Pengaruh Variasi Konsentrasi Dalam Pemanfaatan Limbah Kulit Jagung (Zea Mays L.) Sebagai Inhibitor Organik Terhadap Laju Korosi Pada Baja API 5L Grade B Dengan Media Korosif 1M H2SO4

Rahmadanti, Ardya Safina (2025) Pengaruh Variasi Konsentrasi Dalam Pemanfaatan Limbah Kulit Jagung (Zea Mays L.) Sebagai Inhibitor Organik Terhadap Laju Korosi Pada Baja API 5L Grade B Dengan Media Korosif 1M H2SO4. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2038211071-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (7MB) | Request a copy

Abstract

Korosi dapat terjadi karena reaksi elektrokimia antara logam dengan lingkungannya, yang menyebabkan penurunan kualitas logam seperti peningkatan kerapuhan, permukaan kasar, dan rentan terhadap kerusakan. Salah satu cara untuk mencegah korosi adalah dengan menggunakan inhibitor, yaitu senyawa kimia dalam jumlah kecil yang mampu menahan atau memperlambat reaksi korosi pada baja. Salah satu inhibitor organik yang dapat digunakan adalah kulit jagung. Penelitian ini bertujuan untuk mengetahui pengaruh inhibitor dari kulit jagung terhadap laju korosi baja API 5L grade B dalam larutan korosif H₂SO₄ 1M. Ekstrak diperoleh melalui metode maserasi, dengan variasi konsentrasi inhibitor sebesar 100 ppm, 200 ppm, 300 ppm, 400 ppm, dan 500 ppm serta menggunakan suhu ruang. Pengujian dilakukan menggunakan metode Polarisasi, EIS, Weightloss, FTIR, dan SEM. Pada pengujian polarisasi dengan efisiensi tertinggi terletak pada waktu rendam 2 jam dengan konsentrasi 500 ppm sebesar 91.666% sedangkan pengujian EIS dengan efisiensi tertinggi berada pada konsentrasi 500 ppm dengan waktu perendaman 2 jam sebesar 93.939% konsentrasi 500 ppm. Dari pengujian Weight Loss di dapat hasil pengujian Weight Loss yaitu dengan efisiensi tertinggi sebesar 89.985% pada konsentrasi 500 ppm. Hasil pengujian FTIR menunjukkan adanya gugus fungsi yang terikat pada permukaan baja API 5L grade B. Sementara itu, analisis SEM pada baja dengan variasi konsentrasi 500 ppm memperlihatkan pembentukan lapisan pelindung pada permukaan baja, yang mengindikasi efektivitas inhibitor dalam menghambat laju korosi.
==================================================================================================================================
Corrosion occurs due to an electrochemical reaction between the metal and its environment, which leads to deterioration of the metal such as increased brittleness, rough surface, and susceptibility to damage. One way to prevent corrosion is to use inhibitors, which are chemical compounds in small amounts that are able to resist or slow down the corrosion reaction in steel. One of the organic inhibitors that can be used is corn husk. This study aims to determine the effect of inhibitors from corn husk on the corrosion rate of API 5L grade B steel in 1M H₂SO₄ corrosive solution. The extract was obtained through the maceration method, with variations in inhibitor concentrations of 100 ppm, 200 ppm, 300 ppm, 400 ppm, and 500 ppm and using room temperature. Tests were carried out using Polarization, EIS, Weight Loss, FTIR, and SEM methods. In the polarization test, the highest efficiency was achieved at a soaking time of 2 hours with a concentration of 500 ppm, reaching 91.666%, while in the EIS test, the highest efficiency was achieved at a concentration of 500 ppm with a soaking time of 2 hours, reaching 93.939% at a concentration of 500 ppm. The Weight Loss test yielded the highest efficiency of 89.985% at a concentration of 500 ppm. The FTIR test results showed the presence of functional groups bound to the surface of API 5L grade B steel. Meanwhile, SEM analysis on steel with a concentration variation of 500 ppm showed the formation of a protective layer on the steel surface, indicating the effectiveness of the inhibitor in reducing the corrosion rate.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Korosi, Inhibitor Organik, Kulit Jagung, Baja API 5L, H2SO4 Corrosion, Inhibitor Organic, Corn Husk, Steel API 5L, H2SO4
Subjects:	Q Science > QD Chemistry > QD115 Electrochemical analysis T Technology > TA Engineering (General). Civil engineering (General) > TA418.74 Corrosion and anti-corrosives
Divisions:	Faculty of Vocational > Mechanical Industrial Engineering (D4)
Depositing User:	Ardya Safina Rahmadanti
Date Deposited:	31 Jul 2025 07:11
Last Modified:	31 Jul 2025 07:11
URI:	http://repository.its.ac.id/id/eprint/124390