Peningkatan Daya Serap Spons dengan Karbon Dots Terdoping Nitrogen (N-CDs) sebagai mMaterial Penyerap Minyak

Achadiyat, Rizal Surya (2025) Peningkatan Daya Serap Spons dengan Karbon Dots Terdoping Nitrogen (N-CDs) sebagai mMaterial Penyerap Minyak. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 5001211156-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (2MB) | Request a copy

Abstract

Penelitian ini bertujuan untuk mengetahui sifat dan karakterisasi dari N-CDs yang di sintesis menggunakan metode bottom-up dengan teknik iradiasi gelombang mikro, mengonjugasikan N-CDs dan spons sebagai bahan penyerap minyak, dan membandingkan daya serap minyak spons dengan N-CDs dan tanpa N-CDs. Sintesis N-CDs dilakukan dengan metode bottom-up menggunakan teknik iradiasi gelombang mikro, dengan prekursor citric acid dan carbonyl diamide. Penambahan doping nitrogen pada CDs dapat meningkatkan sifat optiknya. N-CDs yang dihasilkan dikarakterisasi menggunakan Transmission Electron Microscope (TEM) dan Fourier Transform Infrared Spectroscopy (FTIR) mengetahui strukturnya, Ultraviolet-Visible Spectroscopy (UV-Vis) dan fotoluminesensi untuk mengetahui sifat optiknya. Untuk meningkatkan efisiensi penyerapan minyak, diperlukan modifikasi permukaan spons poliuretan (PU) melalui pelapisan spons dengan N-CDs. Dalam penelitian ini diuji 4 spons, yaitu spons A berupa variasi dengan dan tanpa N-CDs pada variasi suhu 200℃ dan spons B berupa variasi dengan dan tanpa N-CDs pada variasi suhu 250℃. Pada spons A memiliki daya serap minyak yang lebih tinggi dibandingkan dengan spons B, hal ini berkaitan dengan besar pori pada spons berbahan dasar PU yang dikonjugasikan dengan N-CDs dengan variasi suhu yang tidak terlalu tinggi, sehingga pengaplikasian penyerapan pada spons meningkat tanpa ada hilangnya gugus fungsi yang ada pada N-CDs untuk menunjang peningkatan kinerja spons sebagai penyerap minyak. Selain itu, kapasitas penyerapan minyak juga meningkat secara signifikan, yakni dari 6,53 gr/gr menjadi 9,75 gr/gr untuk spons A, dan dari 6,87 gr/gr menjadi 7,58 gr/gr untuk spons B. konjugasi N-CDs ke dalam spons PU mampu meningkatkan kapasitas penyerapan minyak hingga 50%.
======================================================================================================================================
This study aims to determine the properties and characterization of N-CDs synthesized using the bottom-up method with microwave irradiation technique, conjugating N-CDs and sponges as oil absorbent materials, and comparing the oil absorption capacity of sponges with and without N-CDs. The synthesis of N-CDs was carried out using the bottom-up method with microwave irradiation, employing citric acid and carbonyl diamide as precursors. The addition of nitrogen doping to CDs can enhance their optical properties. The resulting N-CDs were characterized using Transmission Electron Microscopy (TEM) and Fourier Transform Infrared Spectroscopy (FTIR) to determine their structure, Ultraviolet-Visible Spectroscopy (UV-Vis) and photoluminescence to determine their optical properties. To improve oil absorption efficiency, surface modification of polyurethane (PU) sponges is required through coating the sponges with N-CDs. In this study, four sponges were tested: Sponge A, which varied with and without N-CDs at a temperature of 200°C, and Sponge B, which varied with and without N-CDs at a temperature of 250°C. Sponges A exhibited higher oil absorption capacity compared to sponges B, which is attributed to the larger pore size of the PU-based sponge conjugated with N-CDs at relatively low temperatures, thereby enhancing absorption efficiency without compromising the functional groups of N-CDs, thereby supporting improved performance of the sponge as an oil absorber. Also, oil absorption capacity increased significantly, from 6.53 g/g to 9.75 g/g for Sponge A, and from 6.87 g/g to 7.58 g/g for Sponge B. Conjugating N-CDs into PU sponges can increase oil absorption capacity by up to 50%.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Minyak, Carbon Dots, doping nitrogen, spons poliuretan, Oil, Carbon Dots, nitrogen doping, polyurethane sponge.
Subjects:	T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles. T Technology > TP Chemical technology > TP669 Oils, fats, and waxes
Divisions:	Faculty of Science and Data Analytics (SCIENTICS) > Physics > 45201-(S1) Undergraduate Thesis
Depositing User:	Rizal Surya Achadiyat
Date Deposited:	29 Jul 2025 07:47
Last Modified:	29 Jul 2025 07:47
URI:	http://repository.its.ac.id/id/eprint/122811

Actions (login required)

View Item