Analisis Pengaruh Holding Time ZIF-67 Pada Sintesa Komposit Mikroselulosa/ZIF-67/PEO Sebagai Elektrolit Padat Berbasis Selulosa Tandan Kosong Kelapa Sawit (TKKS) Dalam Aplikasi Baterai Li-Ion

Sari, Aisya Tri Intan Luckyta (2025) Analisis Pengaruh Holding Time ZIF-67 Pada Sintesa Komposit Mikroselulosa/ZIF-67/PEO Sebagai Elektrolit Padat Berbasis Selulosa Tandan Kosong Kelapa Sawit (TKKS) Dalam Aplikasi Baterai Li-Ion. Other thesis, Institut Teknologi Sepuluh Nopember.

[thumbnail of 5011211090-Undergraduate_Thesis.pdf] Text
5011211090-Undergraduate_Thesis.pdf - Accepted Version
Restricted to Repository staff only

Download (5MB) | Request a copy

Abstract

Meningkatnya kesadaran akan dampak perubahan iklim mendorong meningkatnya permintaan global terhadap sumber energi terbarukan seperti baterai. Pada penelitian ini elektrolit padat berbasis mikroselulosa dari limbah TKKS digunakan. Penelitian ini bertujuan untuk menganalisa pengaruh dari holding time ZIF-67 terhadap struktur, morfologi, dan performa elektrokimia dari komposit PEO/Mikroselulosa/ZIF-67 padat. Elektrolit padat merupakan material yang memiliki potensi besar dalam aplikasi penyimpanan energi, terutama dalam baterai dan superkapasitor, karena kemampuannya untuk meningkatkan konduktivitasionik dan stabilitas mekanik. Dalam penelitian ini, menggunakan variasi waktu penahanan ZIF- 67 yaitu 2 jam, 4 jam , 6 jam, dan 8 jam untuk menentukan dampaknya terhadap karakteristik fisik dan elektrokimia dari komposit yang dihasilkan. Serta performa elektrokimia dari variasi komposit PEO/Mikroselulosa/ZIF-67 rasio (80:10:10) dan (80 15:5). Pada hasil uji XRD dan FTIR menunjukkan bahwa dengan variasi holding time 2 jam, 4 jam, 6 jam dan 8 jam pada ZIF-67 dengan menggunakan metode solvothermal tidak memiliki berpengaruh signifikan terhadap struktural. Pada hasil uji SEM menunjukan bahwa dengan semakin lama Waktu holding time akan membentuk ukuran yang lebih seragam, akan tetapi pada saat holding 8 jam bentuk partikel akan mengalami overgrowth. Performa elektrokimia komposit PEO/Mikroselulosa/ZIF-67 sebagai elektrolit padat. Dimana performa elektrokimia sampel (80:10:10) 4 jam, yaitu sebesar (2,6 × 10⁻⁴ S/cm) dengan memiliki kapasitansi rata-rata (0,599 F/m2). Sedangkan untuk sampel (8:1,5:5) terbaik dengan waktu holding 4 jam dengan nilai konduktivitas tertinggi (2,18 × 10⁻⁴ S/cm) dan memiliki kapasitansi memiliki nilai tertinggi (0,0299 F/m²). Secara keseluruhan sampel 80:15:5 dan 80:10:10 dengan holding time 4 jam menunjukkan performa elektrokimia yang lebih baik dengan nilai konduktivitas dan kapasitansi tinggi dibandingkan dengan variasi holding time lain
====================================================================================================================================
Increased awareness of the impact of climate change has driven global demand for renewable energy sources such as batteries. In this study, solid electrolytes based on microcellulose from EPFB waste were used. This study aimed to analyze the effect of ZIF-67 holding time on the structure, morphology, and electrochemical performance of PEO/Microcellulose/ZIF-67 solid composites. Solid electrolytes are materials with great potential in energy storage applications, particularly in batteries and supercapacitors, due to their ability to enhance ionic conductivity and mechanical stability. In this study, variations in ZIF-67 holding time (2 hours, 4 hours, 6 hours, and 8 hours) were used to determine their impact on the physical and electrochemical characteristics of the resulting composite. Additionally, the electrochemical performance of the PEO/Microcellulose/ZIF-67 composite variations with ratios of (80:10:10) and (80:15:5) was evaluated. The results of XRD and FTIR tests showed that variations in holding time of 2 hours, 4 hours, 6 hours, and 8 hours for ZIF-67 using the solvothermal method did not significantly affect the structure. The results of SEM tests showed that longer holding times resulted in more uniform particle sizes; however, at 8 hours of holding time, the particles experienced overgrowth. Electrochemical performance of the PEO/Microcellulose/ZIF-67 composite as a solid electrolyte. The electrochemical performance of the (80:10:10) 4-hour sample was (2.6 × 10⁻⁴ S/cm) with an average capacitance of (0.599 F/m²). Meanwhile, the (8:1.5:5) sample performed best at a holding time of 4 hours, with the highest conductivity value (2.18 × 10⁻⁴ S/cm) and the highest capacitance value (0.0299 F/m²). Overall, the 80:15:5 and 80:10:10 samples with a holding time of 4 hours showed better electrochemical performance with higher conductivity and capacitance values compared to other holding time variations

Item Type: Thesis (Other)
Uncontrolled Keywords: Elektrolit padat, Mikroselulosa, PEO, Tandan Kosong Kelapa Sawit (TKKS), ZIF-67 Keywords: Microcellulose, Solid electrolyte, PEO, Empty Palm Fruit Bunch (EPFB), ZIF-67.
Subjects: T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2921 Lithium cells.
T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK2941 Storage batteries
Divisions: Faculty of Industrial Technology and Systems Engineering (INDSYS) > Material & Metallurgical Engineering > 28201-(S1) Undergraduate Thesis
Depositing User: Aisya Tri Intan Luckyta Sari
Date Deposited: 29 Jul 2025 09:35
Last Modified: 29 Jul 2025 09:35
URI: http://repository.its.ac.id/id/eprint/122760

Actions (login required)

View Item View Item