memastikan bahwa parameter tersebut memenuhi persyaratan penggunaan. Proses ini dilakukan ketika terdapat metode baru yang perlu diuji kemampuannya sebelum digunakan di laboratorium. Pada penelitian dilakukan validasi metode dengan parameter yaitu linearitas, LOD, LOQ, Presisi, dan Akurasi dengan menggunakan Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) untuk penetapan kadar Seng (Zn) dan Besi (Fe) pada Certified Reference Material (CRM) NCS HC 28927 Copper Alloy. Metode ini dilakukan dengan pengulangan sampel sebanyak 10 kali menggunakan konsentrasi standar induk 1000 ppm untuk kedua unsur tersebut. Certified Reference Material (CRM) NCS HC 28927 Copper Alloy merupakan material referensi pengujian dengan kandungan di dalamnya yaitu 68,52% tembaga (Cu), 31,40% seng (Zn), dan 0,0105% besi (Fe). Hasil analisis menunjukkan bahwa kadar Zn dan Fe masing-masing sebesar 36,95% dan 0,01%, dengan metode analisis yang telah melewati uji linearitas menghasilkan koefisien determinasi (R²) sebesar 0,9982 untuk Zn dan 0,9992 untuk Fe, nilai LOD (Limit of Detection) dari blanko masing-masing sebesar 0,0009% untuk Zn dan 0,006% untuk Fe, serta nilai LOQ (Limit of Quantitation) dari blanko masing-masing sebesar 0,003% untuk Zn dan 0,02% untuk Fe. Pada parameter presisi, metode ini memenuhi syarat keberterimaan untuk Zn namun tidak untuk Fe, karena nilai % dari Relative Standard Daviation (RSD) Fe melebihi 2/3 Coefficient of Variation (CV) Horwitz. Pada parameter akurasi diperoleh dari kedua unsur tersebut bias yang menyatakan bahwa kedua unsur tersebut tidak akurat. Pada penelitian yang telah dilakukan dapat disimpulkan bahwa penetapan kadar Seng (Zn) dan Besi (Fe) pada CRM Copper Alloy dengan metode destruksi basah terbuka menggunakan ICP-OES tidak valid.
==============================================================================================================================
Validation Method is an assessment process of certain parameters to ensure they meet specific criteria for usage. This activity is carried out when a new method is proposed and needs to be tested before being used in the laboratory. This study performed a Validation Method using parameters such as linearity, LOD, LOQ, precision, and accuracy with Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES) to determine the zinc (Zn) and iron (Fe) levels in Certified Reference Material (CRM) NCS HC 28927 Copper Alloy. Data were obtained by repeating the test 10 times using a parent standard concentration of 1000 ppm for both elements. The CRM NCS HC 28927 Copper Alloy is a reference testing material containing 68,52% copper (Cu), 31,40% zinc (Zn), and 0,0105% iron (Fe). The results showed that the levels of Zn and Fe were 36,95% and 0,01%, respectively, with the linearity test producing a coefficient of determination (R²) of 0,9982 for Zn and 0,9992 for Fe. The Limit of Detection (LOD) value of the blank was 0,0009% for Zn and 0,006% for Fe, while the Limit of Quantitation (LOQ) value of the blank was 0,003% for Zn and 0,02% for Fe. For the precision parameter, the method meets the acceptance requirements for Zn but not for Fe, since the percentage of the Relative Standard Deviation (RSD) of Fe exceeds 2/3 of the Horwitz Coefficient of Variation (CV). Regarding the accuracy parameter, the bias indicates that both elements are inaccurate. This research concluded that the determination of zinc (Zn) and iron (Fe) levels in CRM Copper Alloy using the wet destruction method with ICP-OES is not valid.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Besi, CRM, ICP-OES, Seng, Validasi Metode
Subjects:	Q Science > QD Chemistry > QD117.S64 Spectrophotometry Q Science > QD Chemistry > QD75.2 Chemistry, Analytic
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Chemistry > 47201-(S1) Undergraduate Thesis