Komposisi 3D Printing Dengan menggunakan Variasi Fiber Polyamide Menggunakan Superplasticizer Polycarboxylate

Zain, Alfarezi Audy Ramadhani (2025) Komposisi 3D Printing Dengan menggunakan Variasi Fiber Polyamide Menggunakan Superplasticizer Polycarboxylate. Other thesis, Institut Teknologi Sepuluh Nopember.

Text 2035211081-UnderGraduate_Thesis.pdf - Accepted Version Restricted to Registered users only Download (25MB) | Request a copy

Abstract

Teknologi 3D printing telah menjadi salah satu inovasi paling transformatif dalam bidang manufaktur, memungkinkan pembuatan objek dengan tingkat kompleksitas tinggi, presisi yang sangat baik, dan efisiensi yang luar biasa. Penelitian ini bertujuan untuk menyelidiki komposisi material yang digunakan dalam 3D printing, khususnya dengan fokus pada variasi serat polyamide yang dipadukan dengan superplasticizer polycarboxylate (PCE). Penambahan PCE bertujuan untuk meningkatkan workability atau kemudahan pengolahan material selama proses pencetakan, yang memungkinkan material lebih mudah diatur dan dicetak dengan lebih lancar. Sementara itu, penambahan serat polyamide bertujuan untuk memperkuat struktur hasil cetakan, meningkatkan kekuatan tarik, dan mengurangi potensi keretakan yang mungkin terjadi. Penelitian ini menguji beberapa variasi komposisi, yaitu PCE 1% dengan variasi serat polyamide 0,04%, 0,07%, dan 0,1%, menggunakan mesin printer 3D tipe D-Shape. Hasil pengujian menunjukkan bahwa campuran PCE 1% dengan 0,07% serat polyamide (MF2) memberikan performa terbaik. Dalam hal kekuatan tekan, MF2 menunjukkan hasil yang terbaik dengan kekuatan tekan mencapai 58,10 MPa pada umur 28 hari. Selain itu, untuk pengujian flowability dalam rentang waktu 15 menit, campuran MF2 menunjukkan stabilitas diameter yang lebih baik, dengan penurunan diameter yang lebih moderat dibandingkan variasi serat polyamide lainnya. Campuran ini juga memberikan hasil terbaik dalam hal shape retention factor (SRF), dengan kemampuan terbaik dalam mempertahankan bentuknya selama proses pencetakan. Kombinasi PCE 1% dan 0,07% serat polyamide menghasilkan cetakan dengan kualitas mekanis yang tinggi, serta efisiensi proses pencetakan yang optimal, menjadikannya pilihan yang paling ideal untuk aplikasi konstruksi dan industri, terutama untuk produksi dalam skala besar di mana material yang kuat, fleksibel, dan efisien sangat dibutuhkan.
========================================================================================================================================
3D printing technology has become one of the most transformative innovations in manufacturing, enabling the creation of objects with high levels of complexity, excellent precision, and extraordinary efficiency. This study aims to investigate the composition of materials used in 3D printing, specifically focusing on variations of polyamide fibers combined with polycarboxylate (PCE) superplasticizers. The addition of PCE aims to improve the workability or ease of processing of the material during the printing process, which allows the material to be more easily arranged and printed more smoothly. Meanwhile, the addition of polyamide fibers aims to strengthen the structure of the printed product, increase tensile strength, and reduce the potential for cracking that may occur. This study tested several composition variations, namely 1% PCE with variations of 0.04%, 0.07%, and 0.1% polyamide fibers, using a D-Shape 3D printer machine. The test results showed that a mixture of 1% PCE with 0.07% polyamide fiber (MF2) provided the best performance. In terms of compressive strength, MF2 showed the best results with a compressive strength reaching 53.09 MPa at the age of 28 days. Furthermore, in flowability testing over a 15-minute period, the MF2 blend demonstrated better diameter stability, with a more moderate diameter decrease compared to other polyamide fiber variations. This blend also provided the best results in terms of shape retention factor (SRF), with the best ability to maintain its shape during the printing process. The combination of 1% PCE and 0.07% polyamide fiber produced prints with high mechanical quality and optimal printing process efficiency, making it the most ideal choice for construction and industrial applications, especially for large-scale production where strong, flexible, and efficient materials are essential.

Item Type:	Thesis (Other)
Uncontrolled Keywords:	3D printing, Mesin D-Shape, Serat polyamide, Superplasticizer polycarboxylate (PCE), Kekuatan tekan, Buildability.
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA418.16 Materials--Testing. T Technology > TA Engineering (General). Civil engineering (General) > TA439 Lightweight concrete. High strength concrete. T Technology > TH Building construction > TH1461 Concrete construction.
Divisions:	Faculty of Vocational > Civil Infrastructure Engineering (D4)
Depositing User:	Alfarezi Audy Ramadhani Zain
Date Deposited:	04 Aug 2025 07:13
Last Modified:	04 Aug 2025 07:13
URI:	http://repository.its.ac.id/id/eprint/126416

Actions (login required)

View Item