Fabrikasi Nanokomposit SiO₂/TiO₂ dengan Kombinasi Teknologi Sol-Gel dan Ultrasonikasi sebagai UV-Shielding dan Acid-Resintence dalam Formulasi Produk Kosmetik

Zanjabiela, Nabielah Salwa and Saputra, Dhanny Yulian (2025) Fabrikasi Nanokomposit SiO₂/TiO₂ dengan Kombinasi Teknologi Sol-Gel dan Ultrasonikasi sebagai UV-Shielding dan Acid-Resintence dalam Formulasi Produk Kosmetik. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2041211028_2041211079-Undergraduate_Thesis.pdf - Accepted Version Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

Paparan sinar UV berlebih dapat menyebabkan penuaan dini dan kanker kulit, sehingga diperlukan bahan fotoprotektif yang efektif. TiO2 umum digunakan sebagai UV-shielding dalam kosmetik, tetapi rentan terhadap aglomerasi dan fotokatalisis yang dapat menurunkan stabilitas formulasi. Kombinasi dengan SiO2 membentuk nanokomposit yang mampu meningkatkan dispersibilitas, mengurangi fotokatalisis, dan meningkatkan ketahanan terhadap lingkungan asam. Penelitian ini mengembangkan nanokomposit TiO2/SiO2 menggunakan metode sol-gel dan ultrasonikasi dengan variasi rasio molar SiO2:TiO2. Sol-gel menghasilkan partikel seragam dengan kemurnian tinggi, sedangkan ultrasonikasi meningkatkan homogenitas dan stabilitas. Karakterisasi dilakukan dengan XRD, FTIR, TEM, UV-Vis, BET, dan SEM-EDX untuk menentukan struktur kristal, gugus fungsi, morfologi, dan efisiensi absorbansi UV. Uji ketahanan asam dilakukan untuk menilai stabilitas dalam kondisi pH ekstrem. Diharapkan nanokomposit yang dihasilkan memiliki distribusi ukuran partikel yang seragam, daya serap UV optimal, serta ketahanan tinggi dalam lingkungan asam, menjadikannya kandidat unggul dalam formulasi kosmetik berdaya proteksi tinggi.
======================================================================================================================================
Excessive UV exposure can cause premature aging and skin cancer, necessitating the use of effective photoprotective materials. TiO2 is commonly used as a UV-Shielding in cosmetics, but it is prone to agglomeration and photocatalysis, which can reduce formulation stability. Combining it with SiO2 forms a nanocomposite that enhances dispersibility, reduces photocatalysis, and improves resistance to acidic environments. This study develops a TiO2/SiO2 nanocomposite using the sol-gel and ultrasonication methods with varying SiO2:TiO2 molar ratios. The sol-gel method produces uniform particles with high purity, while ultrasonication enhances homogeneity and stability. Characterization was performed using XRD, FTIR, TEM, UV-Vis, BET, and SEM-EDX to determine crystal structure, functional groups, morphology, and UV absorption efficiency. Acid resistance tests were conducted to evaluate stability under extreme pH conditions. The resulting nanocomposite is expected to have uniform particle size distribution, optimal UV absorption, and high stability in acidic environments, making it a promising candidate for high-protection cosmetic formulations

Item Type:	Thesis (Other)
Uncontrolled Keywords:	Kata kunci: Acid Resistance, SiO2/TiO2, Sol-Gel, Ultrasonikasi, UV-Shielding ========================================================= Keywords: Acid Resistance, SiO2/TiO2, Sol-gel, Ultrasonication, UV-Shielding
Subjects:	T Technology > TP Chemical technology > TP248 Nanogels. Nanoparticles.
Divisions:	Faculty of Vocational > Industrial Chemical Engineering
Depositing User:	Nabielah Salwa Zanjabiela
Date Deposited:	01 Aug 2025 03:55
Last Modified:	01 Aug 2025 03:55
URI:	http://repository.its.ac.id/id/eprint/124921

Actions (login required)

View Item